Complex oxide, method for producing same and exhaust gas purifying catalyst
Disclosed are a composite oxide which is capable of maintaining a large specific surface area even used in a high temperature environment, and which has excellent heat resistance and reducibility, as well as a method for producing the composite oxide and a catalyst for exhaust gas purification employing the composite oxide. The composite oxide contains cerium and at least one of rare earth metal elements other than cerium and including yttrium, at a mass ratio of 85:15 to 99:1 in terms oxides, and further containing silicon at more than 0 parts by mass and not more than 20 parts by mass in terms of SiO 2 with respect to 100 parts by mass of the total of the cerium and the at least one of rare earth metal elements other than cerium and including yttrium, wherein the composite oxide has a specific surface area of not less than 40 m 2 /g as measured by the BET method after calcination at 900° C. for 5 hours, and a reducibility of not lower than 30% as calculated from measurement of temperature-programmed reduction from 50° C. to 900° C. after calcination at 1000° C. for 5 hours, and is particularly suitable for a co-catalyst for a catalyst for exhaust gas purification.
1. A composite oxide consisting of
(a) cerium;
(b) at least one of rare earth metal elements other than cerium, at a mass ratio of 85:15 to 99:1 in terms oxides; and
(c) silicon at more than 0 parts by mass and not more than 20 parts by mass in terms of SiO 2 with respect to 100 parts by mass of a total of said cerium (a) and said at least one of rare earth metal elements other than cerium (b),
wherein said composite oxide has properties of exhibiting a specific surface area of not less than 40 m 2 /g as measured by BET method after calcination at 900° C. for 5 hours, and a reducibility of not lower than 30% as calculated from measurement of temperature-programmed reduction from 50° C. to 900° C. after calcination at 1000° C. for 5 hours.
2. The composite oxide according to claim 1 having a property of exhibiting a specific surface area of not less than 60 m 2 /g as measured by BET method after calcination at 900° C. for 5 hours.
3. The composite oxide according to claim 1 having a property of exhibiting a specific surface area of not less than 25 m 2 /g as measured by BET method after calcination at 1000° C. for 5 hours.
4. The composite oxide according to claim 1 having a property of exhibiting a reducibility of not lower than 40% as calculated from measurement of temperature-programmed reduction from 50° C. to 900° C. after calcination at 1000° C. for 5 hours.
5. The composite oxide according to claim 1 , wherein a content of silicon (c) is 5 to 20 parts by mass in terms of SiO 2 with respect to 100 parts by mass in total of said cerium (a) and said at least one of rare earth metal elements other than cerium (b) in terms of oxides.
6. A method for producing a composite oxide of claim 1 comprising the steps of:
(a) providing a cerium solution not less than 90 mol % of which cerium ions are tetravalent,
(b) heating and maintaining said cerium solution obtained from step (a) up to and at not lower than 60° C.,
(c) adding an oxide precursor of at least one of rare earth metal elements other than cerium, to a cerium suspension obtained through said heating and maintaining,
(d) heating and maintaining said cerium suspension containing said oxide precursor of at least one of rare earth metal elements other than cerium up to and at not lower than 100° C.,
(e) adding a precipitant to the suspension obtained from step (d) to obtain a precipitate,
(f) calcining said precipitate,
(g) impregnating an oxide obtained through said calcining, with a solution of a silicon oxide precursor, and
(h) calcining said oxide impregnated with the solution of a silicon oxide precursor.
7. A method for producing a composite oxide of claim 1 comprising the steps of:
(A) providing a cerium solution not less than 90 mol % of which cerium ions are tetravalent,
(B) heating and maintaining said cerium solution obtained from step (A) up to and at not lower than 60° C.,
(C) adding a silicon oxide precursor and an oxide precursor of at least one of rare earth metal elements other than cerium, to a cerium suspension obtained through said heating and maintaining,
(D) heating and maintaining said cerium suspension containing said silicon oxide precursor and said oxide precursor of at least one of rare earth metal elements other than cerium, up to and at not less than 100° C.,
(E) adding a precipitant to the suspension obtained from step (D) to obtain a precipitate, and
(F) calcining said precipitate thus obtained.
8. The method according to claim 6 wherein a cerium content of said cerium solution in step (a) or (A) is 5 to 100 g/L in terms of CeO 2 .
9. A catalyst for exhaust gas purification comprising the composite oxide according to claim 1 .