Alkali-swellable crosslinked acrylate copolymer, methods of manufacture thereof, and composition comprising the same
View Patent ↗A rheology modifier including: a water-dispersible, alkali-swellable crosslinked polyacrylate copolymer including 0.02 to 5 weight percent of polysaccharide grafts, based on a total weight of the copolymer.
1. A rheology modifier comprising:
a water-dispersible, alkali-swellable crosslinked polyacrylate copolymer comprising 0.02 to 5 weight percent of polysaccharide grafts, based on a total weight of the copolymer.
2. The rheology modifier of claim 1 , comprising:
20 to 75 weight percent of units derived from an α,β-ethylenically mono-unsaturated carboxylic acid monomer;
20 to 60 weight percent of units derived from an ethylenically unsaturated ester of (meth)acrylic acid; and
0.01 to 1 weight percent of crosslinks derived from a polyethylenically unsaturated crosslinker,
each based on a total weight of the copolymer.
3. The rheology modifier of claim 2 , wherein the α,β-ethylenically mono-unsaturated carboxylic acid monomer is (meth)acrylic acid, maleic acid, itaconic acid, fumaric acid, crotonic acid, aconitic acid, or a combination thereof.
4. The rheology modifier of claim 2 , wherein the ethylenically unsaturated ester of (meth)acrylic acid is a C1 to C30 alkyl ester, a C1 to C30 arylalkyl ester, a C1 to C30 hydroxyalkyl ester, a C1 to C30.
5. The rheology modifier of claim 3 , wherein the ethylenically unsaturated ester of (meth)acrylic acid is methyl (meth)acrylate, ethyl acrylate, 2-ethylhexyl acrylate, butyl acrylate, benzyl acrylate, or a combination thereof.
6. The rheology modifier of claim 2 , wherein the crosslinker is trimethylolpropane diallyl ether, trimethylolpropane triallyl ether, diallyl phthalate, allyl methacrylate, or a combination thereof.
7. The rheology modifier of claim 1 , wherein the polysaccharide is a cellulose ether, a gum, a starch, or a combination thereof.
8. The rheology modifier of claim 7 , wherein the cellulose ether is hydroxyethyl cellulose, hydroxypropyl cellulose, hydroxyethyl methyl cellulose, hydroxypropyl methyl cellulose, hydroxypropylhydroxyethyl cellulose, carboxymethyl cellulose, carboxyethyl cellulose, or combination thereof.
9. The rheology modifier of claim 8 , wherein the cellulose ether is a hydroxyethyl cellulose having a viscosity of 1 to 5000 centipoise, when determined for a 2 weight percent aqueous solution comprising by Brookfield viscometry using a #1 spindle.
10. The rheology modifier of claim 7 , wherein the gum is guar gum, locust bean gum, xanthan gum, hydroxyethyl guar gum, methyl guar gum, ethyl guar gum, hydroxypropyl guar gum, hydroxyethylmethyl guar gum, hydroxypropylmethyl guar gum, or a combination thereof.
11. The rheology modifier of claim 7 , wherein the starch is methyl starch, ethyl starch, hydroxyethylmethyl starch, hydroxypropyl starch, hydroxypropylmethyl starch, or a combination thereof.
12. The rheology modifier of claim 1 , wherein the crosslinked polysaccharide-grafted polyacrylate copolymer further comprises 0.1 to 20 weight percent of units derived from a vinyl ester.
13. The rheology modifier of claim 12 , wherein the vinyl ester is vinyl acetate, vinyl neodecanoate, or a combination thereof.
14. A method of preparing a rheology modifier, the method comprising:
providing an emulsion comprising a water-dispersible, alkali-swellable crosslinked polyacrylate copolymer; and
contacting the emulsion with an aqueous grafting solution comprising a water-dispersible polysaccharide in the presence of a free-radical initiator to form an alkali-swellable crosslinked polysaccharide-grafted polyacrylate copolymer comprising 0.1 to 5 weight percent of polysaccharide grafts, based on a total weight of the copolymer, to form the rheology modifier.
15. The method of claim 14 , wherein the alkali-swellable crosslinked polysaccharide-grafted polyacrylate copolymer comprises 20 to 75 weight percent of units derived from an α,β-ethylenically mono-unsaturated carboxylic acid monomer.
16. The method of claim 14 , wherein the providing an emulsion comprising a water-dispersible, alkali-swellable crosslinked polyacrylate copolymer comprises:
contacting
20 to 75 weight percent of an α,β-ethylenically mono-unsaturated carboxylic acid monomer,
20 to 60 weight percent of an ethylenically unsaturated ester of (meth)acrylic acid,
0.01 to 1 weight percent of a crosslinking monomer comprising a polyunsaturated compound,
a surfactant, a free-radical initiator, and water, each based on a total weight of the α,β-ethylenically mono-unsaturated carboxylic acid monomer, the ethylenically unsaturated ester of (meth)acrylic acid, the crosslinking monomer; and
polymerizing the α,β-ethylenically mono-unsaturated carboxylic acid monomer, the ethylenically unsaturated ester of (meth)acrylic acid, and the crosslinking monomer to form the emulsion comprising the water-dispersible, alkali-swellable crosslinked polyacrylate copolymer.
17. The method of claim 16 , wherein the surfactant is present in an amount of 0.1 to 5 weight percent, based on a total weight of the α,β-ethylenically mono-unsaturated carboxylic acid monomer, the ethylenically unsaturated ester of (meth)acrylic acid, and the crosslinking monomer.
18. The method of claim 14 , wherein the rheology modifier is in the form of an emulsion comprising the alkali-swellable crosslinked polysaccharide-grafted polyacrylate copolymer comprising 0.1 to 5 weight percent of polysaccharide grafts.
19. A composition comprising the rheology modifier of claim 1 .