Rapid hydraulic binder comprising a calcium salt
A hydraulic binder includes a Portland clinker having a Blaine specific surface of 4000 to 5500 cm 2 /g, from 2.5 to 8% of sulphate expressed by mass of SO 3 relative to the mass of clinker, from 1.5 to 10% of calcium nitrite and/or calcium nitrate expressed as anhydrous mass relative to the mass of clinker and from 15 to 50% of a mineral addition including calcium carbonate by mass relative to the total mass of binder.
1. A hydraulic composition comprising
a hydraulic binder comprising a Portland cement clinker having a Blaine specific surface area of 4000 to 5500 cm 2 /g, from 2.5 to 8% of sulphate expressed by mass of SO 3 relative to the mass of clinker, from 1.5 to 10% of calcium nitrite and/or calcium nitrate expressed as anhydrous mass relative to the mass of clinker and from 15 to 50% of a mineral addition comprising calcium carbonate by mass relative to the total mass of binder, and
water,
wherein the quantity of clinker is from 220 to 450 kg/m 3 .
2. The composition according to claim 1 , wherein the quantity of hydraulic binder is greater than or equal to 300 kg/m 3 .
3. A process for production of a hydraulic composition according to claim 1 , comprising mixing the binder with water, wherein the temperature at the time of mixing of the various components with water and the temperature at the time of the setting of the composition is from 5 to 35° C.
4. A shaped article for the construction field comprising the hydraulic composition according to claim 1 .
5. The hydraulic composition according to claim 1 , wherein the hydraulic binder comprises from 2 to 7% of calcium nitrite and/or calcium nitrate expressed as anhydrous mass relative to the mass of clinker.
6. The hydraulic composition according to claim 1 , wherein the hydraulic binder only comprises calcium nitrite.
7. The hydraulic composition according to claim 1 , wherein the hydraulic binder comprises from 25 to 45% of the mineral addition comprising calcium carbonate by mass relative to the total mass of binder.
8. The hydraulic composition according to claim 1 , wherein, in the hydraulic binder, the quantity of clinker is from 40 to 80% by mass relative to the total mass of binder.
9. The hydraulic composition according to claim 1 , wherein the hydraulic binder further comprises a mineral addition other than a mineral addition comprising calcium carbonate.
10. The hydraulic composition according to claim 9 , wherein the mineral addition other than a mineral addition comprising calcium carbonate is selected from the group consisting of pozzolan, fly ash, and any mixture thereof.
11. The hydraulic composition according to claim 1 , wherein, in the hydraulic binder, the quantity of sulphate is at most 4%, expressed by mass of SO 3 relative to the hydraulic binder, the hydraulic binder comprising the clinker, the mineral addition comprising calcium carbonate, the sulphate and optionally a mineral addition other than a mineral addition comprising calcium carbonate.
12. A concrete or mortar having mechanical strength greater than 3 MPa at 6 hours, obtained by hardening the hydraulic composition according to claim 1 .