Method for preparing polyamide granules
The present invention relates to a method for preparing polyamide granules. This method comprises, in particular, steps of extruding the polymer, cooling and cutting the extruded material, and a step of cooling the granules. The method of the invention is simple and quick to implement.
1. A process for the preparation of polyamide granules, comprising the following steps:
a) extruding a polyamide in the molten state,
b) cooling the extruded polyamide obtained in step a) by contact with a liquid that comprises water,
c) cutting the extruded polyimide into granules,
d) separating the liquid and the extruded polyamide,
e) cooling the granules, separate from the liquid, until a mean temperature of the granules of less than or equal to 55° C. is achieved,
wherein:
step a) is carried out through a die which is placed at the outlet of a polymerization reactor, so that the molten polymer present in the polymerization reactor is directly extruded,
step c) is carried out during step b), after step b) and before step d), or after step d),
the duration of the contact between the extruded polyamide and the liquid is less than or equal to 10 seconds, and
the duration of step e) is less than or equal to 10 minutes,
the polyamide granules obtained in step e) have a moisture content of between 0.1% and 0.4% by weight of water (with respect to the weight of granules).
2. The process as claimed in claim 1 , wherein the cooling liquid is water.
3. The process as claimed in claim 1 , wherein the mean temperature of the granules before step e) is between 60 and 150° C.
4. The process as claimed in claim 1 , wherein step e) is carried out by treatment of the granules with a gas at a temperature of between 0 and 40° C.
5. The process as claimed in claim 4 , wherein the gas of step e) is air.
6. The process as claimed in claim 4 , wherein step e) is carried out using a fluidized bed.
7. The process as claimed in claim 4 , wherein step e) is carried out using a conveyor equipped with a system for direct cooling by injection of air.
8. The process as claimed in claim 1 , wherein step e) is carried out by bringing the granules into contact with a surface, the temperature of which is between 5 and 35° C.
9. The process as claimed in claim 8 , wherein moisture exits from the granules during step e) and is eliminated by natural convection.
10. The process as claimed in claim 8 wherein step e) is carried out using a conveyor equipped with a system for indirect cooling by a jacket in which a cooling fluid circulates at a temperature of between 5 and 35° C.
11. The process as claimed in claim 1 , wherein the process does not comprise a step of drying the polyamide granules in an inert gas environment.
12. The process as claimed in claim 1 , wherein the polyamide granules obtained in step e) have a mean weight of between 1.0 and 5.0 g per 100 granules.
13. The process as claimed in claim 1 , wherein the polyamide granules obtained in step e) have a mean weight of between 1.5 and 4.0 g per 100 granules.
14. A process for the preparation of polyamide granules, comprising the following steps:
a) extruding a polyamide in the molten state,
b) cooling the extruded polyamide obtained in step a) by contact with a liquid that comprises water,
c) cutting the extruded polyamide into granules,
d) separating the liquid and granules,
e) cooling the granules obtained in step d) by injecting air into a fluidized bed of the granules until a mean temperature of the granules of less than or equal to 55° is achieved,
wherein step a) is carried out through a die which is placed at the outlet of a polymerization reactor, so that the molten polymer present in the polymerization reactor is directly extruded,
wherein step e) is carried out during step b) or after step b) and before step d), and the duration of the contact between the extruded polyamide and the liquid is less than or equal to 10 seconds and the duration of step e) is less than or equal to 10 minutes,
wherein the polyamide granules obtained step e) have a moisture content of between 0.1% and 0.4% by weight of water (with respect to the weight of granules).
15. A process for the preparation of polyamide granules, comprising the following steps:
a) extruding a polyamide in the molten state,
b) cooling the extruded polyamide obtained in step a) by contact with a liquid that comprises water,
c) cutting the extruded polyamide into granules,
d) separating the liquid and granules,
e) cooling the granules obtained in step d) by bringing the granules into contact with a cooled surface until a mean temperature of the granules of less than or equal to 55° is achieved,
wherein step a) is carried out through a die which is placed at the outlet of a polymerization reactor, so that the molten polymer present in the polymerization reactor is directly extruded,
wherein step c) is carried out during step b) or after step b) and before step d), and the duration of the contact between the extruded polyimide and the liquid is less than or equal to 10 seconds, and the duration of step e) is less than or equal to 10 minutes,
wherein the polyamide granules obtained in step e) have a moisture content of between 0.1% and 0.4% by weight of water (with respect to the weight of granules).