Golf club head and low density alloy thereof
A golf club head and a low density alloy thereof are provided. The low density alloy has a balanced weight percentage of titanium, 10˜11 wt % aluminum, and trace elements including (C+N+O) <0.2 wt %, silicon <0.2 wt %, and (Fe+Cr+V+Mo) <0.4 wt %. The golf club head has a tensile strength of 90˜110 kips/in 2 , and a density of 4.18˜4.30 g/cm 3 . Through heat treatment at a high temperature of 925±25° C., the precipitation or α 2 phase of the interfacial interphase can be avoided, and thus the embrittlement phenomena can be improved.
1. A golf club head having at least a portion of the golf club head made of a titanium-aluminum alloy, the titanium-aluminum alloy comprising:
10˜11 wt % aluminum;
trace elements comprising (C+N+O)<0.2 wt %,Si<0.2 wt %, and (Fe+Cr+V+Mo) <0.4 wt %; and
the balance being titanium;
wherein the titanium-aluminum alloy is subject to a heat treatment at 925 ±25° C. for 1-4hours to obtain a tensile strength in a range of 90˜110 kips/in 2 and a density in a range of 4.18˜4.30 g/cm 3 , and the titanium-aluminum alloy after the heat treatment has no α2-phase in an interfacial interphase thereof.
2. The golf club head according to claim 1 , wherein the heat treatment is hot isostatic pressing, swaging, or forging.
3. The golf club head according to claim 1 , wherein the time of heat treatment is 1 hour.
4. The golf club head according to claim 1 , wherein the elongation of the titanium-aluminum alloy is 6˜15%.
5. The golf club head according to claim 1 , wherein the volume of the golf club head is ranged between 410 and 470 cm3, and the weight is ranged between 180 and 210 grams.
6. A low density alloy of a golf club head, comprising:
10˜11 wt % aluminum,
trace elements comprising (C+N+O)<0.2 wt %, Si<0.2 wt %, and (Fe+Cr+V+Mo) <0.4 wt %; and
the balance being titanium,
wherein the low density alloy has a tensile strength in a range of 90˜110 kips/in 2 , a density in a range of 4.18˜4.30 g/cm 3 and an elongation in a range of 6˜15%, and the low density alloy has no α2-phase in an interfacial interphase thereof.