Siloxane hard coating resin
View Patent ↗The present invention relates to a siloxane hard resin including alicyclic epoxy siloxane alone or a reactive monomer, which is prepared by condensation reaction of alkoxysilanes, and has a weight average molecular weight in the range of 1000 to 4000 and a molecular weight distribution of PDI 1.05 to 1.4. A siloxane hard cured article produced by photo- or thermal polymerization has high hardness by compact crosslinking of siloxane molecules having different molecular weights.
1. A hard coating composition consisting essentially of an alicyclic epoxy group-containing siloxane resin, which has a weight average molecular weight in the range of 1000 to 4000 and a molecular weight distribution of PDI 1.05 to 1.4, and
a reactive monomer which is an oxetane monomer capable of reacting with the alicyclic epoxy group to form crosslinking in an amount of 1 to 100 parts by weight, based on 100 parts by weight of the siloxane resin,
wherein the siloxane resin is prepared, in the presence of water and a catalyst, by hydrolysis and condensation of (i) alkoxysilane containing an alicyclic epoxy group and an alkoxy group represented by the following Chemical Formula 1 alone, or (ii) alkoxysilane having an alicyclic epoxy group and an alkoxy group represented by the following Chemical Formula 1 and one or more selected from the group consisting of tetramethoxysilane, tetraethoxysilane, methyltrimethoxysilane, methyltriethoxysilane, methyltripropoxysilane, dimethyldimethoxysilane, dimethyldiethoxysilane, ethyltriethoxysilane, propyltrimethoxysilane, vinyltrimethoxysilane, vinyltriethoxysilane, vinyltripropoxysilane, N-(3-acryloxy-2-hydroxypropyl)-3-aminopropyltrimethoxysilane, N-(3-acryloxy-2-hydroxypropyl)-3-aminopropyltriethoxysilane, N-(3-acryloxy-2-hydroxypropyl)-3-aminopropyltripropoxysilane, 3-acryloxypropylmethylbis(trimethoxy)silane, 3-acryloxypropyltrimethoxysilane, 3-acryloxypropyltriethoxysilane, 3-acryloxypropyltripropoxysilane, 3-(meth)acryloxypropyltrimethoxysilane, 3-(meth)acryloxypropyltriethoxysilane, 3-(meth)acryloxypropyltripropoxysilane, N-(aminoethyl)-3-aminopropyltrimethoxysilane, N-(2-aminoethyl)-3-aminopropyltriethoxysilane, 3-aminopropyltrimethoxysilane, 3-aminopropyltriethoxysilane, chloropropyltrimethoxysilane, chloropropyltriethoxysilane, and heptadecafluorodecyltrimethoxysilane:
R 1 n Si(OR 2 ) 4-n [Chemical Formula 1]
wherein R 1 is a straight or branched C 1 to C 6 alkyl group containing an alicyclic epoxy group, the alicyclic epoxy group is a C 3 to C 6 cycloalkyl group having an epoxy group, R 2 is a straight or branched C 1 to C 7 alkyl group, and n is an integer of 1 to 3.
2. The hard coating composition according to claim 1 , wherein the alkoxysilane represented by Chemical Formula 1 is 2-(3,4-epoxycyclohexyl)ethyltrimethoxysilane, or 2-(3,4-epoxycyclohexyl)ethyltriethoxysilane.
3. The hard coating composition according to claim 1 , wherein the oxetane monomer includes one or more of the oxetane group of the following Chemical Formula 4:
4. The hard coating composition according to claim 3 , wherein the oxetane monomer is one or more selected from the group consisting of 3-ethyl-3-hydroxymethyloxetane, 2-ethylhexyloxetane, xylene bis oxetane, and 3-ethyl-3[[[3-ethyloxetan-3-yl]methoxy]methyl]oxetane.
5. The hard coating composition according to claim 1 , wherein the catalyst is selected from the group consisting of basic catalysts, and ion exchange resins, including ammonia, potassium hydroxide, sodium hydroxide, barium hydroxide, imidazole, Amberite IRA-400, IRA-67, and combinations thereof.
