Omnidirectional high chroma red structural color with combination metal absorber and dielectric absorber layers
View Patent ↗A high-chroma omnidirectional red structural color pigment. The omnidirectional structural color pigment is in the form of a multilayer stack that has a reflective core layer, a metal absorber layer extending across the reflective core layer and a dielectric absorber layer extending across the metal absorber layer. The multilayer stack reflects a single band of visible light with a hue between 0-40°, and preferably between 10-30°, on an a*b* Lab color map. The single band of visible light has a hue shift of less than 30° on the a*b* Lab color map when viewed from all angles between 0-45° normal to an outer surface of the multilayer stack.
1. An omnidirectional high chroma red structural color comprising:
a multilayer stack having:
a reflective core layer;
a metal absorber layer extending across said reflective core layer; and
a dielectric absorber layer extending across said metal absorber layer;
said multilayer stack reflecting a single band of visible light with a hue between 0-40° on an a*b* Lab color map, said single band of visible light having a hue shift within said 0-40° on said a*b* Lab color map when viewed from all angles between 0-45° normal to an outer surface of said multilayer stack.
2. The omnidirectional high chroma red structural color of claim 1 , wherein said hue is between 10-30° and said hue shift is within said 10-30° on said a*b* Lab color map.
3. The omnidirectional high chroma red structural color of claim 1 , wherein said reflective core layer has a thickness between 50-200 nanometers, inclusive.
4. The omnidirectional high chroma red structural color of claim 3 , wherein said reflective core layer is made from a reflective metal selected from the group consisting of Al, Ag, Pt, Sn and combinations thereof.
5. The omnidirectional high chroma red structural color of claim 3 , wherein said reflective core layer is made from a colorful metal selected from the group consisting of Au, Cu, brass, bronze and combinations thereof.
6. The omnidirectional high chroma red structural color of claim 3 , wherein said metal absorber layer has a thickness between 5-500 nanometers, inclusive.
7. The omnidirectional high chroma red structural color of claim 6 , wherein said metal absorber layer is made from the group consisting of Cu, bronze, brass, amorphous Si, Ge, TiN and combinations thereof.
8. The omnidirectional high chroma red structural color of claim 6 , wherein said dielectric absorber layer has a thickness between 5-500 nanometers, inclusive.
9. The omnidirectional high chroma red structural color of claim 8 , wherein said dielectric absorber layer is made from Fe 2 O 3 .
10. The omnidirectional high chroma red structural color of claim 6 , wherein said reflective core layer is a central reflective core layer and said metal absorber layer is a pair of metal absorber layers extending across opposite sides of said central reflective core layer, said central reflective core layer sandwiched between said pair of metal absorber layers.
11. The omnidirectional high chroma red structural color of claim 10 , wherein said dielectric absorber layer is a pair of dielectric absorber layers, said central reflective core layer and said pair of metal absorber layers sandwiched between said pair of dielectric absorber layers.
12. A process for making an omnidirectional high chroma red structural color, the process comprising:
manufacturing a multilayer stack by:
dry depositing a reflective core layer;
dry depositing a metal absorber layer that extends across the reflective core layer;
dry or wet depositing a dielectric absorber layer that extends across the metal absorber layer; and
the multilayer stack reflecting visible light with a hue between 0-40° on an a*b* Lab color map and having a hue shift within the 0-40° on the a*b* Lab color map when viewed from all angles between 0-45° normal to an outer surface of the multilayer stack.
13. The process of claim 12 , wherein the multilayer stack reflects visible light with a hue between 10-30° on the a*b* Lab color map and has the hue shift between the 10-30° on the a*b* Lab color map.
14. The process of claim 12 , wherein the reflective core layer has a thickness between 50-200 nanometers, inclusive.
15. The process of claim 14 , wherein said reflective core layer is made from a reflective metal selected from the group consisting of Al, Ag, Pt, Sn and combinations thereof.
16. The process of claim 14 , wherein the reflective core layer is made from a colorful metal selected from the group consisting of Au, Cu, brass, bronze and combinations thereof.
17. The process of claim 14 , wherein the metal absorber layer has a thickness between 5-500 nanometers, inclusive.
18. The process of claim 17 , wherein the metal absorber layer is made from the group consisting of Cu, bronze, brass, amorphous Si, Ge, TiN and combinations thereof.
19. The process of claim 17 , wherein the dielectric absorber layer has a thickness between 5-500 nanometers, inclusive, and is made from Fe 2 O 3 .