Corrosion resistant bushing
A method of forming a corrosion resistant bushing includes bonding a sliding layer to a first surface of a load bearing substrate to form a laminate sheet and cutting a blank from the laminate sheet. The laminate sheet includes an exposed surface corresponding to a second surface of the load bearing substrate. The blank includes cut edges having a load bearing substrate portion. The method further includes forming a semi-finished bushing from the blank.
1. A sliding article comprising:
a load bearing substrate, having a first major surface, a second major surface, and an edge, the load bearing substrate having a thickness t 1 ,
an aluminum containing layer overlying and in direct contact with the first major surface, the aluminum containing layer having a thickness t 2 , wherein t 2 is at least 10 microns,
a sliding layer overlying the first or the second major surface,
wherein a ratio of t 2 /t 1 is at least 1/10, further comprising a functional layer comprising an elastomer layer overlying the load bearing substrate opposite the sliding layer.
2. The sliding article according to claim 1 further comprising an additional aluminum containing layer overlying and in direct contact with the second major surface, the additional aluminum containing layer having a thickness t 3 .
3. The sliding article according to claim 1 , wherein the functional layer further comprises a second sliding layer.
4. The sliding article according to claim 1 , wherein the ratio of t 2 /t 1 is not greater than 1/3.
5. The sliding article according to claim 1 , wherein t 2 is at least 25 microns.
6. The sliding article according to claim 1 , wherein t 2 is not greater than 200 microns.
7. The sliding article according to claim 1 , wherein t 1 is in a range from 50 microns to 2000 microns.
8. The sliding article according to claim 1 , wherein the combined tensile strength of the load bearing substrate and the aluminum containing is at least 70% of the tensile strength of the load bearing substrate.
9. The sliding article according to claim 1 , wherein the aluminum containing layer has content of magnesium of at least 20 wt %.
10. The sliding article according to claim 1 , wherein the aluminum containing layer has an aluminum content in a range from 25 wt % to 99.99999 wt %.
11. The sliding article according to claim 1 further comprising a discontinuous metal layer adjacent to the first major surface.
12. The sliding article according to claim 11 , wherein the discontinuous metal layer comprises aluminum, an aluminum alloy, a steel metal, a steel cladded or coated with an aluminum containing layer, or a combination thereof.
13. A bushing comprising:
a multilayered metallic substrate, the multi-layered substrate comprising
a steel layer having a first major surface and a second major surface,
a first aluminum containing layer adjacent to and in direct contact with the first major surface, and
a second aluminum containing layer adjacent to and in direct contact with the second major surface;
an adhesive layer overlying the multilayered metallic substrate;
a fluoropolymer sliding layer overlying and in direct contact with the adhesive layer.
14. The bushing as claimed in claim 13 , characterized in that the bushing has at least one axial collar.
15. The bushing as claimed in claim 13 , characterized in that the bushing has an essentially cylindrical shape.
16. The bushing as claimed in claim 13 , characterized in that the bushing has a conical shape.
17. A sliding article comprising:
a load bearing substrate, having a first major surface, a second major surface, and an edge, the load bearing substrate having a thickness t 1 ,
an aluminum containing layer overlying and in direct contact with the first major surface, the aluminum containing layer having a thickness t 2 , wherein t 2 is at least 10 microns,
a sliding layer overlying the first or the second major surface, and
an adhesive layer disposed between the aluminum containing layer and the sliding layer,
wherein a ratio of t 2 /t 1 is at least 1/10, further comprising a functional layer comprising an elastomer layer overlying the load bearing substrate opposite the sliding layer.
18. The sliding article according to claim 17 further comprising an additional aluminum containing layer overlying and in direct contact with the second major surface, the additional aluminum containing layer having a thickness t 3 .