Method of producing a sulfide solid electrolyte material, sulfide solid electrolyte material, and lithium battery

1. A method of producing a sulfide solid electrolyte material, comprising:

forming a vitrified intermediate having crosslinking sulfur but no Li 2 S, by vitrifying, in a first vitrification process, a starting material composition obtained by mixing Li 2 S and a sulfide of a group 14 or group 15 element such that a molar proportion of Li 2 S with respect to a sum total of the Li 2 S and the sulfide of the group 14 or group 15 element is smaller than a molar proportion of Li 2 S required for the sulfide solid electrolyte material to obtain an ortho composition; and

eliminating the crosslinking sulfur by vitrifying, in a second vitrification process conducted after the first vitrification process, an intermediate-containing composition resulting from mixing a bond cleaving compound with the vitrified intermediate such that a molar proportion of a sum total of the Li 2 S and the bond cleaving compound with respect to a sum total of the Li 2 S, the sulfide of the group 14 or group 15 element and the bond cleaving compound is a value not smaller than the molar proportion of Li 2 S required for the sulfide solid electrolyte material to obtain the ortho composition, the bond cleaving compound cleaving a bond of the crosslinking sulfur, wherein

the first vitrification process includes a mechanochemical reaction,

the second vitrification process includes a mechanochemical reaction, and

the bond cleaving compound is Li 2 O.

2. The production method according to claim 1 , wherein a molar proportion in which the bond cleaving compound is mixed with the intermediate is a molar proportion in which a sulfide solid electrolyte material substantially free of crosslinking sulfur is obtained.

3. The production method according to claim 1 , wherein:

the sulfide of the group 14 or group 15 element is P 2 S 5 ; and

in the starting material composition, the proportion of the Li 2 S with respect to the sum total of the Li 2 S and the P 2 S 5 is smaller than 75%, on a molar basis.

4. The production method according to claim 1 , wherein:

the sulfide of the group 14 or group 15 element is P 2 S 5 ;

in the starting material composition, the proportion of the Li 2 S with respect to the sum total of the Li 2 S and the P 2 S 5 is smaller than 75%, on a molar basis; and

in the intermediate-containing composition, the proportion of the sum total of the Li 2 S and the Li 2 O with respect to the sum total of the Li 2 S, the P 2 S 5 and the Li 2 O is not smaller than 75%, on the molar basis.

5. The production method according to claim 1 , wherein:

the sulfide of the group 14 or group 15 element is GeS 2 ; and

in the starting material composition, the proportion of the Li 2 S with respect to the sum total of the Li 2 S and the GeS 2 is smaller than 66.7%, on a molar basis.

6. The production method according to claim 1 , wherein:

the sulfide of the group 14 or group 15 element is GeS 2 ;

in the starting material composition, the proportion of the Li 2 S with respect to the sum total of the Li 2 S and the GeS 2 is smaller than 66.7%, on a molar basis; and

in the intermediate-containing composition, the proportion of the sum total of the Li 2 S and the Li 2 O with respect to the sum total of the Li 2 S, the GeS 2 and the Li 2 O is not smaller than 66.7%, on the molar basis.

7. The production method according to claim 1 , wherein:

the sulfide of the group 14 or group 15 element is SiS 2 ; and

in the starting material composition, the proportion of the Li 2 S with respect to the sum total of the Li 2 S and the SiS 2 is smaller than 66.7%, on a molar basis.

8. The production method according to claim 1 , wherein:

the sulfide of the group 14 or group 15 element is SiS 2 ;

in the starting material composition, the proportion of the Li 2 S with respect to the sum total of the Li 2 S and the SiS 2 is smaller than 66.7%, on a molar basis; and

in the intermediate-containing composition, the proportion of the sum total of the Li 2 S and the Li 2 O with respect to the sum total of the Li 2 S, the SiS 2 and the Li 2 O is not smaller than 66.7%, on the molar basis.

9. The production method according to claim 1 , wherein: the first vitrification process is mechanical milling.

10. The production method according to claim 1 , wherein: the second vitrification process is mechanical milling.

11. A method of producing a sulfide solid electrolyte material, comprising:

forming a vitrified intermediate having crosslinking sulfur but no Li 2 S, by vitrifying, in a first vitrification process, a starting material composition obtained by mixing Li 2 S and P 2 S 5 such that a molar proportion of Li 2 S with respect to the sum total of the Li 2 S and P 2 S 5 is smaller than a molar proportion of Li 2 S required for the sulfide solid electrolyte material to obtain an ortho composition; and

eliminating the crosslinking sulfur by vitrifying, in a second vitrification process conducted after the first vitrification process, an intermediate-containing composition resulting from mixing Li 2 O with the vitrified intermediate, the Li 2 O cleaving a bond of the crosslinking sulfur, wherein

the first vitrification process includes a mechanochemical reaction,

the second vitrification process includes a mechanochemical reaction,

a molar proportion in which the Li 2 O is mixed with the intermediate is a molar proportion in which a sulfide solid electrolyte material substantially free of crosslinking sulfur is obtained,

in the starting material composition, a proportion of the Li 2 S with respect to a sum total of the Li 2 S and the P 2 S 5 is smaller than 75%, on a molar basis, and

in the intermediate-containing composition, the proportion of a sum total of the Li 2 S and the Li 2 O with respect to a sum total of the Li 2 S, the P 2 S 5 and the Li 2 O is not smaller than 75%, on the molar basis.