Metal oxide dispersion, polymerizable composition comprising the metal oxide dispersion, and polymer thereof
An objective of the present invention is to provide an organic-inorganic hybrid acrylic polymer having an increased refractive index, which has a higher transparency and a less impaired scratch resistance; a metal oxide dispersion and a polymerizable composition as materials for the polymer; and the organic-inorganic hybrid polymer capable of being produced in a crack-free manner. Another objective of the present invention is to provide a high-performance antireflection film using the organic-inorganic hybrid polymer. The metal oxide dispersion of the present invention comprises a phosphorus compound represented by Formula (1): (wherein, R 1 is a hydrogen atom, an alkyl group, an alkynyl group, an alkenyl group, an aryl group, an aliphatic heterocyclic group, or an aromatic heterocyclic group; R 2 is an organic residue; and n is 1 or 2) and a metal oxide.
1. A method for producing a polymer, said method comprising:
producing a titanium oxide dispersion in the sol form comprising a phosphorus compound of Formula (1):
wherein R 1 is a hydrogen atom, an alkyl group, an alkynyl group, an alkenyl group, an aryl group, an aliphatic heterocyclic group, or an aromatic heterocyclic group; R 2 is an organic residue; and n is 1 or 2, by hydrolysis and condensation of a reaction mixture comprising titanium alkoxide or titanium halide and the phosphorous compound of Formula (I) in an organic solvent; and
curing the titanium oxide dispersion to obtain a polymer.
2. A method for producing a titanium oxide dispersion in the sol form comprising a phosphorus compound of the following Formula (1):
wherein R 1 is a hydrogen atom, an alkyl group, an alkynyl group, an alkenyl group, an aryl group, an aliphatic heterocyclic group, or an aromatic heterocyclic group; R 2 is an organic residue; and n is 1 or 2, said method comprising hydrolysis and condensation of a reaction mixture comprising titanium alkoxide or titanium halide and the phosphorus compound of Formula (I) in an organic solvent.
3. The method according to claim 1 , wherein R 1 is a hydrogen atom or a linear or branched alkyl group having 1 to 5 carbon atoms.
4. The method according to claim 1 , wherein R 2 is an organic residue of Formula (2):
wherein Y is a linear or branched alkylene group having 1 to 10 carbon atoms; and p is an integer of 1 to 10.
5. The method according to claim 4 , wherein Y in Formula (2) is a linear or branched alkylene group having 1 to 4 carbon atoms.
6. The method according to claim 1 , wherein the molar ratio of the phosphorus atom in the phosphorus compound to the titanium atom in the titanium alkoxide is 0.04 to 1.00.
7. The method according to claim 1 , wherein the average diameter of titanium oxide is 0.03-0.5 μm.
8. The method according to claim 1 , wherein the reaction mixture for the hydrolysis and condensation comprises tetraalkoxytitanium, a compound of Formula (3):
in which n is 1 or 2, and water.
9. The method according to claim 1 , wherein the titanium alkoxide and the phosphorus compound of Formula (I) are reacted under the irradiation of microwave.