Oil, grease, and moisture resistant paperboard
A coated paperboard is disclosed which includes a base coat and top coat containing substantially no fluorochemical or wax, exhibiting good resistance to oil and grease, no tendency toward blocking, and being fully repulpable. Improved moisture resistance is also exhibited.
1. A coated paperboard, comprising:
a paperboard substrate having a first side and a second side;
a base coat in contact with the first side, the base coat comprising binder and pigment, the base coat containing substantially no fluorochemical or wax;
a top coat in contact with the base coat, the top coat comprising binder and pigment, the top coat containing substantially no fluorochemical or wax;
wherein the coated paperboard has a 3M kit test value of at least 10; and
wherein the coated paperboard is repulpable to the extent that after repulping the percentage accepts is at least 99%.
2. The coated paperboard of claim 1 , wherein the 3M kit test value is 12.
3. The coated paperboard of claim 1 , wherein the percentage accepts is at least 99.9%.
4. The coated paperboard of claim 1 , wherein the base coat weight is 5 to 12 lbs per 3000 ft 2 .
5. The coated paperboard of claim 1 , wherein the top coat weight is 2 to 9 lbs per 3000 ft 2 .
6. The coated paperboard of claim 1 , having no tendency toward blocking after being held for 24 hours at 50° C. at a pressure of 100 psi.
7. The coated paperboard of claim 1 , wherein the binder to pigment ratio in the base coat is between 25 to 40 parts binder per 100 parts pigment, by weight.
8. The coated paperboard of claim 1 , wherein the binder to pigment ratio in the top coat is between 25 to 40 parts binder per 100 parts pigment, by weight.
9. The coated paperboard of claim 1 , wherein the binder comprises at least one of styrene acrylate copolymer and styrene-butadiene copolymer.
10. The coated paperboard of claim 1 , wherein the pigment comprises at least one of a clay and calcium carbonate.
11. The coated paperboard of claim 1 , wherein the pigment comprises a No. 1 ultrafine kaolin clay.
12. The coated paperboard of claim 1 , wherein the pigment comprises a high aspect ratio platy clay.
13. The coated paperboard of claim 1 , wherein the pigment comprises at least one of a coarse ground calcium carbonate and a fine ground calcium carbonate.
14. The coated paperboard of claim 1 , wherein the coated paperboard has a water vapor transmission rate of at most 425 grams per square meter per day at 38° C. and 90% relative humidity.
15. The coated paperboard of claim 1 , wherein the coated paperboard has a two-minute Cobb test of at most 20 grams per square meter.
16. The coated paperboard of claim 1 , wherein the binder comprises both styrene acrylate copolymer (SA) and styrene-butadiene copolymer (SBR).
17. The coated paperboard of claim 16 , wherein the binder comprises at least 20% SA and at least 35% SBR.
18. A coated paperboard comprising:
a paperboard substrate having a first side and a second side;
a base coat in contact with the first side, the base coat having a coat weight from 5 to 12 lbs per 3000 ft 2 and comprising binder and pigment , the base coat containing substantially no fluorochemical or wax;
a top coat in contact with the base coat, the top coat having a coat weight from 2 to 9 lbs per 3000 ft 2 and comprising binder and pigment, the top coat containing substantially no fluorochemical or wax;
wherein the coated paperboard has a 3M Kit test value of at least 10, is at least 99% repulpable, and has no tendency toward blocking after being held for 24 hours at 50° C. at a pressure of 100 psi.
19. The coated paperboard of claim 18 , wherein the base coat weight is 6 to 9 lbs per 3000 ft 2 .
20. The coated paperboard of claim 18 , wherein the top coat weight is 3 to 6 lbs per 3000 ft 2 .
21. A method of treating paperboard, the method comprising:
providing a paperboard substrate having a first side and a second side;
applying to the first side a base coat comprising binder and pigment, and containing substantially no fluorochemical or wax;
applying over the base coat a top coat comprising binder and pigment, the top coat containing substantially no fluorochemical or wax;
wherein the resulting treated paperboard has a 3M kit test value of at least 10; and
wherein the coated paperboard is repulpable to the extent that after repulping the percentage accepts is at least 99%.
22. The method of claim 21 , wherein the base coat is applied by a device selected from the group consisting of a blade coater, curtain coater, air knife coater, rod coater, film coater, short-dwell coater, spray coater, and metering film size press.
23. The method of claim 21 , wherein the top coat is applied by a device selected from the group consisting of a blade coater, curtain coater, air knife coater, rod coater, film coater, short-dwell coater, spray coater, and metering film size press.