Inorganic coating solution composition and method of forming inorganic coating film using the same
An inorganic coating solution composition including an alkali metal silicate, a curing agent, a dispersant, a defoamer, and a solvent, wherein the curing agent is phosphoric acid (H 2 PO 4 ), the dispersant is at least one selected from among Tween 20, Tween 40, Tween 60, Tween 80, polyvinyl pyrrolidone, polyethylene glycol 400 and polyvinyl alcohol, and the defoamer is at least one selected from among a silicone-based defoamer, an alcohol-based defoamer, a mineral oil-based defoamer and a powder defoamer.
1. An inorganic coating solution composition, comprising:
an alkali metal silicate,
a curing agent,
a dispersant,
a defoamer, and
a solvent comprising, based on 100 parts by weight of the inorganic coating solution composition, 0.0000005 to 10 parts by weight of a silver colloid, 0.0000001 to 15 parts by weight of titanium dioxide, 0.000001 to 6 parts by weight of a dispersion stabilizer, and 69 to 99 parts by weight of water,
wherein the curing agent is phosphoric acid (H 3 PO 4 ),
the dispersant is at least one selected from among Polysorbate 20, Polysorbate 40, Polysorbate 60, Polysorbate 80, polyvinyl pyrrolidone, polyethylene glycol 400, and polyvinyl alcohol, and
the defoamer is at least one selected from among a silicone-based defoamer, an alcohol-based defoamer, a mineral oil-based defoamer, and a powder defoamer.
2. The inorganic coating solution composition of claim 1 , comprising, based on a total weight of the inorganic coating solution composition:
9 to 64 parts by weight of the alkali metal silicate,
0.1 to 1 parts by weight of the curing agent,
0.01 to 5 parts by weight of the dispersant,
0.001 to 0.1 parts by weight of the defoamer, and
30 to 90 parts by weight of the solvent.
3. The inorganic coating solution composition of claim 1 , wherein the solvent is a hydrophilic solvent.
4. The inorganic coating solution composition of claim 1 , wherein the inorganic coating solution composition has a pH of 8 to 14.
5. An inorganic coating solution composition, comprising:
an alkali metal silicate,
a curing agent,
a dispersant,
a defoamer,
a solvent, and
a pH controller for preventing precipitation, and a thickener, wherein the pH controller is at least one selected from among ammonium hydroxide (NH 4 OH), tetramethylammonium hydroxide (TMAOH), tetraethylammonium hydroxide (TEAOH), tetrabutylammonium hydroxide (TBAOH), and dimethylethanolamine, and
the thickener is at least one selected from among polyacrylic acid and carboxymethyl cellulose, and
wherein the curing agent is phosphoric acid (H 3 PO 4 ),
the dispersant is at least one selected from among Polysorbate 20, Polysorbate 40, Polysorbate 60, Polysorbate 80, polyvinyl pyrrolidone, polyethylene glycol 400, and polyvinyl alcohol, and
the defoamer is at least one selected from among a silicone-based defoamer, an alcohol-based defoamer, a mineral oil-based defoamer, and a powder defoamer.
6. The inorganic coating solution composition of claim 5 , comprising, based on a total weight of the inorganic coating solution composition:
9 to 64 parts by weight of the alkali metal silicate,
0.1 to 1 parts by weight of the curing agent,
0.01 to 2 parts by weight of the pH controller,
0.01 to 5 parts by weight of the dispersant,
0.01 to 0.2 parts by weight of the thickener,
0.001 to 0.1 parts by weight of the defoamer, and
30 to 90 parts by weight of the solvent.
7. The inorganic coating solution composition of claim 6 , wherein the solvent is a hydrophilic solvent.
8. An inorganic coating solution composition, comprising:
an alkali metal silicate,
a curing agent,
a dispersant,
a defoamer, and
a solvent, and
wherein the curing agent is phosphoric acid (H 3 PO 4 ),
the dispersant is at least one selected from among Polysorbate 20, Polysorbate 40, Polysorbate 60, Polysorbate 80, polyvinyl pyrrolidone, polyethylene glycol 400, and polyvinyl alcohol, and
the defoamer is at least one selected from among a silicone-based defoamer, an alcohol-based defoamer, a mineral oil-based defoamer, and a powder defoamer, and
a pH controller,
a thickener, and
an inorganic filler,
wherein the pH controller is at least one selected from among ammonium hydroxide (NH4OH), tetramethylammonium hydroxide (TMAOH), tetraethylammonium hydroxide (TEAOH), tetrabutylammonium hydroxide (TBAOH), and dimethylethanolamine,
the thickener is at least one selected from among polyacrylic acid and carboxymethyl cellulose, and
the inorganic filler is at least one selected from among titanium dioxide (TiO 2 ), zeolite, silica, and alumina.
9. The inorganic coating solution composition of claim 8 , comprising, based on a total weight of the inorganic coating solution composition:
9 to 64 parts by weight of the alkali metal silicate,
0.1 to 1 parts by weight of the curing agent,
0.01 to 2 parts by weight of the pH controller,
0.01 to 5 parts by weight of the dispersant,
0.01 to 0.2 parts by weight of the thickener,
0.001 to 0.1 parts by weight of the defoamer,
30 to 90 parts by weight of the solvent, and
0.01 to 2 parts by weight of the inorganic filler.
10. The inorganic coating solution composition of claim 8 , wherein the solvent is a hydrophilic solvent.