Fusion formable lithium aluminosilicate glass ceramic
A down-drawable glass ceramic. The glass ceramic has a composition which yields a liquidus viscosity that enables formation of the parent glass by down-draw techniques such as fusion-draw and slot-draw methods. The resulting glass ceramic is white or translucent in appearance with high strength achieved through heat treatment of the fusion-formed glass.
1. A glass, the glass being cerammable and comprising from about 72 wt % to about 85 wt % SiO 2 , from about 7 wt % to about 11 wt % Al 2 O 3 , from about 4.3 wt % to about 6.5 wt % Li 2 O, and from about 4 wt % to about 9 wt % K 2 O, wherein the glass has a composition located within an area defined by a ternary eutectic of β-spodumene-lithium disilicate-tridymite in the SiO 2 —Al 2 O 3 —Li 2 O system and a binary eutectic of orthoclase-tridymite in the SiO 2 —Al 2 O 3 —K 2 O system, and wherein the ternary eutectic and binary eutectic occur at temperatures of less than about 1000° C., wherein the glass has a liquidus viscosity of at least about 100 kP, and wherein the glass comprises 0 wt % of at least one of TiO 2 and ZrO 2 .
2. The glass of claim 1 , further comprising up to 2.6 wt % Na 2 O.
3. The glass of claim 1 , further comprising up to about 5 wt % BaO.
4. The glass of claim 1 , further comprising up to about 3.0 wt % ZnO.
5. The glass of claim 1 , further comprising from about OA wt % to about 5.0 wt % P 2 O 5 .
6. A glass, the glass being cerammable and comprising from about 72 wt % to about 85 wt % SiO 2 , from about 7 wt % to about 11 wt % Al 2 O 3 , from about 4.3 wt % to about 6.5 wt % Li 2 O, from about 4 wt % to about 9 wt % K 2 O, and 0.0001 wt % to about 0.1 wt % of at least one noble metal, wherein the glass has a composition located within an area defined by a ternary eutectic of β-spodumene-lithium disilicate-tridymite in the SiO 2 —Al 2 O 3 —Li 2 O system and a binary eutectic of orthoclase-tridymite in the SiO 2 —Al 2 O 3 —K 2 O system, and wherein the ternary eutectic and binary eutectic occur at temperatures of less than about 1000° C., and the glass has a liquidus viscosity of at least about 100 kP.
7. The glass of claim 6 , wherein the at least one noble metal comprises silver.
8. The glass of claim 1 , wherein the glass has a liquidus viscosity of at least about 120 kpoise.
9. The glass of claim 8 , wherein the glass has a liquidus viscosity of at least about 150 kpoise.
10. The glass of claim 6 , further comprising up to 2.6 wt % Na 2 O.
11. The glass of claim 6 , further comprising up to about 5 wt % BaO.
12. The glass of claim 6 , further comprising up to about 3.0 wt % ZnO.
13. The glass of claim 6 , further comprising from about 0.1 wt % to about 5.0 wt % P 2 O 5 .
14. The glass of claim 6 , wherein the at least one noble metal comprises Ag, Au, Pt, Pd, or Rh.
15. The glass of claim 6 , wherein the glass has a liquidus viscosity of at least about 120 kpoise.
16. The glass of claim 15 , wherein the glass has a liquidus viscosity of at least about 150 kpoise.
17. A glass, the glass being cerammable and comprising from about 72 wt % to about 85 wt % SiO 2 , from about 7 wt % to about 11 wt % Al 2 O 3 , from about 4.3 wt % to about 6.5 wt % Li 2 O, and from about 4 wt % to about 9 wt % K 2 O, wherein the glass has a composition located within an area defined by a ternary eutectic of β-spodumene-lithium disilicate-tridymite in the SiO 2 —Al 2 O 3 —Li 2 O system and a binary eutectic of orthoclase-tridymite in the SiO 2 —Al 2 O 3 —K 2 O system, and wherein the ternary eutectic and binary eutectic occur at temperatures of less than about 1000° C., wherein the glass has a liquidus viscosity of at least about 100 kP, and wherein the glass further comprises Na 2 O.
18. The glass of claim 7 , wherein the glass further comprises at least one of 0.005 wt % to about 0.5 wt % CeO 2 , 0.005 wt % to about 0.5 wt % SnO 2 , and 0.005 wt % to about 0.5 wt % Sb 2 O 3 .