Dental composite compositions for reduced shrinkage stress
A dental composite composition is disclosed that includes a polymerizable resin, filler particles, and at least one polymerizable stable radical. A variety of polymerizable stable radicals may be employed, including those that have a 2,2,6,6-tetramethylpiperidinyl-1-oxyl moiety. Compositions as described herein exhibit excellent mechanical strength, hardness, and flexural modulus, while also significantly decreasing shrinkage stress caused by polymerization.
1. A dental composite composition comprising a free-radically polymerizable (meth)acrylate resin, 75 percent by weight or greater of filler particles, and about 0.005 percent to about 5 percent by weight of at least one polymerizable stable radical, the dental composite composition having a flexural modulus after polymerization of about 9500 MPa or greater;
wherein the polymerizable stable radical reduces shrinkage stress of the dental composite composition caused by polymerization by 10% or greater.
2. The dental composite composition of claim 1 , wherein the polymerizable stable radical is selected from the group consisting of phenothiazine, 2,2-diphenyl-1-picrylhydrazyl radicals, galvinoxyl radicals, triphenylmethyl radicals, and (meth)acrylate substituted or unsubstituted 2,2,6,6-tetramethylpiperidinyl-1-oxyl radicals, and combinations thereof.
3. The dental composite composition of claim 1 , wherein the polymerizable stable radical comprises:
in which R is selected from the group consisting of: —Z, —XZ, —XY 1 Z, —X(Z)(Z), —X(Y 1 Z)(Y 2 Z), —X(Z)(Z)(Z), and —X(Y 1 Z)(Y 2 Z)(Y 3 Z);
wherein X, when present, is N, O, S, C—O, C—O—O, S—O, S—O—O, P—O, P—O—O, or P—O—O—O;
wherein Y 1 , Y 2 , and Y 3 are independently, when present, aryl or substituted aryl, linear or branched alkyl or aryl-alkyl; and
wherein Z, independently, is an unsaturated functional group.
4. The dental composite composition of claim 3 , wherein Y 1 , Y 2 , and Y 3 are independently (CH 2 ) n ; (CH 2 CH 2 O) n ; or (CH 2 CHCH 3 O) n , with n=0-20.
5. The dental composite composition of claim 3 , wherein Z, independently, is vinyl, acrylamide, methacrylamide, acrylate, or methacrylate.
6. The dental composite composition of claim 3 , wherein the polymerizable stable radical comprises a compound selected from the group consisting of:
and combinations thereof.
7. The dental composite composition of claim 3 , wherein the polymerizable stable radical comprises N,N-Bis-(3-oxa-4-oxo-6-methacryloyloxyhexyl)-4-amino-2,2,6,6 tetramethylpiperdin-1-oxyl radical.
8. The dental composite composition of claim 1 , wherein the polymerizable stable radical is present from about 0.03 percent by weight to about 1 percent by weight of the dental composite composition and the polymerizable stable radical reduces shrinkage stress of the dental composite composition caused by polymerization by 20% or greater.
9. The dental composite composition of claim 1 , wherein the free-radically polymerizable (meth)acrylate resin comprises a compound selected from the group consisting of 2,2-bis[4-(2-hydroxy-3-methacryloyloxypropoxy)phenyl] propane (Bis-GMA), 1,6-bis(2-methacryloxyethoxycarbonylamino)-2,4,4-trimethylhexane (UDMA), 2,2-bis[4-(methacryloyloxy-ethoxy)phenyl] propane (or ethoxylated bisphenol A-dimethacrylate) (EBPADMA), isopropyl methacrylate, triethyleneglycol dimethacrylate, diethyleneglycol dimethacrylate, tetraethyleneglycol dimethacrylate, 3-(acryloyloxy)-2-hydroxypropyl methacrylate, 1,3-propanediol dimethacrylate, 1,6-hexanediol di(meth)acrylate, 1,12-dodecanediol dimethacrylate, pentaerythritol triacrylate, pentaerythritol tetraacrylate, pentaerythritol tetramethacrylate, and combinations thereof.
10. The dental composite composition of claim 1 , further comprising a photoinitiator.
11. The dental composite composition of claim 1 , wherein the filler particles are present at about 90 percent or less by weight of the dental composite composition.
12. The dental composite composition of claim 11 , wherein the filler particles comprise a mixture of micron-sized radiopaque filler particles and nano-sized filler particles.
13. A dental composite composition comprising:
a free-radically polymerizable resin selected from the group consisting of 2,2-bis[4-(2-hydroxy-3-methacryloyloxypropoxy)phenyl] propane (Bis-GMA), 1,6-bis(2-methacryloxyethoxycarbonylamino)-2,4,4-trimethylhexane (UDMA), 2,2-bis[4-(methacryloyloxy-ethoxy)phenyl] propane (or ethoxylated bisphenol A-dimethacrylate) (EBPADMA), isopropyl methacrylate, triethyleneglycol dimethacrylate, diethyleneglycol dimethacrylate, tetraethyleneglycol dimethacrylate, 3-(acryloyloxy)-2-hydroxypropyl methacrylate, 1,3-propanediol dimethacrylate, 1,6-hexanediol di(meth)acrylate, 1,12-dodecanediol dimethacrylate, pentaerythritol triacrylate, pentaerythritol tetraacrylate, pentaerythritol tetramethacrylate, and combinations thereof;
75 to about 90 percent by weight filler particles;
about 0.05 to about 1 percent by weight photoinitiator; and
about 0.005 percent to about 5 percent by weight of a polymerizable stable radical containing a 2,2,6,6-tetramethylpiperidinyl-1-oxyl moiety and having the following formula:
in which R is selected from the group consisting of: —Z, —XZ, —XY 1 Z, —X(Z)(Z), —X(Y 1 Z)(Y 2 Z), —X(Z)(Z)(Z), and —X(Y 1 Z)(Y 2 Z)(Y 3 Z);
wherein X, when present, is N, O, S, C—O, C—O—O, S—O, S—O—O, P—O, P—O—O, or P—O—O—O;
wherein Y 1 , Y 2 , and Y 3 are independently, when present, aryl or substituted aryl, linear or branched alkyl or aryl-alkyl;
wherein Z, independently, is an unsaturated functional group;
wherein the dental composite composition has a flexural modulus after polymerization of about 9500 MPa or greater; and
wherein the polymerizable stable radical reduces shrinkage stress of the dental composite composition caused by polymerization by 10% or greater.
14. The dental composite composition of claim 13 , wherein the polymerizable stable radical is selected from the group consisting of:
and combinations thereof.
15. The dental composite composition of claim 13 , wherein the polymerizable stable radical is present from about 0.015 percent by weight to about 3 percent by weight of the dental composite composition.
16. The dental composite composition of claim 13 , wherein the polymerizable stable radical comprises N,N-Bis-(3-oxa-4-oxo-6-methacryloyloxyhexyl)-4-amino-2,2,6,6 tetramethylpiperdin-1-oxyl radical.
17. The dental composite composition of claim 13 , wherein the filler particles comprise a mixture of micron-sized radiopaque filler particles and nanofiller particles.
18. The dental composite composition of claim 1 comprising 80 percent by weight or greater of filler particles, the dental composite composition having a flexural modulus after polymerization of about 10300 MPa or greater.
19. The dental composite composition of claim 1 , wherein the dental composite composition has a flexural strength after polymerization of about 140 MPa or greater.
20. The dental composite composition of claim 1 , wherein the polymerizable stable radical is present from about 0.016 percent by weight to about 0.3 percent by weight of the dental composite composition.