Method for growing a silicon single crystal while suppressing a generation of slip dislocations in a tail portion
A method for growing a silicon single crystal includes determining a diameter to give the maximum value of a ratio of an equivalent stress and a critical resolved shear stress in a tail portion on the occasion of the gradual cooling of the silicon single crystal in an after-heating step, in advance; wherein, the tail portion is grown in the tail forming step under a condition that an interstitial oxygen concentration at a position of the determined diameter is 8.8×10 17 atoms/cm 3 (ASTM '79) or more. This method for growing a silicon single crystal by a CZ method can efficiently grow a heavy weight and large-diameter silicon single crystal while suppressing a generation of slip dislocations in the tail portion of the silicon single crystal in the after-heating step to gradually cool the crystal after finishing the tail forming step.
1. A method for growing a silicon single crystal by a Czochralski method, comprising: bringing a seed crystal into contact with a raw material melt, growing an enlarging-diameter portion in a cone forming step, growing a straight body portion successive to the enlarging-diameter portion in a straight body forming step, decreasing the diameter of the straight body portion gradually to form a tail portion in a tail forming step, separating the silicon single crystal from the melt followed by gradual cooling of the silicon single crystal in an after-heating step to grow the silicon single crystal, and
determining a diameter to give the maximum value of a ratio of an equivalent stress and a critical resolved shear stress in the tail portion on the occasion of the gradual cooling of the silicon single crystal in the after-heating step, in advance; wherein,
the tail portion is grown in the tail forming step under a condition that an interstitial oxygen concentration at a position of the determined diameter is 8.8×10 17 atoms/cm 3 (ASTM '79) or more.
2. The method for growing a silicon single crystal according to claim 1 , wherein the silicon single crystal is grown in the cone forming step to have a diameter of the enlarging-diameter portion being 450 mm or more.
3. The method for growing a silicon single crystal according to claim 1 , wherein the silicon single crystal is grown in the tail forming step to have a length of the tail portion being 450 mm or less.
4. The method for growing a silicon single crystal according to claim 2 , wherein the silicon single crystal is grown in the tail forming step to have a length of the tail portion being 450 mm or less.
5. The method for growing a silicon single crystal according to claim 1 , wherein
the after-heating step runs for 2.5 hours or more, and
the after-heating step is performed with the position of the determined diameter being at a height of 186 mm or more from the surface of the melt at the end of the after-heating step.
6. The method for growing a silicon single crystal according to claim 2 , wherein
the after-heating step runs for 2.5 hours or more, and
the after-heating step is performed with the position of the determined diameter being at a height of 186 mm or more from the surface of the melt at the end of the after-heating step.
7. The method for growing a silicon single crystal according to claim 3 , wherein
the after-heating step runs for 2.5 hours or more, and
the after-heating step is performed with the position of the determined diameter being at a height of 186 mm or more from the surface of the melt at the end of the after-heating step.
8. The method for growing a silicon single crystal according to claim 4 , wherein
the after-heating step runs for 2.5 hours or more, and
the after-heating step is performed with the position of the determined diameter being at a height of 186 mm or more from the surface of the melt at the end of the after-heating step.
9. The method for growing a silicon single crystal according to claim 1 , wherein the diameter to give the maximum value of the ratio of the equivalent stress and the critical resolved shear stress in the tail portion is determined by simulation.