Laminate film using polylactic acid-based resin
Our invention is a laminate film comprising a water-soluble resin layer and a polylactic acid-based resin layer laminated on at least one side of a substrate film, the water-soluble resin layer has a thickness of 0.1 to 15 μm, the polylactic acid-based resin layer has a thickness of 10 to 500 nm. Such a configuration provides a laminate film of which the water-soluble resin layer and the polylactic acid-based resin layer are easily separated from the substrate film and which is excellent in coating ability, adherence and followability to a soft and curved adherend, as well as compatibility to skin and organs such as viscera, so as to be suitable for wound dressing, adhesion prevention material and a skin external agent such as skin-care product.
1. A laminate film comprising a water-soluble resin layer and a polylactic acid-based resin layer laminated on a polyester or polyolefin substrate film surface, wherein
the water-soluble resin layer has a thickness of 0.1 to 15 μm,
the polylactic acid-based resin layer has a thickness of 10 to 500 nm, and
the substrate film surface has a center-line average surface roughness (SRa) of 3 to 50 nm and a ten-point average surface roughness (SRz) of 50 to 1000 nm.
2. The laminate film according to claim 1 , wherein the water-soluble resin layer contains a polyvinyl alcohol.
3. The laminated film according to claim 2 , wherein the polyvinyl alcohol has a saponification degree of 85 to 98.5 mol %.
4. The laminate film according to claim 1 , wherein the polylactic acid-based resin layer contains a polylactic acid-based resin including a poly-D-lactic acid of 4 to 13 mol %.
5. The laminate film according to claim 1 , wherein the water-soluble resin layer contains a pullulan.