Method for laser welding one or more workpieces made of hardenable steel in a butt joint
A method for laser welding one or more workpieces made of press-hardenable steel in a butt joint, wherein the workpiece or workpieces have a thickness of between 0.5 and 1.8 mm, and/or a jump in thickness of between 0.2 and 0.4 mm occurs at the butt joint, and wherein laser welding is carried out with the feed of filler wire into the molten bath, which is generated only by at least one laser beam. The filler wire contains at least one alloy element from the group comprising manganese, chromium, molybdenum, silicon and/or nickel, which alloy element promotes the formation of austenite in the molten bath generated by the laser beam, wherein said at least one alloy element is present in the filler wire in a mass percentage greater by at least 0.1 wt. % than in the steel of the workpiece or workpieces and the workpiece or workpieces used are non-coated or the coating thereof is partially removed.
1. A method for laser welding one or more workpieces made of press-hardenable steel in a butt joint, wherein the one or more workpieces have a thickness of between 0.5 and 1.8 mm, or a jump in thickness of between 0.2 and 0.4 mm occurs at the butt joint, or the one or more workpieces have a thickness of between 0.5 and 1.8 mm and a jump in thickness of between 0.2 and 0.4 mm occurs at the butt joint, comprising the steps of:
generating a molten bath with only at least one laser beam;
carrying out the laser welding with a feed of filler wire into the molten bath,
wherein the filler wire contains at least one alloy element from the group comprising manganese, chromium, molybdenum, silicon and nickel, wherein the at least one alloy element promotes formation of austenite in the molten bath generated by the at least one laser beam,
wherein the at least one alloy element is present in the filler wire in a mass percentage greater by at least 0.1 wt. % than in the press-hardenable steel of the one or more workpieces,
wherein the one or more workpieces used are non-coated or partially de-coated by ablation of their coating before the laser welding in a peripheral region along an abutting to be welded together,
wherein filler wire comprises:
0.05 to 0.15 wt. % C,
0.5 to 2.0 wt. % Si,
1.0 to 2.5 wt. % Mn,
0.5 to 2.0 wt. % Cr+Mo, and
1.0 to 4.0 wt. % Ni,
remainder Fe and unavoidable impurities, and
wherein the filler wire has a carbon mass percentage which is lower by at least 0.1 wt. % than the press-hardenable steel of the workpiece or workpieces.
2. The method according to claim 1 , wherein the steel of the one or more workpieces has the following composition:
0.16 to 0.50 wt. % C,
max. 0.40 wt. % Si,
0.50 to 2.00 wt. % Mn,
max. 0.025 wt. % P,
max. 0.010 wt. % S,
max. 0.60 wt. % Cr,
max. 0.50 wt. % Mo,
max. 0.050 wt. % Ti,
0.0008 to 0.0070 wt. % B, and
min. 0.010 wt. % Al,
remainder Fe and unavoidable impurities.
3. The method according to claim 1 , wherein the filler wire is fed in a heated state to the molten bath.
4. The method according to claim 3 , wherein at least a length portion of the filler wire is heated to a temperature of at least 50° C. before it is fed into the molten bath.
5. The method according to claim 1 , wherein inert gas is applied to the molten bath during laser welding.
6. The method according to claim 5 , wherein the inert gas used is pure argon or a mixture of argon and carbon dioxide.
7. The method according to claim 1 , wherein the partially de-coated one or more workpieces used have a surface layer based on aluminium or on aluminium-silicon.