Bioactive glass scaffolds, and method of making
A glass, glass-ceramic, or ceramic bead is described, with an internal porous scaffold microstructure that is surrounded by an amorphous shield. The shield serves to protect the internal porous microstructure of the shield while increasing the overall strength of the porous microstructure and improve the flowability of the beads either by themselves or in devices such as biologically degradable putty that would be used in bone or soft tissue augmentation or regeneration. The open porosity present inside the bead will allow for enhanced degradability in-vivo as compared to solid particles or spheres and also promote the growth of tissues including but not limited to all types of bone, soft tissue, blood vessels, and nerves.
1. A shielded glass scaffold comprising
sintered 45S5 bioactive glass fibers and 45S5 bioactive glass beads, some of the fibers and beads being bonded to one another to create a sintered, porous agglomerate having a melted and then cooled shield of fused glass about the sintered agglomerate, thereby forming the shielded glass scaffold.
2. The shielded glass scaffold of claim 1 wherein the fibers are 20 μm to 3 mm in length and 300 nm to 30 μm in diameter.
3. The shielded glass scaffold of claim 1 wherein 90% of the beads are from 30 to 425 μm in diameter.
4. The shielded glass scaffold of claim 1 wherein there are 10 to 60% fibers and 40 to 90% beads.
5. The shielded glass scaffold of claim 1 wherein there is 25% fibers and 75% beads.
6. A glass scaffold comprising sintered fibers and sintered beads formed from two or more different glass compositions and being a sintered agglomerate with a melted and cooled shield of fused glass about the sintered agglomerate.
7. The glass scaffold of claim 6 including glass beads that have a mean particle size of about 25 μm with 90% less than 53 μm.
8. The glass scaffold of claim 6 wherein some of the fibers and beads are not fused to one another.