Powder polymer, method for the preparation thereof, and use as a thickener
A cross-linked anionic polyelectrolyte resulting from the polymerization, for 100 mol %: (i) of a proportion no smaller than 30 mol % and smaller than 99.5 mol % monomer units from a monomer having a partially or totally salified strong acid function; (ii) of a proportion no smaller than 0.5 mol % and no greater than 5 mol % monomer units from at least one monomer having Formula (I): CH 2 ═CH(CH 3 )—C(=0)—OR 1 (I), wherein Ri is an alkyl radical including 6 to 18 carbon atoms; (iii) of a proportion greater than 0 mol % and no greater than 5 mol % monomer units from at least one diethylene or polyethylene cross-linking monomer; and (iv) optionally, of a proportion smaller than 69.5 mol % monomer units from a neutral monomer. Also, a method for preparing the polyelectrolyte and to the use thereof as a thickener in topical compositions.
1. A crosslinked anionic polyelectrolyte resulting from the polymerization, for 100 mol %:
(i) of a proportion greater than or equal to 30 mol % and less than 99.5 mol % of monomer units derived from partially salified or totally salified 2-methyl-2-[(1-oxo-2-proenyl)amino]-1-propanesulfonic acid in sodium salt or ammonium salt form;
(ii) of a proportion greater than or equal to 0. 5 mol % and less than or equal to 5% of monomer units derived from at least one monomer of formula (I):
CH 2 ═CH(CH 3 )—C(=O)—OR 1 (I)
in which R 1 represents an alkyl radical comprising from ten to eighteen carbon atoms, wherein monomer units are derived from: lauryl methacrylate of a formula (I 1 ) corresponding to formula (I) in which R 1 represents a dodecyl radical, and from stearyl methacrylate of formula (I 2 ) corresponding to formula (I) in which R 1 represents an octadecyl radical, in a mole ratio of the monomer units of formula (I 1 )/ the monomer units of formula (I 2 ) greater than or equal to 1/10 and less than equal to 10/1;
(iii) of a proportion greater than 0 mol % and less than or equal to 5 mol % of monomer units derived from at least one diethylene or polyethylene crosslinking monomer; and
(iv) of a proportion of greater than 0 mol % and less than 69.5 mol % of monomer units derived from a neutral monomer.
2. The crosslinked anionic polyelectrolyte as defined in claim 1 , wherein the mole proportion of monomer units derived from at least one diethylene or polyethylene crosslinking monomer is greater than or equal to 0.1 mol % and less than or equal to 3.0 mol %.
3. The crosslinked anionic polyelectrolyte as defined in claim 1 , wherein the crosslinking agent and/or the branching agent is selected from the group consisting of ethylene glycol dimethacrylate, tetraallyloxyethane, ethylene glycol diacrylate, diallylurea, triallylamine, trimethylolpropane triacrylate and methylenebis(acrylamide), and a mixture thereof.
4. The anionic polyelectrolyte as defined in claim 1 , wherein the anionic polyelectrolyte is obtained by polymerization in the presence of one or more neutral monomers, in a mole proportion of neutral monomer, for 100 mol % of the monomers used, of less than or equal to 30 mol %.
5. The crosslinked anionic polyelectrolyte as defined claim 1 , resulting from the polymerization, for 100 mol %:
(i) of a mole proportion greater than or equal to 75 mol % and less than or equal to 95 mol %, of the monomer units derived from partially salified or totally salified 2-methyl-2-[(1-oxo-2-propenyl)amino]-1-propanesulfonic acid in sodium salt or ammonium salt form;
(ii) of a proportion greater than or equal to 0.5 mol % and less than or equal to 5 mol % of monomer units derived from the lauryl methacrylate of formula (I 1 ), and from the stearyl methacrylate of formula (I 2 ), in a mole ratio of the monomer units of formula (I 1 )/ the monomer units of formula (I 2 ) greater than or equal to 1/6 and less than or equal to 6/1;
(iii) of a proportion greater than or equal to 0.5 mol % and less than or equal to 3.0 mol % of monomer units derived from at least one diethylene or polyethylene crosslinking monomer selected from the group consisting of triallylamine, trimethylolpropane triacrylate and methylenebis(acrylamide); and
(iv) from a mole proportion greater than or equal to 4.0 mol % and less than or equal to 20 mol % of the monomer units derived from a neutral monomer.
6. The crosslinked anionic polyelectrolyte as defined in claim 2 , resulting from the polymerization, for 100 mol %:
(i) of a proportion greater than or equal to 83 mol % and less than or equal to 90 mol % of the monomer units derived from partially salified or totally salified 2-methyl-2-[(1-oxo-2-propenyl)amino]-1-propanesulfonic acid in sodium salt or ammonium salt form;
(ii) of a proportion greater than or equal to 1.5 mol % and less than or equal to 2.5 mol % of monomer units derived from the lauryl methacrylate of formula (I 1 ) and from the stearyl methacrylate of formula (I 2 ), in a mole ratio of the monomer units of formula (I 1 )/ the monomer units of formula (I 2 ) greater than or equal to 1/6 and less than or equal to 6/1;
(iii) of a proportion greater than or equal to 0.5 mol % and less than or equal to 3.0 mol % of monomer units derived from trimethylolpropane triacrylate or methylenebis(acrylamide); and
(iv) of a proportion greater than or equal to 8 mol % to less than or equal to 15 mol % of monomer units derived from (2-hydroxyethyl) acrylate.
7. A cosmetic, dermopharmaceutical or pharmaceutical topical composition comprising the anionic polyelectrolyte as defined in claim 1 , as a thickener and/or as a stabilizer and/or as an emulsifier.
8. A topical composition, comprising from 0.1% to 10% by weight of the anionic polyelectrolyte as defined in claim 1 .