Binder composition, separator including binder formed from the binder composition, lithium battery including the separator, and method of preparing the binder composition
A separator for a battery, a battery, and a method of preparing a graft copolymer for a binder, the separator including a porous substrate; a coating layer on at least one surface of the porous substrate, the coating layer including an inorganic oxide; and a binder between the porous substrate and the inorganic oxide or between adjacent particles of the inorganic oxide, the binder including a graft copolymer, wherein the graft copolymer has a backbone of a polyvinylidene fluoride-based polymer or a polyvinylidene fluoride-based copolymer, and a pendant chain grafted to the backbone, the pendant chain including a hydrophilic repeating unit, and fluorine atoms in the backbone of the graft copolymer are partially substituted with at least one of chlorine, bromine, or iodine.
1. A separator for a battery, the separator comprising:
a porous substrate;
a coating layer on at least one surface of the porous substrate, the coating layer including an inorganic oxide; and
a binder between the porous substrate and the inorganic oxide or between adjacent particles of the inorganic oxide, the binder including a graft copolymer, wherein:
the graft copolymer has:
a backbone of a polyvinylidene fluoride-based polymer or a polyvinylidene fluoride-based copolymer, and
a pendant chain grafted to the backbone, the pendant chain including a hydrophilic repeating unit, and
fluorine atoms in the backbone of the graft copolymer are partially substituted with at least one of chlorine, bromine, or iodine.
2. The separator as claimed in claim 1 , wherein an amount of the fluorine atoms partially substituted with the at least one of chlorine, bromine, or iodine is about 1 wt % to about 10 wt %, based on a total weight of fluorine atoms in the backbone.
3. The separator as claimed in claim 1 , wherein the backbone includes polyvinylidene fluoride-co-chlorotrifluoroethylene or polyvinylidene fluoride-co-chlorotrifluoroethylene/polyvinylidene fluoride-co-hexafluoropropylene.
4. The separator as claimed in claim 1 , wherein the pendant chain has a weight average molecular weight of from about 100 g/mol to about 1,000,000 g/mol.
5. The separator as claimed in claim 1 , wherein the pendant chain includes a carboxyl group in the hydrophilic repeating unit.
6. The separator as claimed in claim 1 , wherein the hydrophilic repeating unit is derived from a vinyl-based monomer.
7. The separator as claimed in claim 6 , wherein the vinyl-based monomer includes at least one of acrylic acid, butyl acrylate, triethylene glycol acrylate, acrylonitrile, acrylamide, 2-hydroxyethyl acrylate, maleic anhydride, ethylene glycol vinyl ether, or itaconic acid.
8. The separator as claimed in claim 1 , wherein the graft copolymer is included in the binder in an amount of about 0.1 wt % to about 100 wt %, based on a total weight of the binder.
9. The separator as claimed in claim 1 , wherein the inorganic oxide includes at least one selected from α-Al 2 O 3 , γ-Al(O)OH, TiO 2 , ZrO 2 , and SiO 2 .
10. The separator as claimed in claim 1 , wherein the binder is included in the separator in an amount of about 1 wt % to about 50 wt %, based on a total weight of the inorganic oxide.
11. The separator as claimed in claim 1 , wherein the porous substrate is a polyolefin-based porous substrate.
12. The separator as claimed in claim 1 , wherein the binder has an adhesive strength of about 40 mN/mm or greater with respect to the porous substrate.
13. A battery, comprising:
a cathode;
an anode; and
a separator between the cathode and the anode, the separator being the separator as claimed in claim 1 .