Durable antimicrobial treatments for textiles and other substrates
This invention relates to regenerable antimicrobial coatings with long-lasting efficacy for use in medical applications including implants, medical instruments or devices, and hospital equipment. The same coatings would also have broad utility in the consumer, industrial, and institutional markets. The coating technology would be based on sequestration of hydrogen peroxide (HP) by zinc oxide binders incorporated into the coatings.
1. A liquid water-borne formulation for imparting durable antimicrobial activity to a substrate, wherein said formulation is an aqueous dispersion, suspension, emulsion, or solution comprising:
a. a metal derivative, wherein said metal derivative is a hydroxide, an oxide, or a peroxide of a metal selected from the group consisting of zinc, magnesium, titanium, and zirconium, and wherein the metal derivative is 0.1% to 15% (w/w) of the formulation,
b. a polymer, wherein the water absorbency of said polymer is between 0.5% and 20% (w/w), and wherein the polymer is up to 50% (w/w) of the formulation and
c. hydrogen peroxide, wherein the hydrogen peroxide concentration is between 0.1% and 10% (w/w) of the formulation.
2. The liquid water-borne formulation of claim 1 , wherein the metal derivative is 0.25% to 5% (w/w) of the formulation.
3. The liquid water-borne formulation of claim 1 , wherein the metal derivative is 0.5% to 2.5% (w/w) of the formulation.
4. The liquid water-borne formulation of claim 1 , wherein the hydrogen peroxide concentration is between 0.5% to 7.0% (w/w) of the formulation.
5. The liquid water-borne formulation of claim 1 , wherein the hydrogen peroxide concentration is between 1.0% to 5.0% (w/w) of the formulation.
6. The water-borne formulation of claim 1 , wherein said polymer is selected from the group consisting of polyacrylonitrile, acrylonitrile butadiene styrene (ABS) polymer, acrylic (PMMA), celluloid, cellulose acetate, ethylene-vinyl acetate (EVA), ethylene vinyl alcohol (EVOH), fluoropolymers (PTFE, FEP, PFA, CTFE, ECTFE, ETFE), ionomers, acrylic/PVC alloy, liquid crystal polymer (LCP), polyacetal (POM or Acetal), polyacrylates (acrylic), polyacrylonitrile (PAN or acrylonitrile), polyamide (PA or Nylon), polyamide-imide (PAI), polyaryletherketone (PAEK or Ketone), polybutadiene (PBD), polybutylene (PB), polybutylene terephthalate (PBT), polycaprolactone (PCL), polychlorotrifluoroethylene (PCTFE), polyethylene terephthalate (PET), polycyclohexylene dimethylene terephthalate (PCT), polycarbonate (PC), polyhydroxyalkanoates (PHAs), polyketone (PK), polyester, polyethylene (PE), polyetheretherketone (PEEK), polyetherketoneketone (PEKK), polyetherimide (PEI), polyethersulfone (PES), polyethylenechlorinates (PEC), polyimide (PI), polylactic acid (PLA), polymethylpentene (PMP), polyphenylene oxide (PPO), polyphenylene sulfide (PPS), polyphthalamide (PPA), polypropylene (PP), polystyrene (PS), polysulfone (PSU), polytrimethylene terephthalate (PTT), polyurethane (PU), polyvinyl acetate (PVA), polyvinyl chloride (PVC), polyvinylidene chloride (PVDC); styrene-acrylonitrile (SAN), silicone polymers, thermoplastics, thermosets, elastomers; and copolymers, blends, and mixtures thereof.
7. The water-borne formulation of claim 1 , wherein said polymer is selected from the group of polyurethanes, polyacrylates, and mixtures thereof.
8. The water-borne formulation of claim 1 , wherein said metal derivative is selected from the group consisting of zinc hydroxide, zinc peroxide, zinc oxide, zinc oxide nanoparticles, and zinc oxide micron particles.
9. A method of enhancing and regenerating durable antimicrobial activity of the surface of a substrate, wherein said method comprises the steps of:
a. providing, on the surface of a substrate on which durable antimicrobial activity is desired, a water-borne coating formulation for imparting durable antimicrobial activity to a substrate, wherein said formulation is an aqueous dispersion, suspension, emulsion, or solution comprising,
i. a metal derivative, wherein said metal derivative is a hydroxide, an oxide, or a peroxide of a metal selected from the group consisting of zinc, magnesium, titanium, and zirconium, and wherein the metal derivative is 0.1% to 15% of the formulation
ii. a polymer, wherein the water absorbency of said polymer is between 0.5% and 20% (w/w), and wherein the polymer is up to 50% of the formulation, and
iii. hydrogen peroxide, wherein the hydrogen peroxide concentration is between 0.1% and 10% of the formulation, and
b. drying said substrate.
