Flame retardant resin composition and cable using the same
Disclosed is a flame retardant resin composition in which relative to 100 parts by mass of the base resin, a silicone based compound is blended at a ratio of 0.1 to 10 parts by mass a fatty acid metal salt is blended at a ratio of 0.1 to 20 parts by mass, a flame retardant agent is blended at a ratio of 5 to 200 parts by mass, a hindered phenol based compound is blended at a ratio of 0.05 to 10 parts by mass, and a hindered amine based compound is blended at a ratio of 0.05 to 10 parts by mass. The hindered amine based compound has a group represented by the following formula (1). (R 1 represents an alkyl or alkoxy group having 1 to 30 carbon atoms, and R 2 to R 5 each independently represent an alkyl group having 1 to 6 carbon atoms).
1. A flame retardant resin composition comprising:
a base resin containing a polyolefin based compound;
a silicone based compound;
a fatty acid metal salt;
a flame retardant agent containing at least one kind selected from the group consisting of calcium carbonate particles and silicate compound particles;
a hindered phenol based compound; and
a hindered amine based compound,
wherein the silicone based compound is blended at a ratio of 0.1 part by mass or more and 10 parts by mass or less relative to 100 parts by mass of the base resin,
the fatty acid metal salt is blended at a ratio of 0.1 part by mass or more and 20 parts by mass or less relative to 100 parts by mass of the base resin,
the flame retardant agent is blended at a ratio of 5 parts by mass or more and 200 parts by mass or less relative to 100 parts by mass of the base resin,
the hindered phenol based compound is blended at a ratio of 0.05 part by mass or more and 10 parts by mass or less relative to 100 parts by mass of the base resin,
the hindered amine based compound is blended at a ratio of 0.05 part by mass or more and 10 parts by mass or less relative to 100 parts by mass of the base resin, and
the hindered amine based compound has a monovalent group represented by the following formula (1):
(in the formula (1), R 1 represents an alkyl group or alkoxy group having 1 to 30 carbon atoms and R 2 to R 5 each independently represent an alkyl group having 1 to 6 carbon atoms)
2. The flame retardant resin composition according to claim 1 , wherein the flame retardant agent is composed of calcium carbonate particles.
3. The flame retardant resin composition according to claim 1 , wherein the flame retardant agent is composed of silicate compound particles.
4. The flame retardant resin composition according to claim 1 , wherein the hindered amine based compound has a monovalent group represented by the formula (1).
5. The flame retardant resin composition according to claim 1 ,
wherein the silicone based compound is blended at a ratio of more than 0.2 part by mass relative to 100 parts by mass of the base resin,
the fatty acid metal salt is blended at a ratio of more than 3 parts by mass relative to 100 parts by mass of the base resin,
the hindered amine based compound is blended at a ratio of 0.05 part by mass or more and less than 1 part by mass relative to 100 parts by mass of the base resin, and
the hindered amine based compound has a molecular weight of 1000 or more.
6. The flame retardant resin composition according to claim 1 , wherein the hindered amine based compound has a molecular weight of 1000 or more.
7. The flame retardant resin composition according to claim 6 , wherein the hindered amine based compound has a molecular weight of 3000 or less.
8. The flame retardant resin composition according to claim 5 ,
wherein the silicone based compound is blended at a ratio of more than 1 part by mass relative to 100 parts by mass of the base resin, and
the hindered amine based compound has a monovalent group represented by the formula (1) and R 1 in the formula (1) represents the alkyl group.
9. A cable comprising:
a sheath; and
a transmission medium provided on the inner side of the sheath and composed of a conductor or an optical fiber,
wherein the sheath is composed of the flame retardant resin composition according to claim 1 .
10. A flame retardant resin composition comprising:
a base resin containing a polyolefin based compound;
a silicone based compound;
a fatty acid metal salt;
a flame retardant agent containing at least one kind selected from the group consisting of calcium carbonate particles and silicate compound particles;
a hindered phenol based compound; and
a hindered amine based compound,
wherein the silicone based compound is blended at a ratio of 0.1 part by mass or more and 10 parts by mass or less relative to 100 parts by mass of the base resin,
the fatty acid metal salt is blended at a ratio of 0.1 part by mass or more and 20 parts by mass or less relative to 100 parts by mass of the base resin,
the flame retardant agent is blended at a ratio of 5 parts by mass or more and 200 parts by mass or less relative to 100 parts by mass of the base resin,
the hindered phenol based compound is blended at a ratio of 0.05 part by mass or more and 10 parts by mass or less relative to 100 parts by mass of the base resin,
the hindered amine based compound is blended at a ratio of 0.05 part by mass or more and 10 parts by mass or less relative to 100 parts by mass of the base resin,
the hindered amine based compound has a molecular weight of 3000 or less and
the hindered amine based compound has a monovalent group represented by the following formula (2):
(in the formula (2), R 6 represents an alkylene group having 1 to 30 carbon atoms and R 7 to R 10 each independently represent an alkyl group having 1 to 6 carbon atoms).
11. A cable comprising:
a sheath; and
a transmission medium provided on the inner side of the sheath and composed of a conductor or an optical fiber,
wherein the sheath is composed of the flame retardant resin composition according to claim 10 .