Dental block
A system, method and composition for making a dental ceramics block. The system, method, and composition resulting in natural color matching without drying time between color layers. The system, method and composition also resulting in good color preparation on restorations of about 0.001 mm-1.000 mm thickness.
1. A method of producing an enamel colored zirconia mill blank, the method comprising:
combining cobalt 2-ethyl hexanoate, iron 2-ethyl hexanoate, chromium 2-ethyl hexanoate, and nickel 2-ethyl hexanoate to create an enamel shaded pigment and dissolving the enamel shaded pigment in at least one component selected from the group consisting of hydrocarbons, mineral spirits and phyto-oils to produce a mixed enamel shaded pigment;
combining the mixed enamel shaded pigment with an amount of unpigmented zirconia powder to create a concentrated enamel shaded zirconia;
drying the concentrated enamel shaded zirconia to create a concentrated enamel colored zirconia powder;
serially diluting the concentrated enamel colored zirconia powder into unpigmented zirconia powder to achieve a predetermined enamel color shaded powder;
pressing the predetermined enamel color shaded powder to form a mill blank.
2. The method of claim 1 where the phyto-oil is selected from the group consisting of lavendar oil and d-limonene.
3. The method of claim 1 where the hydrocarbon is 3-methyl-1-butanol.
4. The method of claim 1 where the enamel shaded pigment is dissolved in a mixture comprising d-limonene and 3-mehtyl-1-butanol.
5. The method of claim 1 further wherein the enamel shaded pigment further comprises about 0.1% to about 0.4% calcium tungstate.
6. A method of producing an enamel colored zirconia mill blank, the method comprising:
combining cobalt 2-ethyl hexanoate, iron 2-ethyl hexanoate, chromium 2-ethyl hexanoate, and nickel 2-ethyl hexanoate to create an enamel shaded pigment;
the enamel shaded pigment with at least one component selected from the group consisting of manganese nitrate, cobalt nitrate, chromium nitrate, and iron nitrate;
dissolving the enamel shaded pigment with at least one dissolving agent from the group consisting of water, alcohol and acid to produce a mixed enamel shaded pigment;
combining the mixed enamel shaded pigment with an amount of unpigmented zirconia powder to create a concentrated enamel shaded zirconia;
drying the concentrated enamel shaded zirconia to create a concentrated enamel colored zirconia powder;
serially diluting the concentrated enamel colored zirconia powder into unpigmented zirconia powder to achieve a predetermined enamel color shaded powder;
pressing the predetermined enamel color shaded powder to form a mill blank.
7. The method of claim 6 further wherein the enamel shaded pigment further comprises about 0.1% to about 0.4% calcium tungstate.
8. A method of producing an enamel colored zirconia mill blank, the method comprising:
combining cobalt 2-ethyl hexanoate, iron 2-ethyl hexanoate, chromium 2-ethyl hexanoate, and nickel 2-ethyl hexanoate to create an enamel shaded pigment;
creating an enamel shaded pigment consisting of at least one of Nickel octanoate and copper carboxylate;
dissolving the enamel shaded pigment in at least one component selected from the group consisting of hydrocarbons, mineral spirits and phyto-oils to produce a mixed enamel shaded pigment;
combining the mixed enamel shaded pigment with an amount of unpigmented zirconia powder to create a concentrated enamel shaded zirconia;
drying the concentrated enamel shaded zirconia to create a concentrated enamel colored zirconia powder;
serially diluting the concentrated enamel colored zirconia powder into unpigmented zirconia powder to achieve a predetermined enamel color shaded powder;
pressing the predetermined enamel color shaded powder to form a mill blank.
9. The method of claim 8 where the phyto-oil is selected from the group consisting of lavendar oil and d-limonene.
10. The method of claim 8 where the hydrocarbon is 3-methyl-1-butanol.
11. The method of claim 8 where the enamel shaded pigment is dissolved in a mixture comprising d-limonene and 3-methyl-1-butanol.
12. The method of claim 8 further wherein the enamel shaded pigment further comprises about 0.1% to about 0.4% calcium tungstate.