10. The method of claim 9 , wherein said polymer is selected from the group consisting of polyacrylonitrile, acrylonitrile butadiene styrene (ABS) polymer, acrylic (PMMA), celluloid, cellulose acetate, ethylene-vinyl acetate (EVA), ethylene vinyl alcohol (EVOH), fluoropolymers (PTFE, FEP, PFA, CTFE, ECTFE, ETFE), ionomers, acrylic/PVC alloy, liquid crystal polymer (LCP), polyacetal (POM or Acetal), polyacrylates (acrylic), polyacrylonitrile (PAN or acrylonitrile), polyamide (PA or Nylon), polyamide-imide (PAT), polyaryletherketone (PAEK or Ketone), polybutadiene (PBD), polybutylene (PB), polybutylene terephthalate (PBT), polycaprolactone (PCL), polychlorotrifluoroethylene (PCTFE), polyethylene terephthalate (PET), polycyclohexylene dimethylene terephthalate (PCT), polycarbonate (PC), polyhydroxyalkanoates (PHAs), polyketone (PK), polyester, polyethylene (PE), polyetheretherketone (PEEK), polyetherketoneketone (PEKK), polyetherimide (PEI), polyethersulfone (PES), polyethylenechlorinates (PEC), polyimide (PI), polylactic acid (PLA), polymethylpentene (PMP), polyphenylene oxide (PPO), polyphenylene sulfide (PPS), polyphthalamide (PPA), polypropylene (PP), polystyrene (PS), polysulfone (PSU), polytrimethylene terephthalate (PTT), polyurethane (PU), polyvinyl acetate (PVA), polyvinyl chloride (PVC), polyvinylidene chloride (PVDC); styrene-acrylonitrile (SAN), silicone polymers, thermoplastics, thermosets, elastomers; and copolymers, blends, and mixtures thereof.
11. The method of claim 9 , wherein said polymer is selected from the group of polyurethanes, polyacrylates, and mixtures thereof.
12. The method of claim 9 , wherein the polymer is a mixture that further comprises a hydrophilic acrylic polymer.
13. The method of claim 9 , wherein said metal derivative is selected from the group consisting of zinc hydroxide, zinc peroxide, zinc oxide, zinc oxide nanoparticles, and zinc oxide micron particles.
14. The method of claim 9 , wherein said substrate is a textile article, wherein said textile article comprises cotton, rayon, polyester, nylon, or acrylic.
15. The method of claim 14 , wherein the textile article is selected from the group consisting of a diaper, a surgical gown, an isolation gown, a lab coat, a glove, surgical scrubs, a head cover, a hair cover, a face mask, a floor mat, a lamp handle cover, an exam table cover, a cast liner, a splint liner, padding, a mattress cover, bedding, a sheet, a towel, clothing, underwear, a sock, shoe-cover, a protective garment for military or other use, apparel for food handling, and carpet.
16. A regenerable antimicrobial water-borne coating on a substrate comprising,
a. a metal derivative, wherein said metal derivative is a hydroxide, an oxide, or a peroxide of a metal selected from the group consisting of zinc, magnesium, titanium, and zirconium,
b. a polymer, wherein said polymer is doped with 1% to 90% (w/w) of said metal derivative, and
c. sequestered hydrogen peroxide,
wherein the water absorbency of said polymer is between 0.5% and 20% (w/w), wherein said polymer doped with said metal derivative has been determined to be capable of sequestering hydrogen peroxide when exposed to said source of aqueous hydrogen peroxide; wherein the antimicrobial activity of said doped polymer can be regenerated on subsequent exposure to aqueous hydrogen peroxide,
whereby said antimicrobial coating, when tested using ASTM Standard Method E2180 at least 24 hours after preparation, provides at least a 3-log reduction of viable Escherichia coli bacteria greater than that of a corresponding coating which has not been exposed to hydrogen peroxide.
17. The regenerable antimicrobial coating of claim 16 , wherein said polymer is selected from the group consisting of polyacrylonitrile, acrylonitrile butadiene styrene (ABS) polymer, acrylic (PMMA), celluloid, cellulose acetate, ethylene-vinyl acetate (EVA), ethylene vinyl alcohol (EVOH), fluoropolymers (PTFE, FEP, PFA, CTFE, ECTFE, ETFE), ionomers, acrylic/PVC alloy, liquid crystal polymer (LCP), polyacetal (POM or Acetal), polyacrylates (acrylic), polyacrylonitrile (PAN or acrylonitrile), polyamide (PA or Nylon), polyamide-imide (PAI), polyaryletherketone (PAEK or Ketone), polybutadiene (PBD), polybutylene (PB), polybutylene terephthalate (PBT), polycaprolactone (PCL), polychlorotrifluoroethylene (PCTFE), polyethylene terephthalate (PET), polycyclohexylene dimethylene terephthalate (PCT), polycarbonate (PC), polyhydroxyalkanoates (PHAs), polyketone (PK), polyester, polyethylene (PE), polyetheretherketone (PEEK), polyetherketoneketone (PEKK), polyetherimide (PEI), polyethersulfone (PES), polyethylenechlorinates (PEC), polyimide (PI), polylactic acid (PLA), polymethylpentene (PMP), polyphenylene oxide (PPO), polyphenylene sulfide (PPS), polyphthalamide (PPA), polypropylene (PP), polystyrene (PS), polysulfone (PSU), polytrimethylene terephthalate (PTT), polyurethane (PU), polyvinyl acetate (PVA), polyvinyl chloride (PVC), polyvinylidene chloride (PVDC); styrene-acrylonitrile (SAN), silicone polymers, thermoplastics, thermosets, elastomers; and copolymers, blends, and mixtures thereof.
18. The regenerable antimicrobial coating of claim 16 , wherein said metal derivative is selected from the group consisting of zinc hydroxide, zinc peroxide, zinc oxide, zinc oxide nanoparticles, and zinc oxide micron particles.
19. The regenerable antimicrobial coating of claim 16 , wherein said water-borne coating comprises a self-crosslinking linking acrylic dispersion or a self-crosslinking polyurethane dispersion, and further comprises an alcohol, a glycol, a defoamer, a photoinitiator, a thermal stabilizer, an anti-oxidant, a surfactant, or a mixture thereof.
20. The regenerable antimicrobial coating of claim 16 , wherein said substrate is a textile article, wherein said textile article comprises cotton, rayon, polyester, nylon, acrylic, or a mixture thereof.