Mineralized wood materials and methods providing mineralized wood materials

1. A mineralized wood material comprising at least one metal salt of the formula MA in the lumina of the mineralized wood material, in particular in the lumina and the cell walls of the mineralized wood material, wherein the at least one metal salt MA comprises a weight in the range of 5 wt % to 40 wt % with respect to the weight of the unmineralized wood material and A is selected from inorganic compounds.

2. The mineralized wood material according to claim 1 , wherein

M is selected from multivalent metals, in particular from earth alkali metals, more particularly from magnesium, barium or calcium and

A is selected from inorganic compounds, more particularly from sulfate, carbonate, borate, fluoride or phosphate.

3. A method for treatment of a wood material comprising the steps of:

a) provision of a metal salt solution comprising at least one metal salt of the formula MX dissolved in a solvent and a salt solution comprising at least one salt of the formula YA dissolved in another solvent,

b) treatment of said wood material by

an impregnation cycle comprising a first impregnation step using one of said solutions and a subsequent second impregnation step using the other one of said solutions, or

a diffusion step comprising a diffusion of the metal salt solution from one side and a diffusion of the salt solution from the other side into the wood material, and

c) providing a precipitation of a metal salt of the formula MA inside the wood material yielding a mineralized wood material,

wherein

the weight of said metal salt MA of said mineralized wood material is between 5 wt % and 40 wt % in relation to the weight of the unmineralized wood material, and the solvents of the metal salt solution and the salt solution are characterized in that the metal salt MA has a low or almost no solubility in said solvents, in particular the metal salt MA has a solubility below 0.01 g per 100 mL in said solvents and A is selected from inorganic compounds.

4. The method for treatment of wood according to claim 3 , wherein in said first impregnation step said metal salt solution is used and in said subsequent second impregnation step said salt solution is used, providing a metal salt of the formula MA.

5. The method according to claim 3 , wherein one of the solvents, in particular the solvent of the metal salt solution, is an organic solvent and the other one of the solvents is water, in particular the solvent of the salt solution is water.

6. A method for treatment of a wood material comprising the steps of:

a) provision of a solution comprising at least one metal salt of the formula MX dissolved in dimethyl carbonate or diethyl carbonate,

b) impregnation of wood with at least one impregnation step using said solution, c) hydrolysis of the impregnated wood with an aqueous solution, in particular with an aqueous solution comprising a pH range of more than 7, providing a metal carbonate.

7. The method according to claim 3 , wherein M is selected from multivalent metals, in particular from earth alkali metals, more particularly from magnesium, barium or calcium.

8. The method according to claim 3 , wherein A is selected from sulfate, carbonate, borate, fluoride or phosphate.

9. The method according to claim 3 , wherein Y is selected from monovalent compounds, in particular from alkali metals, more particularly from sodium or potassium.

10. The method according to claim 3 , wherein X is selected from nitrate, bromide, iodide or chloride, in particular from bromide, iodide or chloride, more particularly X is chloride.

11. The method for treatment of wood according to claim 6 , wherein the pH is in the range of 8.5 to 9.5, in particular said pH is approximately 9.

12. The method according to claim 3 , wherein the impregnation of step is performed for 2 to 24 hours and/or the impregnation cycle is performed for several times, in particular for 1, 2, 3 or 4 times.

13. The method according to claim 3 , wherein the concentration of the metal salt MX in the metal salt solution is in the range of 0.1 to 5 mol/l, in particular 0.5 to 2.5 mol/l, more particularly 1 to 2 mol/l, and the concentration of the salt YA in the salt solution is in the range of 0.1 to 5 mol/l, in particular 0.5 to 2.5 mol/l, more particularly 0.5 to 1.5 mol/l.

14. The method according to claim 6 , wherein the solution comprises a concentration of the metal salt MX in the range of 0.1 to 5 mol/l, in particular 0.5 to 2.5 mol/l, more particularly 0.5 to 1.5 mol/l.