Curable dental material

1. A curable dental material produced by mixing starting materials, wherein the starting materials to be mixed are exclusively:

one or more polymerizable monomers which form the total amount (A) of the polymerizable monomers in the curable dental material,

one or more particulate fillers which form the total amount (B) of the particulate fillers in the curable dental material, and

one or more auxiliaries which form the total amount (C) of the auxiliaries in the curable dental material,

wherein the total amount (A) of the polymerizable monomers has a refractive index n A in the range from 1.45 to 1.55,

wherein the curable dental material comprises a component (B1) which forms part of the total amount (B), comprising:

(a) nonaggregated and nonagglomerated filler particles having a particle size in the range from 25 to 120 nm of ytterbium fluoride or

(b) nonaggregated and nonagglomerated filler particles having a particle size in the range from 25 to 120 nm of barium sulphate, or

(c) both (a) and (b),

wherein the proportion of component (B1) is

at least 2.5% by weight based on the total mass of the curable dental material, and

at least 90% based on the total mass of filler particles of ytterbium fluoride and barium sulphate in the curable dental material.

2. The curable dental material according to claim 1 , wherein the total amount (A) of the polymerizable monomer(s) has a refractive index n A in the range from 1.48 to 1.55.

3. The curable dental material according to claim 1 , wherein the proportion of component (B1) is within a range from 2.5% by weight to 20% by weight based on the total mass of the curable dental material.

4. The curable dental material according to claim 1 , wherein the total amount (B) of the particulate fillers consists of component (B1) and a component (B2), wherein the total amount of the particulate fillers in component (B2) has a refractive index n B2 in the range from 1.49 to 1.62.

5. The curable dental material according to claim 1 , wherein the proportion of the total amount (B) is in the range from 72% to 92% by weight based on the total amount of the starting materials to be mixed.

6. The curable dental material according to claim 1 , wherein:

the curable dental material has an x-ray opacity of 3.5 mm Al or greater and/or

by polymerizing polymerizable monomers in the curable dental material it is possible to obtain a cured dental material having an x-ray opacity of 3.5 mm Al or greater.

7. The curable dental material according to claim 1 , wherein 70% by weight or more of the particulate fillers which form the total amount (B) of the particulate fillers in the curable dental material have been organically surface-modified.

8. The curable dental material according to claim 1 , wherein component (B1) comprises:

(a) nonaggregated and nonagglomerated filler particles having a particle size in the range from 30 to 100 nm of ytterbium fluoride or

(b) nonaggregated and nonagglomerated filler particles having a particle size in the range from 30 to 100 nm of barium sulphate or

(c) both (a) and (b).

9. The curable dental material according to claim 1 , wherein the starting materials to be mixed are exclusively:

in a total amount in the range from 7.95% to 27.95% by weight, based on the total mass of the starting materials to be mixed, one, two, three or more than three polymerizable monomers which form the total amount (A) of the polymerizable monomers in the curable dental material, wherein the total amount (A) of the polymerizable monomer(s) has a refractive index n A within a range from 1.45 to 1.55,

in a total amount in the range from 72% to 92% by weight, based on the total mass of the starting materials to be mixed, one, two, three or more than three particulate fillers which form the total amount (B) of the particulate fillers in the curable dental material,

in a total amount in the range from 0.05% to 2% by weight, based on the total mass of the starting materials to be mixed, one, two, three or more than three auxiliaries which form the total amount (C) of the auxiliaries in the curable dental material,

wherein the curable dental material comprises a component (B1) which forms part of the total amount (B), comprising of the total amount of the following that are present in the curable dental material:

(a) nonaggregated and nonagglomerated filler particles having a particle size in the range from 25 to 120 nm of ytterbium fluoride, and

(b) nonaggregated and nonagglomerated filler particles having a particle size in the range from 25 to 120 nm of barium sulphate,

wherein the proportion of component (B1) is

2.5% by weight or greater based on the total mass of the curable dental material and

90% by weight or greater based on the total mass of filler particles of ytterbium fluoride and barium sulphate in the curable dental material and

the total amount of the particulate fillers in component (B1) has a refractive index n B1 in the range from 1.55 to 1.64.

10. A cured dental material obtained by polymerizing polymerizable monomers in a curable dental material according to claim 1 .

11. A method of producing a dental product, comprising:

producing or providing a curable dental material according to claim 1 , and

curing the curable dental material into a dental product;

wherein the producing is not effected in a human or animal body,

wherein the dental product is selected from the group consisting of artificial teeth, inlays, onlays, crowns, bridges, mill blanks, implants and dentures.

