Bentonite modifier, modified bentonite, and use thereof
View Patent ↗The present disclosure relates to a bentonite modifier, comprising a water-soluble thiosulfate, a water-soluble alcohol compound, and a water-soluble amine compound, wherein the amounts of thiosulfate, the alcohol compound, and the amine compound are in the ratio of (0.3˜1):(0.3˜1):(0.3˜1). The present disclosure further relates to a bentonite-containing cement additive capable of resisting permeation and salt corrosion, comprising bentonite and said modifier, wherein the content of the bentonite modifier is 0.2˜5% of the bentonite by weight. Meanwhile, the present disclosure also provides use of the modified bentonite.
1. A cement additive capable of resisting permeation and salt corrosion, consisting of a modified bentonite and a bentonite texturizer, wherein
the modified bentonite consists of bentonite and a bentonite modifier, wherein, the bentonite modifier consists of a water-soluble thiosulfate, a water-soluble alcohol compound, and a water-soluble amine compound, wherein the mass ratio of the thiosulfate to the alcohol compound to the amine compound is (0.3˜1):(0.3˜1):(0.3˜1), and the content of the bentonite modifier is 0.2˜5% of the bentonite by weight,
the bentonite has a crystalline structure,
the bentonite texturizer is a mixture of active silica powder and a water reducer, and
the amounts of the modified bentonite, the active silica powder, and the water reducer by weight are in the ratio of 100:(3˜30):(0.3˜3.5).
2. The additive of claim 1 , wherein said active silica powder is at least one of fine powder with 80 μm screen residue ≤12% manufactured from a silicon industrial waste residue, an amorphous SiO 2 powder, and a natural SiO 2 mineral.
3. The additive of claim 1 , wherein said water reducer is at least one selected from the group consisting of naphthalene-based water reducers, melamine sulfonate-based water reducers, polycarboxylate-based water reducers, sulfamate-based water reducers, and modified lignosulfonate-based water reducers.
4. A cement capable of resisting permeation and salt corrosion, comprising cement clinker, and the cement additive capable of resisting permeation and salt corrosion according to claim 1 , wherein the content of said cement additive accounts for 4% to 20% of the total weight of the cement.
5. The cement capable of resisting permeation and salt corrosion of claim 4 , wherein the content of said cement additive accounts for 5% to 15% of the total weight of the cement.
6. The additive of claim 2 , wherein said amorphous SiO 2 powder is white carbon black, and said natural SiO 2 mineral is silica stone or diatomite.
7. The additive of claim 1 , wherein the water-soluble thiosulfate is at least one selected from the group consisting of lithium thiosulfate, sodium thiosulfate, and potassium thiosulfate.
8. The additive of claim 1 , wherein the water-soluble alcohol compound is at least one selected from the group consisting of polyol, polyvinyl alcohol, and polyethylene glycol.
9. The additive of claim 1 , wherein the water-soluble amine compound is at least one selected from the group consisting of triethanolamine, isopropanol amine, hydrazine hydrate, water-soluble alkylamines, and alkenamides.
10. The additive of claim 8 , wherein said polyol is ethylene glycol and/or isopropanol, and said polyethylene glycol is at least one selected from the group consisting of polyethylene glycol 200 (PEG 200), polyethylene glycol 400 (PEG 400), and polyethylene glycol 600 (PEG 600).