6. A method for producing a hard cured article by polymerization of the hard coating composition according to claim 1 .
7. The method according to claim 6 , wherein the polymerization includes a step of radiation or heating.
8. An optical film or sheet comprising the hard cured article that is produced by polymerization of the hard coating composition according to claim 1 .
9. A hard coating composition consisting essentially of an alicyclic epoxy group-containing siloxane resin, which has a weight average molecular weight in the range of 1000 to 4000 and a molecular weight distribution of PDI 1.05 to 1.4, and
an organic solvent in an amount of 0.1 to 10 parts by weight, based on 100 parts by weight of the siloxane resin,
wherein the siloxane resin is prepared, in the presence of water and a catalyst, by hydrolysis and condensation of (i) alkoxysilane containing an alicyclic epoxy group and an alkoxy group represented by the following Chemical Formula 1 alone, or (ii) alkoxysilane having an alicyclic epoxy group and an alkoxy group represented by the following Chemical Formula 1 and one or more selected from the group consisting of tetramethoxysilane, tetraethoxysilane, methyltrimethoxysilane, methyltriethoxysilane, methyltripropoxysilane, dimethyldimethoxysilane, dimethyldiethoxysilane, ethyltriethoxysilane, propyltrimethoxysilane, vinyltrimethoxysilane, vinyltriethoxysilane, vinyltripropoxysilane, N-(3-acryloxy-2-hydroxypropyl)-3-aminopropyltrimethoxysilane, N-(3-acryloxy-2-hydroxypropyl)-3-aminopropyltriethoxysilane, N-(3-acryloxy-2-hydroxypropyl)-3-aminopropyltripropoxysilane, 3-acryloxypropylmethylbis(trimethoxy)silane, 3-acryloxypropyltrimethoxysilane, 3-acryloxypropyltriethoxysilane, 3-acryloxypropyltripropoxysilane, 3-(meth)acryloxypropyltrimethoxysilane, 3-(meth)acryloxypropyltriethoxysilane, 3-(meth)acryloxypropyltripropoxysilane, N-(aminoethyl)-3-aminopropyltrimethoxysilane, N-(2-aminoethyl)-3-aminopropyltriethoxysilane, 3-aminopropyltrimethoxysilane, 3-aminopropyltriethoxysilane, chloropropyltrimethoxysilane, chloropropyltriethoxysilane, and heptadecafluorodecyltrimethoxysilane:
R 1 n Si(OR 2 ) 4-n [Chemical Formula 1]
wherein R 1 is a straight or branched C 1 to C 6 alkyl group containing an alicyclic epoxy group, the alicyclic epoxy group is a C3 to C6 cycloalkyl group having an epoxy group, R 2 is a straight or branched C1 to C7 alkyl group, and n is an integer of 1 to 3.
10. A hard coating composition consisting essentially of an alicyclic epoxy group-containing siloxane resin, which has a weight average molecular weight in the range of 1000 to 4000 and a molecular weight distribution of PDI 1.05 to 1.4;
an oxetane monomer capable of reacting with the alicyclic epoxy group to form crosslinking in an amount of 1 to 100 parts by weight, based on 100 parts by weight of the siloxane resin; and
a polymerization initiator selected from the group consisting of onium salts, organometallic salts, amines, and imidazoles in an amount of 0.1 to 10 parts by weight, based on 100 parts by weight of the siloxane resin,
