Image sensor, an inspection system and a method of inspecting an article
A high sensitivity image sensor comprises an epitaxial layer of silicon that is intrinsic or lightly p doped (such as a doping level less than about 10 13 cm −3 ). CMOS or CCD circuits are fabricated on the front-side of the epitaxial layer. Epitaxial p and n type layers are grown on the backside of the epitaxial layer. A pure boron layer is deposited on the n-type epitaxial layer. Some boron is driven a few nm into the n-type epitaxial layer from the backside during the boron deposition process. An anti-reflection coating may be applied to the pure boron layer. During operation of the sensor a negative bias voltage of several tens to a few hundred volts is applied to the boron layer to accelerate photo-electrons away from the backside surface and create additional electrons by an avalanche effect. Grounded p-wells protect active circuits as needed from the reversed biased epitaxial layer.
1. A method of fabricating a backside-illuminated avalanche image sensor, the method comprising:
forming an intrinsic or p-doped silicon epitaxial layer on a silicon wafer with a p-dopant concentration less than 2×10 13 atoms per cubic centimeter (cm −3 );
forming at least one of CMOS, CCD and bipolar circuits on a front-side surface of the epitaxial layer, said circuits comprising at least a buried n-type channel, and at least part of those circuits are formed in a p+-doped well with a doping concentration greater than 10 16 atoms cm −3 ;
polishing or etching away the silicon wafer to expose a back-side surface of the epitaxial layer in at least a light sensitive area;
epitaxially growing a p-type layer on the exposed surface with a dopant concentration greater than 5×10 18 dopant atoms cm −3 ;
epitaxially growing an n-type layer on the exposed surface with a dopant concentration between 5×10 15 dopant atoms cm −3 and 10 17 dopant atoms cm −3 ; and
depositing a pure boron coating on the exposed back-side surface of the epitaxial layer.
2. The method of claim 1 , further comprising depositing an anti-reflection coating on the pure boron coating.
3. The method of claim 1 , further comprising annealing the wafer for between 1 and 5 minutes at a temperature between 800° C. and 950° C. after depositing the pure boron coating.
4. The method of claim 1 , wherein forming said intrinsic or p-doped silicon epitaxial layer comprises generating the epitaxial layer with a thickness between 20 μm and 200 μm.
5. A method of fabricating a backside-illuminated avalanche image sensor, the method comprising:
epitaxially growing an n-type layer on a surface of a silicon wafer, the n-type layer having a dopant concentration between 5×10 15 dopant atoms cm −3 and 10 17 dopant atoms cm −3 and a thickness between 1 μm and 5 μm;
epitaxially growing a p-type layer on the surface of the n-type layer with a dopant concentration greater than 5×10 18 dopant atoms cm −3 and a thickness between 10 nm and 50 nm;
epitaxially growing an intrinsic or p-doped silicon epitaxial layer on the surface of the p-type layer with a p-dopant concentration less than 2×10 13 atoms cm −3 and a thickness between 20 μm and 200 μm;
forming at least one of CMOS, CCD and bipolar circuits on a front-side surface of the intrinsic or p-doped silicon epitaxial layer, said circuits comprising at least a buried n-type channel, and at least part of those circuits are formed in a p+-doped well with a doping concentration greater than 10 16 atoms cm −3 ;
removing the silicon wafer to expose at least a part of a back-side surface of the n-type layer; and
depositing a pure boron coating on the exposed back-side surface of the n-type layer.
6. The method of claim 5 , further comprising depositing an anti-reflection coating on the pure boron coating.
7. A backside-illuminated avalanche sensor comprising:
an epitaxial silicon layer;
a thin highly doped p-type layer, an n-type doped layer and a boron layer disposed on a light-sensitive surface of the epitaxial silicon layer; and
circuits formed on an opposing surface of the epitaxial silicon layer,
wherein the epitaxial silicon layer comprises one of intrinsic silicon and p-type doped silicon with less than 2×10 13 dopant atoms cm −3 ,
wherein the circuits comprise an n-type doped buried channel and a resistive gate configured to control electron accumulation in the n-type doped buried channel,
wherein at least some of the circuits are fabricated in a grounded p+ well with a dopant concentration greater than 10 16 dopant atoms cm −3 ,
wherein the thin highly doped p-type layer comprises p-type doped silicon with a dopant concentration greater than 5×10 18 dopant atoms cm −3 , and a thickness of less than 50 nm, and
wherein the n-type doped layer comprises n-type doped silicon with a dopant concentration between 5×10 15 dopant atoms cm −3 and 10 17 dopant atoms cm −3 , and a thickness of between 1 μm and 5 μm.
8. The sensor of claim 7 ,
wherein the boron layer comprises pure boron having a thickness in the range of 2 nm to 6 nm, and
wherein the sensor further comprises one or more anti-reflection layers disposed on the boron layer.
9. The sensor of claim 7 , wherein the sensor further comprises means for maintaining the boron layer at a negative potential of between −10V and −400V relative to the opposing surface of the epitaxial layer.
10. The sensor of claim 7 , wherein the circuits comprise at least one of CMOS image circuits, CCD circuits and bipolar transistors.
11. The sensor of claim 7 , wherein the sensor comprises a linear array of pixels.
12. The sensor of claim 7 , wherein the sensor comprises a two-dimensional array of pixels.
13. The sensor of claim 7 , wherein each pixel comprises circuits including a floating diffusion region configured for charge-to-voltage conversion.
14. The sensor of claim 13 , wherein the sensor further comprises one output for every two columns of pixels of the linear array.