Preparation method of graphene/metal composite board
A method for preparing a graphene/metal composite sheet includes adding polyvinyl alcohol into distilled water and heat to about 100° C. under stirring to prepare a polyvinyl alcohol solution; dispersing graphene in distilled water using ultrasonication to prepare a graphene solution; mixing the polyvinyl alcohol solution and the graphene solution to form a graphene/polyvinyl alcohol mixed slurry; after a metal sheet is subjected to a surface activation treatment, coating the graphene/polyvinyl alcohol mixed slurry onto the metal sheet at both upper and lower surfaces; vacuum sintering to remove the polyvinyl alcohol in the surface coating to obtain a graphene/metal plate; overlaying at least two graphene/metal plates and bonding them together via hot isostatic pressing to form multilayer graphene/metal plates; and hot rolling the bonded multilayer graphene/metal plates to form the graphene/metal composite sheet.
1. A method for preparing a graphene/metal composite sheet, wherein: the method comprises:
adding polyvinyl alcohol into distilled water and heat to about 100° C. under stirring to prepare a polyvinyl alcohol solution;
dispersing graphene in distilled water using ultrasonication to prepare a graphene solution;
mixing the polyvinyl alcohol solution and the graphene solution to form a graphene/polyvinyl alcohol mixed slurry;
after a metal sheet is subjected to a surface activation treatment, coating the graphene/polyvinyl alcohol mixed slurry onto the metal sheet at both upper and lower surfaces;
vacuum sintering to remove the polyvinyl alcohol in the surface coating to obtain a graphene/metal plate;
overlaying at least two graphene/metal plates and bonding them together via hot isostatic pressing to form multi layer graphene/metal plates; and
hot rolling the bonded multilayer graphene/metal plates to form the graphene/metal composite sheet.
2. The method of claim 1 , wherein the ultrasonication is for about 30 minutes.
3. The method of claim 1 , wherein the graphene/polyvinyl alcohol mixed slurry is coated onto the metal sheet by spraying.
4. The method of claim 1 , wherein the thickness of the coating is greater than 100 μm.
5. The method of claim 1 , wherein the vacuum sintering temperature is 500° C.
6. The method of claim 1 , wherein the hot isostatic pressing is done at a temperature of about 480° C.
7. The method of claim 1 , wherein the hot isostatic pressing is done at a pressure of about 110 MPa.
8. The method of claim 1 , wherein the hot isostatic pressing lasts for about two hours.
9. The method of claim 1 , wherein the hot rolling is done at a temperature between about 440° C. and 480° C.
10. The method of claim 1 , wherein the polyvinyl alcohol solution has a weight:volume ratio of polyvinyl alcohol:water of about 1:9.
11. The method of claim 1 , wherein the graphene solution has a weight:volume ratio of graphene:water of about 1:19.