Aqueous-based hydrolytically stable dispersion of a biodegradable polymer
Embodiments of an aqueous-based dispersion of a hydrolytically unstable polymer comprise particles of said hydrolytically unstable polymer and a stabilizing agent in water. The dispersion is substantially free of volatile organic solvents.
1. An aqueous-based dispersion of a hydrolytically unstable polymer which is substantially free of volatile organic compounds, consisting of biodegradable polymer particles, stabilizing agent, and optionally one or more components selected from the group consisting of viscosity increasing rheology modifiers and pH buffering agents in water, wherein the stabilizing agent consists of polyvinyl alcohol, and wherein the biodegradable polymer particles consist of biodegradable polymer.
2. The aqueous-based dispersion of claim 1 , wherein the biodegradable polymer is a polyester.
3. The aqueous-based dispersion of claim 2 , wherein the polyester is a polymer selected from the group consisting of polylactic acid (PLA), polymalate (PMA), polyhydroxyalkanoate (PHA), polyhydroxybutyrate (PHB), polycaprolactone (PCL), polyesteramide (PEA), polyhydroxyvalerate (PHV), polyhydroxyhexanoate (PHH), aliphatic copolyesters (PBSA), polyethylene furanoate (PEF), polybutylene succinate (PBS), poly(poly sebate) (PPS), polyglycolic acid, and blends thereof.
4. The aqueous-based dispersion of claim 2 , wherein the polyester is polylactic acid (PLA).
5. The aqueous-based dispersion of claim 1 , wherein the biodegradable polymer is present in an amount of from about 5 wt % to about 95 wt % based on a total weight of the aqueous-based dispersion.
6. The aqueous-based dispersion of claim 1 , wherein the stabilizing agent is present in an amount of from about 0.1 wt % to about 25 wt % based on a total weight of the aqueous-based dispersion.
7. The aqueous-based dispersion of claim 1 , wherein the stabilizing agent is present in an amount of from about 0.5 wt % to about 15 wt % based on a total weight of the aqueous-based dispersion.
8. The aqueous-based dispersion of claim 1 , wherein the rheology modifier is selected from the group consisting of inorganic clays, and polysaccharides.
9. The aqueous-based dispersion of claim 1 , wherein the rheology modifier is present in an amount from about 0.01 wt % to about 5 wt % based on a total weight of the aqueous-based dispersion.
10. The aqueous-based dispersion of claim 1 , wherein the rheology modifier is present in an amount from about 0.1 wt % to about 3 wt % based on a total weight of the aqueous-based dispersion.
11. The aqueous-based dispersion of claim 1 , wherein the rheology modifier comprises polysaccharide.
12. The aqueous-based dispersion of claim 11 , wherein the polysaccharide comprises xanthan gum.
13. The aqueous-based dispersion of claim 1 , wherein the biodegradable polymer particles have an average diameter of from about 25 nm to about 600 μm.
14. The aqueous-based dispersion of claim 1 , wherein said pH buffering agent is selected from the group consisting of salts of weak acids and bases.
15. The aqueous-based dispersion of claim 1 , wherein said pH buffering agent is present in an amount of from about 0.01 wt % to about 1 wt % based on a total weight of the aqueous-based dispersion.