Method for producing a stable dispersion of nano-particles, dispersion produced, and use thereof

1. A method for producing a stable dispersion of nano-particles, comprising:

a) first, mixing an aqueous suspension of nano-particles with an aqueous solution of gelatine hydrolysate and obtaining a mixture, wherein the gelatine hydrolysate has an average molecular weight of approximately 500 to approximately 9,000 Da; and

b) thereafter, adding an aqueous solution of gelatine to the mixture obtained in a), and obtaining a stable dispersion of nano-particles, wherein the gelatine has an average molecular weight of at least 20,000 Da and a gel-strength of approximately 200 to approximately 320 g Bloom,

wherein the nano-particles are formed from an inorganic material selected from titanium dioxide, aluminium oxide, silicon dioxide, zirconium dioxide, indium tin oxide (ITO), zinc oxide, zinc sulphide, molybdenum sulphide or silver, and wherein an iso-electric point of the gelatine hydrolysate is selected in such a way that the nano-particles have a value of a zeta potential that is increased by mixing in accordance with a).

2. The method in accordance with claim 1 , wherein b) is carried out at a temperature of approximately 40 to approximately 60° C.

3. The method in accordance with claim 2 , further comprising:

c) letting the mixture obtained in b) cool down.

4. The method in accordance with claim 1 , wherein the nano-particles exhibit a positive zeta potential and wherein the gelatine hydrolysate is a gelatine hydrolysate of type A.

5. The method in accordance with claim 1 , wherein an iso-electric point of the gelatine employed in b) is smaller than or equal to the iso-electric point of the gelatine hydrolysate employed in a).

6. The method in accordance with claim 1 , wherein the gelatine is a gelatine of type A or comprises a mixture of gelatines of types A and B, and wherein the gelatine or the mixture has an iso-electric point of 6 to 10.

7. The method in accordance with claim 6 , wherein the gelatine or the mixture has an iso-electric point of 7 to 9.

8. The method in accordance with claim 1 , wherein the gelatine is a gelatine of type B and has an iso-electric point of 4 to 6.

9. The method in accordance with claim 1 , wherein the nano-particles and the gelatine hydrolysate in accordance with a) are mixed in a dry weight ratio of approximately 2:1 to approximately 1:1.5.

10. The method in accordance with claim 1 , wherein the solution of gelatine added in b) has a concentration of approximately 5 to approximately 20 weight-%, and wherein the concentration of the gelatine in the dispersion resulting from b) is approximately 1 to approximately 10 weight-%.

11. The method in accordance with claim 10 , wherein the concentration of the gelatine in the dispersion resulting from b) is approximately 1 to approximately 5 weight-%.

12. The method in accordance with claim 1 , wherein the nano-particles have an average particle size within the range of approximately 1 to approximately 100 nm.

13. The method in accordance with claim 12 , wherein the nano-particles have an average particle size within the range of approximately 3 to approximately 10 nanometer.

14. A stable dispersion produced in accordance with the method of claim 1 .

15. The stable dispersion in accordance with claim 14 , in which there is no coagulation of the nano-particles in a temperature range from approximately −18° C. to approximately 80° C.

16. A film, a foil or a coating containing nano-particles, produced from the stable dispersion of nano-particles according to claim 14 .

17. The method of claim 1 , wherein the gelatine hydrolysate has an

average molecular weight of approximately 2,500 to approximately 5,000 Da.