Ceramic capacitor dielectric material
A ceramic capacitor dielectric material includes BaTiO 3 , BaZrO 3 , SrTiO 3 , MgCO 3 , SiO 2 , and at least one compound selected from transition element and rare earth element. The amount of the BaTiO 3 in the ceramic capacitor dielectric material is 40-80 mol %; the amount of the BaZrO 3 is 20-40 mol %; and the amount of the SrTiO 3 is smaller than or equal to 20 mol %. The permittivity of the ceramic capacitor dielectric material is larger than 350, and the dielectric loss is lower than 0.5%. Moreover, the resistivity can reach 10 12 Ω-cm under room temperature, and further reach 10 11 Ω-cm at 125° C. Besides that, the performance of the capacitance change rate of the ceramic capacitor dielectric material under DC bias is excellent, thus the ceramic capacitor dielectric material can fulfill the X7T dielectric properties of EIA.
1. A ceramic capacitor dielectric material comprising 40-65 mol % of BaTiO 3 , 20-40 mol % of BaZrO 3 , 5-20 mol % of SrTiO 3 , 2-6 mol % of MgCO 3 , 2 mol % of SiO 2 , and 0.5-10 mol % of at least one compound selected from the group consisting of La 2 O 3 , CeO 2 , Pr 6 O 11 , Nd 2 O 3 , Pm 2 O 3 , Sm 2 O 3 , Eu 2 O 3 , Gd 2 O 3 , Dy 2 O 3 , Ho 2 O 3 , Er 2 O 3 , Tm 2 O 3 , Yb 2 O 3 Nb 2 O 5 , WO 3 , Ta 2 O 5 , CoCO 3 , CuO, MnCO 3 , Cr 2 O 3 , TiO 2 , ZrO 2 , Sc 2 O 3 , NiO, and ZnO.
2. The ceramic capacitor dielectric material according to claim 1 , wherein a dielectric loss of the ceramic capacitor dielectric material under room temperature is smaller than 0.5%.
3. The ceramic capacitor dielectric material according to claim 1 , wherein a capacitance change rate of the ceramic capacitor dielectric material between −55 to 125° C. is +22% to −33%.