Aromatic polyamide porous film, separator for battery, and battery
An aromatic polyamide porous film has a total number of branch points of pores in an area of 3 cubic micrometers obtained by three-dimensional structural analysis is 2,000 to 20,000, which ensures high rate characteristics and is also capable of suppressing deterioration of cycle characteristics and storage characteristics as well as abnormal heat generation, when used as a separator for battery, and also has excellent heat resistance; and a separator for battery and a battery, each including the aromatic polyamide porous film.
1. An aromatic polyamide porous film comprising an aromatic polyamide having a logarithmic viscosity (η inh ) of 2.0 to 3.5 dl/g and polyvinylpyrrolidone having a weight average molecular weight of 500,000 to 2,000,000 and having 5,000 to 15,000 total branch points of pores in an area of 3 cubic micrometers of the film as determined from a three-dimensional structural image of the area created by assembling a series of SEM images of width direction-thickness direction cross-sections of the area in 20 nm increments.
2. The aromatic polyamide porous film according to claim 1 , having an average tortuosity in a thickness direction determined from the three-dimensional structural image of 1.2 to 2.1, and an average tortuosity determined from the three-dimensional structural image of 1.0 to 2.1 in both longitudinal and width directions.
3. The aromatic polyamide porous film according to claim 2 , having a lithium ion diffusion coefficient in a thickness direction measured by a pulsed-field-gradient NMR analysis method of 4.0 to 12.0 m 2/ s.
4. The aromatic polyamide porous film according to claim 2 , having a thickness of 9 to 40 μm, and a Gurley permeability of 5 to 200 seconds/100 ml.
5. A separator for a battery, comprising the aromatic polyamide porous film according to claim 2 .
6. The aromatic polyamide porous film according to claim 1 , having a lithium ion diffusion coefficient in a thickness direction measured by a pulsed-field-gradient NMR analysis method of 4.0 to 12.0 m 2 /s.
7. The aromatic polyamide porous film according to claim 6 , having a thickness of 9 to 40 μm, and a Gurley permeability of 5 to 200 seconds/100 ml.
8. A separator for a battery, comprising the aromatic polyamide porous film according to claim 6 .
9. The aromatic polyamide porous film according to claim 1 , having a thickness of 9 to 40 μm, and a Gurley permeability of 5 to 200 seconds/100 ml.
10. A separator for a battery, comprising the aromatic polyamide porous film according to claim 9 .
11. A separator for a battery, comprising the aromatic polyamide porous film according to claim 1 .
12. A battery comprising the separator for a battery according to claim 11 .