Printable compostable paperboard
A coated paperboard is disclosed which includes a printable coating containing substantially no fluorochemical or wax in which the coated paperboard is fully compostable as well as repulpable, and exhibits no tendency toward blocking. The coating may be a multiple layer coating.
1. A coated paperboard comprising:
a paperboard substrate having a first side and a second side;
a multilayer coating having two or more layers in contact with the first side of the paperboard substrate, the multilayer coating comprising a base coating in contact with the paperboard substrate, the base coating having a coat weight from 6 to 10 lbs per 3000 ft 2 and comprising binder and pigment, and a top coating forming the outermost layer of the multilayer coating, the top coating having a coat weight from 3 to 10 lbs per 3000 ft 2 and comprising binder and pigment;
wherein the coated paperboard has a caliper of at least 0.010″; and
wherein the coated paperboard is compostable according to the ASTM D6868-11 standard for compostability.
2. The coated paperboard of claim 1 , wherein the multilayer coating is further applied in contact with the second side of the paperboard substrate.
3. The coated paperboard of claim 1 , wherein the multilayer coating has two layers, and wherein the top coating is formed in contact with the base coating.
4. The coated paperboard of claim 1 , wherein the multilayer coating is a printable coating.
5. The coated paperboard of claim 1 , wherein the coated paperboard has a caliper of at least 0.012″.
6. The coated paperboard of claim 1 , wherein the binder to pigment ratio in the multilayer coating is between 10 to 25 parts binder per 100 parts pigment, by weight.
7. The coated paperboard of claim 6 , wherein the binder to pigment ratio in the multilayer coating is between 12 to 22 parts binder per 100 parts pigment, by weight.
8. The coated paperboard of claim 1 , wherein the binder comprises one or more synthetic polymer binders.
9. The coated paperboard of claim 8 , wherein the binder further comprises one or more additional natural biodegradable binders.
10. The coated paperboard of claim 9 , wherein the additional biodegradable binders include at least one of polysaccharide, protein, and derivatives thereof.
11. The coated paperboard of claim 9 , wherein the additional biodegradable binder comprises between 1 to 10 parts per 100 parts pigment, by weight.
12. The coated paperboard of claim 1 , wherein the coated paperboard is repulpable to the extent that after repulping the percentage accepts is at least 99%.
13. The coated paperboard of claim 12 , wherein the percentage accepts is at least 99.9%.
14. The coated paperboard of claim 1 , wherein the multilayer coating includes two layers, and wherein the total coating weight is 9 to 20 lbs per 3000 ft'.
15. The coated paperboard of claim 1 , having no tendency toward blocking after being held for 24 hours at 50° C. at a pressure of 100 psi.
16. The coated paperboard of claim 1 , wherein the pigment comprises at least one of a clay and calcium carbonate.
17. A coated paperboard comprising:
a paperboard substrate having a first side and a second side;
a coating having at least one layer in contact with the first side of the paperboard substrate, the coating having a coat weight from 9 to 15 lbs per 3000 ft 2 and comprising binder and pigment;
wherein the coated paperboard has a caliper of at least 0.010″; and
wherein the coated paperboard is compostable according to the ASTM D6868-11 standard for compostability.
18. A method of treating paperboard, the method comprising:
providing a paperboard substrate having a first side and a second side;
applying to the first side a multilayer coating having two or more layers, by applying a base coating in contact with the paperboard substrate, the base coating having a coat weight from 6 to 10 lbs per 3000 ft 2 and comprising binder and pigment, and applying a top coating forming the outermost layer of the multilayer coating, the top coating having a coat weight from 3 to 10 lbs per 3000 ft 2 and comprising binder and pigment;
wherein the treated paperboard has a caliper of at least 0.010″; and
wherein the treated paperboard is compostable according to the ASTM D6868-11 standard for compostability.
19. The method of claim 18 , comprising the further step of applying the multilayer coating to the second side of the paperboard substrate.
20. The method of claim 18 , wherein the treated paperboard is repulpable to the extent that after repulping the percentage of accepts is at least 99%.
21. The method of claim 18 , wherein the coating is applied by a device selected from the group consisting of a blade coater, curtain coater, air knife coater, rod coater, film coater, short-dwell coater, spray coater, and metering film size press.