wherein the siloxane resin is prepared, in the presence of water and a catalyst, by hydrolysis and condensation of (i) alkoxysilane containing an alicyclic epoxy group and an alkoxy group represented by the following Chemical Formula 1 alone, or (ii) alkoxysilane having an alicyclic epoxy group and an alkoxy group represented by the following Chemical Formula 1 and one or more selected from the group consisting of tetramethoxysilane, tetraethoxysilane, methyltrimethoxysilane, methyltriethoxysilane, methyltripropoxysilane, dimethyldimethoxysilane, dimethyldiethoxysilane, ethyltriethoxysilane, propyltrimethoxysilane, vinyltrimethoxysilane, vinyltriethoxysilane, vinyltripropoxysilane, N-(3-acryloxy-2-hydroxypropyl)-3-aminopropyltrimethoxysilane, N-(3-acryloxy-2-hydroxypropyl)-3-aminopropyltriethoxysilane, N-(3-acryloxy-2-hydroxypropyl)-3-aminopropyltripropoxysilane, 3-acryloxypropylmethylbis(trimethoxy)silane, 3-acryloxypropyltrimethoxysilane, 3-acryloxypropyltriethoxysilane, 3-acryloxypropyltripropoxysilane, 3-(meth)acryloxypropyltrimethoxysilane, 3-(meth)acryloxypropyltriethoxysilane, 3-(meth)acryloxypropyltripropoxysilane, N-(aminoethyl)-3-aminopropyltrimethoxysilane, N-(2-aminoethyl)-3-aminopropyltriethoxysilane, 3-aminopropyltrimethoxysilane, 3-aminopropyltriethoxysilane, chloropropyltrimethoxysilane, chloropropyltriethoxysilane, and heptadecafluorodecyltrimethoxysilane:
R 1 n Si(OR 2 ) 4-n [Chemical Formula 1]
wherein R 1 is a straight or branched C 1 to C 6 alkyl group containing an alicyclic epoxy group, the alicyclic epoxy group is a C3 to C6 cycloalkyl group having an epoxy group, R 2 is a straight or branched C1 to C7 alkyl group, and n is an integer of 1 to 3.
11. A hard coating composition consisting essentially of an alicyclic epoxy group-containing siloxane resin, which has a weight average molecular weight in the range of 1000 to 4000 and a molecular weight distribution of PDI 1.05 to 1.4;
an oxetane monomer capable of reacting with the alicyclic epoxy group to form crosslinking in an amount of 1 to 100 parts by weight, based on 100 parts by weight of the siloxane resin; and
one or more additives selected from the group consisting of an organic solvent, an antioxidant, a leveling agent, and a coating control agent,
wherein the siloxane resin is prepared, in the presence of water and a catalyst, by hydrolysis and condensation of (i) alkoxysilane containing an alicyclic epoxy group and an alkoxy group represented by the following Chemical Formula 1 alone, or (ii) alkoxysilane having an alicyclic epoxy group and an alkoxy group represented by the following Chemical Formula 1 and one or more selected from the group consisting of tetramethoxysilane, tetraethoxysilane, methyltrimethoxysilane, methyltriethoxysilane, methyltripropoxysilane, dimethyldimethoxysilane, dimethyldiethoxysilane, ethyltriethoxysilane, propyltrimethoxysilane, vinyltrimethoxysilane, vinyltriethoxysilane, vinyltripropoxysilane, N-(3-acryloxy-2-hydroxypropyl)-3-aminopropyltrimethoxysilane, N-(3-acryloxy-2-hydroxypropyl)-3-aminopropyltriethoxysilane, N-(3-acryloxy-2-hydroxypropyl)-3-aminopropyltripropoxysilane, 3-acryloxypropylmethylbis(trimethoxy)silane, 3-acryloxypropyltrimethoxysilane, 3-acryloxypropyltriethoxysilane, 3-acryloxypropyltripropoxysilane, 3-(meth)acryloxypropyltrimethoxysilane, 3-(meth)acryloxypropyltriethoxysilane, 3-(meth)acryloxypropyltripropoxysilane, N-(aminoethyl)-3-aminopropyltrimethoxysilane, N-(2-aminoethyl)-3-aminopropyltriethoxysilane, 3-aminopropyltrimethoxysilane, 3-aminopropyltriethoxysilane, chloropropyltrimethoxysilane, chloropropyltriethoxysilane, and heptadecafluorodecyltrimethoxysilane:
R 1 n Si(OR 2 ) 4-n [Chemical Formula 1]
wherein R 1 is a straight or branched C 1 to C 6 alkyl group containing an alicyclic epoxy group, the alicyclic epoxy group is a C3 to C6 cycloalkyl group having an epoxy group, R2 is a straight or branched C1 to C7 alkyl group, and n is an integer of 1 to 3.