Multilayer ceramic capacitor
A multilayer ceramic capacitor that includes a ceramic laminated body having dielectric layers and internal electrodes at the interfaces between the dielectric layers, and external electrodes on the outer surface of the ceramic laminated body. The dielectric layers contain, as their main constituent, a perovskite-type compound including Ba, Ti, Zr, and M. M is at least one element of Ta, Nb, V, and W. The dielectric layers further contain Mn and Si as additive constituents. With respect to the total amount of Ti, Zr, and M, 40 mol %<Zr≤90 mol %, M is 1 mol %≤M≤10 mol %. When the total amount of Ti, Zr, and M is regarded as 100 parts by mol, 1 part by mol≤Mn≤10 parts by mol, 1 part by mol≤Si≤5 parts by mol, and 0.5≤Mn/M≤3.0.
1. A multilayer ceramic capacitor comprising:
a laminated body comprising a plurality of dielectric layers and a plurality of internal electrodes provided respectively at interfaces between adjacent dielectric layers of the plurality of dielectric layers; and
an external electrode on an outer surface of the laminated body, and electrically connected to the plurality of internal electrodes,
the plurality of dielectric layers containing, as their main constituent, a perovskite-type compound comprising Ba, Ti, Zr, and M, where M is at least one element of Ta, Nb, V, and W, and the plurality of dielectric layers further containing Mn and Si as additive constituents,
with respect to a total amount of Ti, Zr, and M, a content of Zr is 40 mol %≤Zr≤90 mol %, and a content of M is 1 mol %≤M≤10 mol %; and
when the total amount of Ti, Zr, and M is regarded as 100 parts by mol, a content of Mn is 1 part by mol≤Mn≤10 parts by mol, a content of Si is 1 part by mol≤Si≤5 parts by mol, and a molar ratio between Mn and M is 0.5≤Mn/M≤3.0.
2. The multilayer ceramic capacitor according to claim 1 , wherein the Ba is an element constituting an A site in the main constituent of the perovskite-type compound, the Ti, the Zr, and the M are elements constituting a B site in the main constituent of the perovskite-type compound, and a ratio between the element constituting the A site and the elements constituting the B site is 1.00 to 1.03.
3. A multilayer ceramic capacitor comprising:
a laminated body comprising a plurality of dielectric layers and a plurality of internal electrodes provided respectively at interfaces between adjacent dielectric layers of the plurality of dielectric layers; and
an external electrode on an outer surface of the laminated body, and electrically connected to the plurality of internal electrodes,
the laminated body having a composition containing, as its main constituent, a perovskite-type compound comprising Ba, Ti, Zr, and M, where M is at least one element of Ta, Nb, V, and W, and the laminated body further contains Mn and Si as additive constituents,
when the laminated body is dissolved to produce a solution, with respect to a total amount of Ti, Zr, and M in the solution, a content of Zr is 40 mol %≤Zr≤90 mol %, and a content of M is 1 mol %≤M≤10 mol %, and
when the total amount of Ti, Zr, and M is regarded as 100 parts by mol, a content of Mn is 1 part by mol≤Mn≤10 parts by mol, a content of Si is 1 part by mol≤Si≤5 parts by mol, and a molar ratio between Mn and M is 0.5≤Mn/M≤3.0.
4. The multilayer ceramic capacitor according to claim 3 , wherein the Ba is an element constituting an A site in the main constituent of the perovskite-type compound, the Ti, the Zr, and the M are elements constituting a B site in the main constituent of the perovskite-type compound, and a ratio between the element constituting the A site and the elements constituting the B site is 1.00 to 1.03.
5. A dielectric layer material for a multilayer ceramic capacitor, the dielectric layer comprising:
a main constituent perovskite-type compound comprising Ba, Ti, Zr, and M;
Mn; and
Si,
where M is at least one element of Ta, Nb, V, and W,
with respect to a total amount of Ti, Zr, and M:
40 mol %≤Zr≤90 mol %,
1 mol %≤M≤10 mol %,
when the total amount of Ti, Zr, and M is regarded as 100 parts by mol:
1 part by mol≤Mn≤10 parts by mol,
1 part by mol≤Si≤5 parts by mol, and
0.5≤Mn/M≤3.0.
6. The dielectric layer material according to claim 1 , wherein the Ba is an element constituting an A site in the main constituent perovskite-type compound, the Ti, the Zr, and the M are elements constituting a B site in the main constituent perovskite-type compound, and a ratio between the element constituting the A site and the elements constituting the B site is 1.00 to 1.03.