Electrode material for lithium-ion rechargeable battery, electrode for lithium-ion rechargeable battery, and lithium-ion rechargeable battery
[Problems] To provide an electrode material for a lithium-ion rechargeable battery capable of improving the battery characteristics, durability, and stability of a lithium-ion rechargeable battery, an electrode for a lithium-ion rechargeable battery, and a lithium-ion rechargeable battery. [Means] An electrode material for a lithium-ion rechargeable battery of the present invention is an electrode material for a lithium-ion rechargeable battery formed by coating the surface of an electrode active material represented by General Formula Li x A y D z PO 4 (here, A represents at least one element selected from Co, Mn, Ni, Fe, Cu, and Cr, D represents at least one element selected from Mg, Ca, Sr, Ba, Ti, Zn, B, Al, Ga, In, Si, Ge, Sc, and Y, 1≤x≤1.1, 0<y≤1, 0≤z<1, 0.9<y+z≤1) with a carbonaceous film, in which a saturated adsorbed moisture amount in a carbonaceous film single body, which is detected in a temperature range of room temperature or more and 250° C. or less by means of Karl Fischer (coulometric titration), is 5000 ppm or more and 50000 ppm or less.
1. A cathode material for a lithium-ion rechargeable battery, characterized in that:
a surface of an electrode active material represented by General Formula Li x A y D z PO 4 (A represents at least one element selected from Co, Mn, Ni, Fe, Cu, and Cr, D represents at least one element selected from Mg, Ca, Sr, Ba, Ti, Zn, B, Al, Ga, In, Si, Ge, Sc, and Y, 1≤x≤1.1, 0<y≤1, 0≤z<1, 0.9<y+z≤1) is coated with a carbonaceous film made of pyrolytic carbon, derived from an organic compound having 60% or more purity of carbon, and
a saturated adsorbed moisture amount in a single body of the carbonaceous film, which is detected in a temperature range of room temperature or more and 250° C. or less by means of Karl Fischer (coulometric titration), is 10000 ppm or more and 40000 ppm or less.
2. The cathode material for a lithium-ion rechargeable battery according to claim 1 ,
wherein a ratio of a 0.1 C discharge capacity to a 3 C discharge capacity measured at 25° C. is 80% or more.
3. The cathode material for a lithium-ion rechargeable battery according to claim 1 ,
wherein, when an amount of carbon is represented by A (mass by mass), and a specific surface area is represented by B (m 2 /g), A and B satisfy 0.07≤A/B≤0.15.
4. A cathode for a lithium-ion rechargeable battery comprising:
a current collector; and
an electrode mixture layer formed on the current collector,
wherein the electrode mixture layer includes the cathode material for a lithium-ion rechargeable battery according to claim 1 .
5. A lithium-ion rechargeable battery comprising:
the cathode for a lithium-ion rechargeable battery according to claim 4 .
6. The cathode material for a lithium-ion rechargeable battery according to claim 1 , wherein the carbonaceous film has a thickness of 1 to 12 nm.
7. The cathode material for a lithium-ion rechargeable battery according to claim 1 , wherein the amount of carbon included in the cathode material is 0.5% by mass or more and 5.0% by mass or less.
8. The cathode material for a lithium-ion rechargeable battery according 1 , wherein the amount of carbon included in the cathode material is 0.8% by mass or more and 2.5% by mass or less.
9. The cathode material for a lithium-ion rechargeable battery according to claim 1 , wherein the average primary particle diameter of primary particles of the electrode active material made of Li x A y D z PO 4 is preferably 50 nm or more and 400 nm or less.
10. The cathode material for a lithium-ion rechargeable battery according to claim 3 , wherein A and B satisfy 0.08≤A/B≤0.13.
11. The cathode material for a lithium-ion rechargeable battery according to claim 1 , wherein the specific surface area of the cathode material is 6 m 2 /g or more and 25 m 2 /g or less.
12. The cathode material for a lithium-ion rechargeable battery according to claim 11 , wherein the specific surface area of the cathode material is 8 m 2 /g or more and 20 m 2 /g or less.
13. The cathode material for a lithium-ion rechargeable battery according to claim 1 , wherein the average primary particle diameter of primary particles of the electrode active material made of Li x A y D z PO 4 is preferably 50 nm or more and 260 nm or less, and
the average particle diameter of the cathode material is preferably 75 nm or more and 270 nm or less.
14. The cathode material for a lithium-ion rechargeable battery according to claim 1 , wherein the cathode material is manufactured by the method comprising:
preparing a raw material slurry which is obtained by mixing an electrode active material or precursor of the electrode active material, an organic compound having 60% or more of purity of carbon and a solvent including water; and
spraying and drying the slurry at a temperature of 70° C. or more and 250° C. or less to generate a granulated body.
15. The cathode material for a lithium-ion rechargeable battery according to claim 1 , wherein the steps of spraying and drying are performed in an inert atmosphere or a reducing atmosphere.