Methods of use of calcium hexa aluminate refractory linings and/or chemical barriers in high alkali or alkaline environments
A method for improving the insulating character/and or penetration resistance of a surface comprising lining a surface of a lime kiln, a cement kiln, a roasting kiln, a thermal oxidizer, or a fluidized bed reactor that is subject to wear by an alkali environment and/or an alkaline environment with a refractory composition comprising a refractory aggregate consisting essentially of a calcium hexa aluminate clinker having the formula CA 6 , wherein C is equal to calcium oxide, wherein A is equal to aluminum oxide, and wherein the hexa aluminate clinker has from zero to less than about fifty weight percent C 12 A 7 , and wherein greater than 98 weight percent of the calcium hexa aluminate clinker having a particle size ranging from −20 microns to +3 millimeters, for forming a liner of the surface.
1. A method for manufacturing a liner of a lime kiln, a cement kiln, a roasting kiln, a thermal oxidizer, or a fluidized bed reactor comprising:
lining a surface of a lime kiln, a cement kiln, a roasting kiln, a thermal oxidizer, or a fluidized bed reactor, said lined surface subject to wear by an aqueous alkali environment and/or an aqueous alkaline environment, with a refractory composition comprising greater than 70 percent by weight of a refractory aggregate consisting essentially of a calcium hexa aluminate clinker having the formula CA 6 , wherein C is equal to calcium oxide, wherein A is equal to aluminum oxide, and wherein said hexa aluminate clinker has from zero to less than about fifty weight percent C 12 A 7 , and wherein greater than 98 weight percent of said calcium hexa aluminate clinker having a particle size ranging from −20 microns to +3 millimeters, for forming a liner of said surface prior to contacting said surface with at least one of an alkali material, and an alkaline material, or combinations of said alkali and said alkaline materials; and
providing said liner wherein said refractory composition has a surface that is devoid of thermal expansive glass phases when contacted with said aqueous alkali and/or aqueous alkaline environments below 1830° degrees C.
2. The method of claim 1 including contacting said lined surface with at least one said alkali material, said alkaline material, or combinations thereof, in said aqueous environment.
3. The method of claim 1 including wherein said lined surface is resistant to chemical wear by said alkali material and/or said alkaline material in said aqueous environment.
4. The method of claim 3 including contacting said lined surface with at least one of said alkali material, said alkaline material, and combinations thereof at temperatures ranging from about −20 degrees Centigrade to up to but not including about 1830 degrees Centigrade.
5. The method of claim 1 including wherein said refractory composition comprises one or more of the following of a calcium aluminate cement, a phenolic resin, a hydratable alumina, and an organic polymer as a binder, and combinations thereof.
6. The method of claim 1 including wherein said refractory composition comprises one or more of the following of an alumina, a MgO, a Mg(OH) 2 , a spinel, a graphite, a zirconia, and a zirconia containing compound, and combinations thereof.
7. The method of claim 1 including wherein said refractory composition comprises one or more of the following of a fiber, an alumina, and a surfactant, and combinations thereof.
8. The method of claim 1 including wherein said refractory composition comprises one or more sized fractions of said CA 6 clinker.
9. The method of claim 1 including wherein said lined surface functions as a refractory lining.
10. The method of claim 1 including wherein said lined surface functions as a chemical barrier that is substantially resistant to attack by at least one or more of said alkali material, alkaline material, and combinations thereof, in said aqueous environment.