Liquid optically clear photo-curable adhesive

1. A liquid photo-curable adhesive composition comprising:

(a) 5 to 30 wt % of urethane acrylate, having a T g value from −80° C. to −10° C., and a viscosity ranging from 5,000 to 500,000 mPa at 25° C. at a shear rate of 2.55 s −1 ,

(b) 30 to 80 wt % of plasticizer,

(c) 0.02 to 5 wt % of photo initiator,

(d) 1 to 30 wt % of acrylate monomers and/or acrylate oligomer, wherein the acrylate oligomer has a T g value from −80° C. to 100° C.,

wherein the hardness of the cured adhesive is 0 to 30 (shore 00), determined in accordance with ASTM D 2240, wherein the elastic modulus of the cured adhesive is <5.0·10 4 Pa, determined using photorheometry, wherein the shrinkage of the cured adhesive is <1.5%, determined using photorheometry.

2. Adhesive composition according to claim 1 , wherein the urethane acrylate is an aliphatic polyether urethane acrylate.

3. Adhesive composition according to claim 1 , wherein the plasticizer is selected from the group consisting of polyisoprene resin, polybutadiene resin, hydrogenated polybutadiene, xylene polymer, hydroxyl-terminated polybutadiene and hydroxyl-terminated polyolefin.

4. Adhesive composition according to claim 1 , wherein the photo initiator is selected from the group consisting of 2,2-dimethoxyl-1,2-diphenylethyl-1-ketone; trimethylbenzoyldi-phenyl oxyphosphate; 1-hydroxylcyclohexyl benzophenone; 2-methyl-1-[4-methylthiophenyl]-2-dimethylthio-propyl-1-ketone and combinations thereof.

5. Adhesive composition according to claim 1 comprising:

(a) 10 to 25 wt % of the urethane acrylate,

(b) 30 to 70 wt % of the plasticizer,

(c) 1.2 to 3.5 wt % of the photo initiator, and

(d) 4 to 19 wt % of the acrylate monomers.

6. Adhesive composition according to claim 1 , which comprises additional ingredients selected from the group consisting of tackifier, antifoaming agent, antioxidant, and adhesion promoter.