Wide operating temperature range electrolytes for lithium-ion capacitors achieving high performance
The present invention provides for two types of wide operating temperature range electrolyte formulations that contain methyl butyrate (MB) and additives have been investigated and compared in Lithium-ion capacitors (LICs), which were consisted of hard carbon (HC)/stabilized lithium metal powder (SLMP) anodes and activated carbon (AC) cathodes. The electrolyte L1 that was 1M LiPF 6 in ethylene carbonate (EC)+ethyl methyl carbonate (EMC)+MB (20:20:60 v/v %)+0.1M lithium bis(oxalato)borate (LiBOB) and electrolyte L2 that was 1M LiPF 6 in EC+EMC+MB (20:20:60 v/v %)+0.1M lithium difluoro(oxalato)borate (LiDFOB) enabled the LICs to discharge at the temperature as low as −40° C., which the conventional electrolyte LP30 that was 1 M LiPF 6 in EC+dimethyl carbonate (DMC) (50:50 w/w %) could not achieve. At the low temperature of −40° C., L2 held more than 64% of the discharge capacity at 30° C., while the L1 only had the discharge capacity retention of 30%. In addition, L2 proved to achieve better cycling performance compared to L1. After 10,000 cycles, the capacity retention of L1 and L2 were about 86.6% and 84.7%, which demonstrated the stable cycling performance for electrolyte L1 and L2. In summary, L2 was the most suitable electrolyte for the LICs energy storage devices which would be applied in the temperature as low as −40° C.
1. A lithium-ion capacitor (LIC) laminate cell, comprising:
an electrolyte including 1M LiPF6 in ethylene carbonate (EC)+ethyl methyl carbonate (EMC)+methyl butyrate (MB) in a ratio of 20:20:60 v/v %, respectively, including a 0.1M lithium based salt additive;
a positive electrode including activated carbon (AC) as its active material;
a negative electrode including hard carbon (HC) as its active material;
a lithium source; and
a separator;
wherein the negative electrode is pre-doped with sufficient lithium ions by placing lithium sources on the surface of negative electrodes, and wherein the 0.1M lithium based salt additive is lithium bis(oxalato)borate (LiBOB) or lithium difluoro(oxalato)borate (LiDFOB);
and further wherein the cell operating voltage range is from 3.8 V to 2.2 V, and further wherein the resulting LIC cell is capable of high performance functioning in a wide temperature range down to −40 C.
2. The LIC laminate cell according to claim 1 , wherein said lithium source loaded on the surface of negative electrodes include stabilized lithium metal powder (SLMP).
3. The LIC laminate cell according to claim 1 , wherein said lithium source loaded on the surface of negative electrodes include square-shaped lithium film pieces.
4. The LIC laminate cell according to claim 1 , wherein said lithium source loaded on the surface of negative electrodes include round-shaped lithium film pieces.
5. The LIC laminate cell according to claim 1 , wherein said lithium source loaded on the surface of negative electrodes include lithium film strips.
6. The method for making a lithium-ion capacitor (LIC) laminate cell, comprising:
providing an electrolyte including 1M LiPF6 in ethylene carbonate (EC)+ethyl methyl carbonate (EMC)+methyl butyrate (MB) in a ratio of 20:20:60 v/v %, respectively, including a 0.1M lithium based salt additive;
providing a positive electrode including activated carbon (AC) as its active material;
providing a negative electrode including hard carbon (HC) as its active material;
providing a lithium source; and
providing a separator;
wherein the negative electrode is pre-doped with sufficient lithium ions by placing lithium sources on the surface of negative electrodes, and wherein the 0.1M lithium based salt additive is lithium bis(oxalato)borate (LiBOB) or lithium difluoro(oxalato)borate (LiDFOB);
and further wherein the cell operating voltage range is from 3.8 V to 2.2 V, and further wherein the resulting LIC cell is capable of high performance functioning in a wide temperature range down to −40 C.
7. The method for making an LIC laminate cell according to claim 6 , wherein said lithium source loaded on the surface of negative electrodes include stabilized lithium metal powder (SLMP).
8. The method for making an LIC laminate cell according to claim 6 , wherein said lithium source loaded on the surface of negative electrodes include square-shaped lithium film pieces.
9. The method for making an LIC laminate cell according to claim 6 , wherein said lithium source loaded on the surface of negative electrodes include round-shaped lithium film pieces.
10. The method for making an LIC laminate cell according to claim 6 , wherein said lithium source loaded on the surface of negative electrodes include lithium film strips.