Fiber-reinforced epoxy resin material, prepreg and, tubular body made of fiber-reinforced epoxy resin material
An object of the present invention is to provide a novel fiber-reinforced epoxy resin material having improved strength. The fiber-reinforced epoxy resin material of the present invention comprises a cured product of an epoxy resin composition and a reinforcing fiber, wherein the epoxy resin composition comprises a novolac type epoxy resin as an epoxy resin component, and the cured product of the epoxy resin composition has a swelling ratio in a range from 20 mass % to 44 mass % in methyl ethyl ketone.
1. A fiber-reinforced epoxy resin material comprising a cured product of an epoxy resin composition and a reinforcing fiber,
wherein the epoxy resin composition comprises an epoxy resin component including a novolac type epoxy resin, and a thermoplastic resin,
the novolac type epoxy resin content in the epoxy resin component ranges from 2 mass % to 10 mass %,
the thermoplastic resin is present in an amount ranging from 2 parts by mass to 12 parts by mass with respect to 100 parts by mass of the epoxy resin component, and
the cured product of the epoxy resin composition has a swelling ratio in a range from 20 mass % to 44 mass % in methyl ethyl ketone at 40° C. for 48 hours.
2. The fiber-reinforced epoxy resin material according to claim 1 , wherein the epoxy resin composition comprises a polyvinyl formal as the thermoplastic resin.
3. The fiber-reinforced epoxy resin material according to claim 1 , wherein the epoxy resin composition comprises dicyandiamide as a curing agent and a urea derivative as a curing accelerator.
4. The fiber-reinforced epoxy resin material according to claim 1 , wherein the epoxy resin composition comprises dicyandiamide as a curing agent in an amount ranging from 13 g to 40 g with respect to 1 mole of an epoxy group of the epoxy resin component.
5. The fiber-reinforced epoxy resin material according to claim 1 , wherein the epoxy resin component comprises the novolac type epoxy resin and a phenoxy type epoxy resin.
6. The fiber-reinforced epoxy resin material according to claim 5 , wherein a mass ratio of the novolac type epoxy resin to the phenoxy type epoxy resin (novolac type epoxy resin/phenoxy type epoxy resin) in the epoxy resin component ranges from 0.4 to 7.
7. The fiber-reinforced epoxy resin material according to claim 5 , wherein the epoxy resin component further comprises a bisphenol A type epoxy resin and a bisphenol F type epoxy resin.
8. The fiber-reinforced epoxy resin material according to claim 5 , wherein a weight average molecular weight of the phenoxy type epoxy resin is 1,000 or more and 130,000 or less.
9. The fiber-reinforced epoxy resin material according to claim 5 , wherein an epoxy equivalent (g/eq) of the phenoxy type epoxy resin is 4,000 or more and 20,000 or less.
10. The fiber-reinforced epoxy resin material according to claim 1 , wherein a content of the reinforcing fiber in the fiber-reinforced epoxy resin material ranges from 65 mass % to 85 mass %.
11. The fiber-reinforced epoxy resin material according to claim 1 , wherein the reinforcing fiber includes a carbon fiber.
12. The fiber-reinforced epoxy resin material according to claim 1 , wherein the reinforcing fiber has a tensile modulus ranging from 10 tf/mm 2 to 70 tf/mm 2 .
13. A prepreg used for preparing a fiber-reinforced epoxy resin material,
wherein the prepreg comprises an epoxy resin composition and a reinforcing fiber,
the epoxy resin composition comprises an epoxy resin component including a novolac type epoxy resin, and a thermoplastic resin,
the novolac type epoxy resin content in the epoxy resin component ranges from 2 mass % to 10 mass %,
the thermoplastic resin is present in an amount ranging from 2 parts by mass to 12 parts by mass with respect to 100 parts by mass of the epoxy resin component, and
a cured product of the epoxy resin composition has a swelling ratio in a range from 20 mass % to 44 mass % in methyl ethyl ketone at 40° C. for 48 hours.
14. The prepreg according to claim 13 , wherein the epoxy resin component comprises the novolac type epoxy resin and a phenoxy type epoxy resin.
15. A tubular body made of a fiber-reinforced epoxy resin material, wherein the fiber-reinforced epoxy resin material comprises a cured product of an epoxy resin composition and a reinforcing fiber,
the epoxy resin composition comprises an epoxy resin component including a novolac type epoxy resin, and a thermoplastic resin,
the novolac type epoxy resin content in the epoxy resin component ranges from 2 mass % to 10 mass %,
the thermoplastic resin is present in an amount ranging from 2 parts by mass to 12 parts by mass with respect to 100 parts by mass of the epoxy resin component, and
the cured product of the epoxy resin composition has a swelling ratio in a range from 20 mass % to 44 mass % in methyl ethyl ketone at 40° C. for 48 hours.
16. A tubular body made of a fiber-reinforced epoxy resin material, wherein the tubular body is obtained by laminating multiple prepregs and curing a resin composition comprised in the prepregs;
the outermost prepreg locating on the outermost side is a prepreg comprising an epoxy resin composition and a reinforcing fiber, in which the epoxy resin composition comprises an epoxy resin component including a novolac type epoxy resin, and a thermoplastic resin,
the novolac type epoxy resin content in the epoxy resin component ranges from 2 mass % to 10 mass %,
the thermoplastic resin is present in an amount ranging from 2 parts by mass to 12 parts by mass with respect to 100 parts by mass of the epoxy resin component, and
a cured product of the epoxy resin composition has a swelling ratio in a range from 20 mass % to 44 mass % in methyl ethyl ketone at 40° C. for 48 hours; and
at least one of the prepregs locating on the inner side of the outermost prepreg has a smaller density than the outermost prepreg.
17. The tubular body made of the fiber-reinforced epoxy resin material according to claim 16 , wherein the reinforcing fiber comprised in the prepreg which has a smaller density than the outermost prepreg has a larger tensile modulus than the reinforcing fiber comprised in the outermost prepreg.
18. The tubular body made of the fiber-reinforced epoxy resin material according to claim 16 , wherein the reinforcing fiber comprised in the outermost prepreg has a tensile modulus ranging from 10 tf/mm 2 to 38 tf/mm 2 , and the reinforcing fiber comprised in the prepreg which has a smaller density than the outermost prepreg has a tensile modulus ranging from 30 tf/mm 2 to 70 tf/mm 2 .
19. A golf club shaft comprising a tubular body made of a fiber-reinforced epoxy resin material, wherein the fiber-reinforced epoxy resin material comprises a cured product of an epoxy resin composition and a reinforcing fiber,
the epoxy resin composition comprises an epoxy resin component including a novolac type epoxy resin, and a thermoplastic resin,
the novolac type epoxy resin content in the epoxy resin component ranges from 2 mass % to 10 mass %,
the thermoplastic resin is present in an amount ranging from 2 parts by mass to 12 parts by mass with respect to 100 parts by mass of the epoxy resin component, and
the cured product of the epoxy resin composition has a swelling ratio in a range from 20 mass % to 44 mass % in methyl ethyl ketone at 40° C. for 48 hours.