Biaxially oriented, laminated polyamide resin film
The present invention is to provide stable slipperiness in highly humid environments, further to provide suitability for printing and packaging with various design properties, stable bagmaking workability, and processability properties by simultaneously giving excellent transparency as same as that of common polyamide resin films, and still further to provide a biaxially oriented, laminated polyamide resin film producible at a low cost in the case of film production. A biaxially oriented, laminated polyamide resin film comprising at least one substrate layer and at least one slippery layer, wherein the substrate layer and the slippery layer contain polyamide resins and the biaxially oriented, laminated polyamide resin film has a static friction coefficient of 0.9 or lower in 65% RH environments and a haze value of 3.0% or lower.
1. A biaxially oriented, laminated polyamide resin film comprising at least one substrate layer and at least one slippery layer,
wherein
the biaxially oriented, laminated polyamide resin film has a thickness of 6 to 25 μm, a static friction coefficient of 0.9 or lower at 23° C. and 65% RH, and a haze value of 3.0% or lower,
the substrate layer comprises an aliphatic polyamide resin consisting of nylon 6,
the slippery layer contains (i) at least 2 kinds of polyamide resins consisting of nylon 6 and 1 to 5 wt % of a semi-aromatic polyamide resin, (ii) 3000 to 5000 ppm of inorganic fine particle A having a pore volume of 1.0 to 1.8 mL/g and an average particle diameter of 3 to 7 μm, and (iii) 300 to 1000 ppm of inorganic fine particle B having a pore volume of less than 1.0 mL/g and an average particle diameter of smaller than 3 μm, and
the substrate layer contains not more than 0.37 wt % of poly(m-xylylene adipamide).
2. The biaxially oriented, laminated polyamide resin film according to claim 1 , wherein the slippery layer contains 0.05 to 0.30 wt % of ethylene bis(stearic acid amide).
3. The biaxially oriented, laminated polyamide resin film according to claim 2 , wherein the biaxially oriented, laminated polyamide resin film is produced by a co-extrusion method and the slippery layer is layered on at least one face or both faces of the substrate layer.
4. The biaxially oriented, laminated polyamide resin film according to claim 3 , wherein the thickness ratio of the total thickness of the slippery layer to the thickness of the entire laminated film is 6 to 30%.
5. The biaxially oriented, laminated polyamide resin film according to claim 4 , wherein the substrate layer contains an aliphatic polyamide resin, or an aliphatic polyamide as well as a raw material recovered from its film.
6. The biaxially oriented, laminated polyamide resin film according to claim 3 , wherein the substrate layer contains an aliphatic polyamide resin, or an aliphatic polyamide as well as a raw material recovered from its film.
7. The biaxially oriented, laminated polyamide resin film according to claim 2 , wherein the thickness ratio of the total thickness of the slippery layer to the thickness of the entire laminated film is 6 to 30%.
8. The biaxially oriented, laminated polyamide resin film according to claim 7 , wherein the substrate layer contains an aliphatic polyamide resin, or an aliphatic polyamide as well as a raw material recovered from its film.
9. The biaxially oriented, laminated polyamide resin film according to claim 2 , wherein the substrate layer contains an aliphatic polyamide resin, or an aliphatic polyamide as well as a raw material recovered from its film.
10. The biaxially oriented, laminated polyamide resin film according to claim 1 , wherein the biaxially oriented, laminated polyamide resin film is produced by a co-extrusion method and the slippery layer is layered on at least one face or both faces of the substrate layer.
11. The biaxially oriented, laminated polyamide resin film according to claim 10 , wherein the thickness ratio of the total thickness of the slippery layer to the thickness of the entire laminated film is 6 to 30%.
12. The biaxially oriented, laminated polyamide resin film according to claim 11 , wherein the substrate layer contains an aliphatic polyamide resin, or an aliphatic polyamide as well as a raw material recovered from its film.
13. The biaxially oriented, laminated polyamide resin film according to claim 10 , wherein the substrate layer contains an aliphatic polyamide resin, or an aliphatic polyamide as well as a raw material recovered from its film.
14. The biaxially oriented, laminated polyamide resin film according to claim 1 , wherein the thickness ratio of the total thickness of the slippery layer to the thickness of the entire laminated film is 6 to 30%.
15. The biaxially oriented, laminated polyamide resin film according to claim 1 , wherein the substrate layer contains an aliphatic polyamide resin, or an aliphatic polyamide as well as a raw material recovered from its film.