Mixtures of polyvinylamines and of liquid compositions of cationic amylaceous materials as agents for improving the dry strength of paper and cardboard
Mixtures of polyvinylamines and of liquid compositions of cationic amylaceous materials having very specific characteristics in terms of dry matter, viscosity, nitrogen content and pH. With such mixtures, it is possible to produce preparations that are particularly effective at increasing the dry strength of paper and cardboard. Also, the use of such mixtures for the production of paper and cardboard, the corresponding production method and the resulting paper and cardboard.
1. A mixture of at least one polyvinylamine and of at least one liquid composition of cationic starchy materials, in a ratio between 55 to 90 parts by dry weight of polyvinylamine per 10 to 45 parts by dry weight of cationic starchy material, wherein the liquid composition of cationic starchy materials has:
a solids content by weight of between 10% and 50%,
a viscosity—of greater than 200 mPa·s and at most equal to 350 mPa·s, said viscosity being determined by adjusting the solids content of the liquid composition of cationic starchy material to 10% and then measuring the Brookfield viscosity at 25° C. and at 20 rpm,
a total nitrogen content at least equal to 0.6% and at most equal to 1.6%, these percentages being expressed by dry weight relative to the dry weight of composition,
a pH below 9, and
wherein said cationic starchy material is obtained by enzymatic hydrolysis.
2. The mixture as claimed in claim 1 , wherein the mixture has a total solids content of between 5% and 30% by weight.
3. The mixture as claimed in claim 1 , wherein the ratio is between 60 to 80 parts by dry weight of polyvinylamine per 20 to 40 parts by dry weight of cationic starchy material.
4. The mixture as claimed in claim 1 , wherein the liquid composition of cationic starchy materials has a solids content by weight of between 10% and 30%.
5. The mixture as claimed in claim 1 , wherein the liquid composition of cationic starchy materials has a pH between 3.5 and 8.5.
6. The mixture as claimed in claim 1 , wherein the polyvinylamine comprises at least one vinylamine polymer selected from vinylamine homopolymers and terpolymers, vinylformamide-based polymers, said polymers being optionally modified after polymerization and said polymers being completely or partially neutralized or else in acid form.
7. A process for manufacturing a mixture of at least one polyvinylamine and of at least one cationic starchy material, in a ratio between 55 to 90 parts by dry weight of polyvinylamine per 10 to 45 parts by dry weight of cationic starchy material, characterized in that at least one polyvinylamine is mixed with at least one liquid composition of cationic starchy materials having:
a solids content by weight of between 10% and 50%,
a viscosity, determined according to a test T, of greater than 200 mPa·s and at most equal to 350 mPa·s,
a total nitrogen content at least equal to 0.6% and at most equal to 1.6%, these percentages being expressed by dry weight relative to the dry weight of composition,
a pH below 9, and
wherein said cationic starchy material is obtained by enzymatic hydrolysis.
8. A process for manufacturing a paper or cardboard by using the mixtures as claimed in claim 1 .
9. A paper or cardboard manufactured from the mixtures as claimed in claim 1 .