12. A method for producing a curable dental material according to claim 1 , comprising:

(i) producing or providing a plurality of starting materials, or producing or providing partial mixtures of the plurality of starting materials,

(ii) mixing the starting materials produced or provided in (i) or the partial mixtures produced or provided in (i), so as to result in the curable dental material in each case,

wherein the plurality of starting materials comprise

one or more polymerizable monomers which form the total amount (A) of the polymerizable monomers in the curable dental material,

one or more particulate fillers which form the total amount (B) of the particulate fillers in the curable dental material, and

one or more auxiliaries which form the total amount (C) of the auxiliaries in the curable dental material,

wherein the curable dental material comprises a component (B1) which forms part of the total amount (B), comprising:

(a) nonaggregated and nonagglomerated filler particles having a particle size in the range from 25 to 120 nm of ytterbium fluoride, or

(b) nonaggregated and nonagglomerated filler particles having a particle size in the range from 25 to 120 nm of barium sulphate, or

(c) both (a) and (b),

wherein the proportion of component (B1) is

2.5% by weight or greater than 2.5% by weight, based on the total mass of the curable dental material, and

90% by weight or greater than 90% by weight, based on the total mass of filler particles of ytterbium fluoride and barium sulphate in the curable dental material.

13. A method for producing a cured dental material according to claim 10 , comprising:

(I) producing or providing a curable dental material, and

(II) polymerizing polymerizable monomers in the curable dental material, so as to result in the cured dental material,

wherein the curable dental material comprises:

one or more polymerizable monomers which form the total amount (A) of the polymerizable monomers in the curable dental material,

one more particulate fillers which form the total amount (B) of the particulate fillers in the curable dental material, and

one or more auxiliaries which form the total amount (C) of the auxiliaries in the curable dental material,

wherein the curable dental material comprises a component (B1) which forms part of the total amount (B), comprising:

(a) nonaggregated and nonagglomerated filler particles having a particle size in the range from 25 to 120 nm of ytterbium fluoride, or

(b) nonaggregated and nonagglomerated filler particles having a particle size in the range from 25 to 120 nm of barium sulphate, or

(c) both (a) and (b),

wherein the proportion of component (B1) is

2.5% by weight or greater than 2.5% by weight, based on the total mass of the curable dental material, and

90% by weight or greater than 90% by weight, based on the total mass of filler particles of ytterbium fluoride and barium sulphate in the curable dental material.

14. A kit comprising:

one or more than one dental syringe and

(i) one or more curable dental materials according to claim 1 , and/or

(ii) one or more base pastes and one, two or more than two catalyst pastes, wherein the curable dental material according to claim 1 is obtained by mixing a base paste and the corresponding catalyst paste.

15. A method for a diagnostic method or dental treatment of a patient, comprising:

(1) producing or providing a curable dental material according to claim 1 ,

(2) introducing and positioning the curable dental material produced or provided in the patient's oral cavity and curing the curable dental material or introducing and positioning the cured dental material produced or provided in the patient's oral cavity.

16. The method of claim 15 , wherein the method comprises using the curable dental material for a treatment selected from the group consisting of:

temporary or permanent filling of a dental cavity,

tooth filling material,

dental cement,

dental lining material,

a free-flowing composite material (flow material),

a crown material,

an inlay and/or onlay,

a bridge material and/or

a core build-up material.

17. The method for producing a cured dental material according to claim 13 , wherein:

(a) nonaggregated and nonagglomerated filler particles having a particle size in the range from 25 to 120 nm of ytterbium fluoride and

(b) nonaggregated and nonagglomerated filler particles having a particle size in the range from 25 to 120 nm of barium sulphate, are included in the curable dental material as x-ray-opaque filler in a curable dental material.

18. A method for producing a dental product by means of an additive manufacturing method that uses a digital data model, comprising the steps of:

producing or providing a curable dental material according to claim 1 ,

processing the curable dental material produced or provided in an additive manufacturing method that uses a digital data model, so as to result in the dental product or a precursor of the dental product,

wherein the dental product is selected from the group comprising of artificial teeth, inlays, onlays, crowns, bridges, mill blanks, implants and dentures.

19. The curable dental material according to claim 1 , wherein the filler particles of component (B1) have been organically surface-modified by a first functional group selected from the group consisting of a phosphate, a phosphonate, a carboxylate, a dithiophosphate, a dithiophosphonate, an amine and an amide linked to a second functional group selected from the group consisting of linear or branched alkyl, arenyl and alkenyl groups.

20. The curable dental material according to claim 19 , wherein the first functional group and the second functional group are linked together by a linker selected from the group consisting of linear or branched alkyl chains, aromatic groups, and combinations thereof, each of which may be interrupted by heteroatoms selected from the group consisting of O, N, S, and P.