Ferritic stainless steel for biofuel supply system part, biofuel supply system part, ferritic stainless steel for exhaust heat recovery unit, and exhaust heat recovery unit

1. A ferritic stainless steel for a biofuel supply system part comprising, by mass %:

C: 0.03% or less;

N: 0.03% or less;

Si: more than 0.1% to 1% or less;

Mn: 0.02% to 1.2%;

Cr: 15% to 23%;

Al: 0.002% to 0.5%; and

either one or both of Nb and Ti,

with the remainder being Fe and unavoidable impurities,

wherein Expression (1) and Expression (2) illustrated below are satisfied, and

wherein an oxide film is formed on a surface thereof and carbonitrides containing either one or both Nb and Ti are produced on the surface by heat treatment in a vacuum atmosphere containing N 2 with a vacuum of 10 −2 torr to 1 torr, and the oxide film contains Cr, Si, Nb, Ti and Al in a total cationic fraction of 30% or more and Cr in a cationic fraction of 20% or more,

8(C+N)+0.03≦Nb+Ti≦0.6  (1)

Si+Cr+Al+{Nb+Ti−8(C+N)}≦15.5  (2)

each element symbol represents the content (mass %) of the element in Expression (1) and Expression (2).

2. The ferritic stainless steel for a biofuel supply system part according to claim 1 , further comprising, by mass %:

one or more elements selected from a group consisting of Ni: 2% or less, Cu: 1.5% or less, Mo: 3% or less, Sn: 0.5% or less, V: 1% or less, W: 1% or less, B: 0.005% or less, Zr: 0.5% or less, Co: 0.2% or less, Mg: 0.002% or less, Ca: 0.002% or less, and REM: 0.01% or less.

3. A biofuel supply system part made of the ferrtic stainless steel for a biofuel supply system part according to claim 1 .

4. A biofuel supply system part made of the ferrtic stainless steel for a biofuel supply system part according to claim 2 .

5. A ferritic stainless steel for an exhaust heat recovery unit comprising, by mass %:

C: 0.03% or less;

N: 0.05% or less;

Si: more than 0.1% to 1% or less;

Mn: 0.02% to 1.2%;

Cr: 17% to 23%;

Al: 0.002% to 0.5%;

either one or both of Nb and Ti; and

two or three elements selected from a group consisting of Ni: 0.25% to 1.5%, Cu: 0.25% to 1%, and Mo: 0.5% to 2%,

with the remainder being Fe and unavoidable impurities,

wherein Expression (3) and Expression (4) illustrated below are satisfied, and

wherein an oxide film is formed on a surface thereof and (Nb, Ti) carbonitrides containing either one or both Nb and Ti are produced on the surface by heat treatment in a vacuum atmosphere containing N 2 with a vacuum of 10 −2 torr to 1 torr, and the oxide film contains Cr, Si, Nb, Ti and Al in a total cationic fraction of 40% or more and Cr in a cationic fraction of 20% or more,

8(C+N)+0.03≦Nb+Ti≦0.6  (3)

Si+Cr+Al+{Nb+Ti−8(C+N)}≧17.5  (4)

each element symbol represents the content (mass %) of the element in Expression (3) and Expression (4), and in addition, the value of Nb+Ti−8(C+N) is equal to or greater than 0 in Expression (4).

6. The ferritic stainless steel for an exhaust heat recovery unit according to claim 5 , further comprising, by mass %:

one or more elements selected from a group consisting of V: 0.5% or less, W: 1% or less, B: 0.005% or less, Zr: 0.5% or less, Sn: 0.5% or less, Co: 0.2% or less, Mg: 0.002% or less, Ca: 0.002% or less, and REM: 0.01% or less.

7. An exhaust heat recovery unit comprising:

a heat exchange section of which members are fabricated by brazing,

wherein the heat exchange section is made of a ferritic stainless steel,

wherein the ferritic stainless steel comprises, by mass %: C: 0.03% or less; N: 0.05% or less; Si: more than 0.1% to 1% or less; Mn: 0.02% to 1.2%; Cr: 17% to 23%; Al: 0.002% to 0.5%; either one or both of Nb and Ti; and two or three elements selected from a group consisting of Ni: 0.25% to 1.5%, Cu: 0.25% to 1% and Mo: 0.5% to 2%, with the remainder being Fe and unavoidable impurities,

wherein Expression (3) and Expression (4) illustrated below are satisfied, and

wherein an oxide film is formed on a surface thereof and (Nb, Ti) carbonitrides containing either one or both Nb and Ti are produced on the surface by heat treatment in a vacuum atmosphere containing N 2 with a vacuum of 10 −2 torr to 1 torr, and the oxide film contains Cr, Si, Nb, Ti and Al in a total cationic fraction of 40% or more and Cr in a cationic fraction of 20% or more,

8(C+N)+0.03≦Nb+Ti≦0.6  (3)

Si+Cr+Al+{Nb+Ti−8(C+N)}≧17.5  (4)

each element symbol represents the content (mass %) of the element in Expression (3) and Expression (4), and the value of Nb+Ti−8(C+N) is equal to or greater than 0 in Expression (4).

8. The exhaust heat recovery unit according to claim 7 ,

wherein the ferritic stainless steel further comprises one or more elements selected from a group consisting of, by mass %, V: 0.5% or less, W: 1% or less, B: 0.005% or less, Zr: 0.5% or less, Sn: 0.5% or less, Co: 0.2% or less, Mg: 0.002% or less, Ca: 0.002% or less, and REM: 0.01% or less.