Chemically strengthenable lithium aluminosilicate glasses with inherent damage resistance
A group of glass compositions in the Li 2 O—Al 2 O 3 —SiO 2 —B 2 O 3 family that can be chemically strengthened in single or multiple ion exchange baths containing at least one of NaNO 3 and KNO 3 for a short time (2-4 hours) to develop a deep depth of layer (DOL). In some instances, the DOL is at least 70 μm; in others, at least 100 μm. The ion exchanged glasses have a high damage resistance (indentation fracture toughness ranging form greater than 10 kgf to greater than 50 kgf) that is better than or at least comparable to that of sodium aluminosilicate glasses.
1. A lithium aluminosilicate glass comprising:
from 55 mol % to 75 mol % SiO 2 ;
from 10 mol % to 18 mol % Al 2 O 3 ;
from 3.5 mol % to 9.5 mol % B 2 O 3 ;
from 7 mol % to 12.6 mol % Li 2 O; and
from 0 mol % to 4 mol % P 2 O 5 ,
wherein Li 2 O (mol %)/R 2 O (mol %) is in a range from 0.22 to 0.4 and R 2 O=Li 2 O+Na 2 O+K 2 O+Rb 2 O+Cs 2 O.
2. The lithium aluminosilicate glass of claim 1 , wherein R 2 O (mol %)−Al 2 O 3 (mol %) is in a range from −0.5 mol % to 5.6 mol %.
3. The lithium aluminosilicate glass of claim 1 , wherein Al 2 O 3 (mol %)>B 2 O 3 (mol %).
4. The lithium aluminosilicate glass of claim 1 , wherein the lithium aluminosilicate glass comprises:
from 58 mol % to 69 mol % SiO 2 ;
from 10 mol % to 17 mol % Al 2 O 3 ;
from 3.5 mol % to 9.5 mol % B 2 O 3 ;
from 0 mol % to 2.5 mol % P 2 O 5 ;
from 7 mol % to 11.4 mol % Li 2 O;
from 0.2 mol % to 14 mol % Na 2 O;
from 0 mol % to 2.5 mol % K 2 O;
from 0 mol % to 5 mol % MgO; and
from 0 mol % to 4 mol % ZnO,
wherein Li 2 O (mol %)/R 2 O (mol %) is in a range from 0.25 to 0.4.
5. The lithium aluminosilicate glass of claim 4 , wherein the lithium aluminosilicate glass comprises:
from 5 mol % to 9 mol % B 2 O 3 ;
from 7 mol % to 10 mol % Li 2 O;
from 4 mol % to 14 mol % Na 2 O; and
from 0 mol % to 1 mol % K 2 O.
6. The lithium aluminosilicate glass of claim 1 , wherein (Al 2 O 3 (mol %)+B 2 O 3 (mol %))/R 2 O (mol %) is in a range from 0.9 to 1.57.
7. The lithium aluminosilicate glass of claim 1 , wherein R 2 O (mol %)+R′O (mol %)−Al 2 O 3 (mol %)−B 2 O 3 (mol %)−P 2 O 5 (mol %) is in a range from −10 mol % to −0.11 mol %, where R′O=MgO+CaO+SrO+BaO.
8. The lithium aluminosilicate glass of claim 1 , wherein the lithium aluminosilicate glass comprises from 7 mol % to 12 mol % Li 2 O.
9. The lithium aluminosilicate glass of claim 1 , wherein the lithium aluminosilicate glass comprises:
from 0 mol % to 5 mol % Na 2 O;
from 0 mol % to 4 mol % K 2 O;
from 0 mol % to 8 mol % MgO;
from 0 mol % to 4 mol % ZnO;
from 0 mol % to 5 mol % TiO 2 ; and
from 0 mol % to 3 mol % P 2 O 5 .
10. The lithium aluminosilicate glass of claim 9 , wherein the lithium aluminosilicate glass comprises:
from 55 mol % to 60 mol % SiO 2 ;
from 12 mol % to 15 mol % Al 2 O 3 ;
from 3.5 mol % to 7.5 mol % B 2 O 3 ;
from 7 mol % to 10 mol % Li 2 O; and
from 0 mol % to 3 mol % P 2 O 5 .
11. The lithium aluminosilicate glass of claim 1 , wherein the lithium aluminosilicate glass comprises from 5 mol % to 7 mol % B 2 O 3 .
12. The lithium aluminosilicate glass of claim 1 , wherein the lithium aluminosilicate glass comprises:
from 0 mol % to 5 mol % Na 2 O; and
from 0.05 mol % to 0.5 mol % SnO 2 .
13. The lithium aluminosilicate glass of claim 1 , wherein the lithium aluminosilicate glass has a liquidus viscosity of at least 10 kP.
14. The lithium aluminosilicate glass of claim 1 , wherein the lithium aluminosilicate glass has a softening point of 840° C. or less.
15. The lithium aluminosilicate glass of claim 1 , wherein the lithium aluminosilicate glass has an anneal point of at least 510° C.
16. The lithium aluminosilicate glass of claim 1 , wherein the lithium aluminosilicate glass has an elastic modulus of at least 68 GPa.
17. The lithium aluminosilicate glass of claim 1 , wherein the lithium aluminosilicate glass is ion exchanged.
18. The lithium aluminosilicate glass of claim 17 , wherein the ion exchanged lithium aluminosilicate glass has a compressive layer extending to a depth of layer of at least 70 μm from at least one surface into the glass, the compressive layer having a maximum compressive stress of at least 600 MPa.
19. The lithium aluminosilicate glass of claim 18 , wherein the compressive layer has a compressive stress of at least 100 MPa at a depth of 50 μm below the surface.
20. The lithium aluminosilicate glass of claim 17 , wherein the lithium aluminosilicate glass has a Vickers crack initiation threshold of at least 10 kgf.
21. The lithium aluminosilicate glass of claim 17 , wherein the lithium aluminosilicate glass has a Knoop scratch threshold of at least 8 N.
22. A consumer electronic product, comprising:
a housing having a front surface, a back surface and side surfaces;
electrical components provided at least partially within the housing, the electrical components including at least a controller, a memory, and a display, the display being provided at or adjacent the front surface of the housing; and
a cover glass disposed over the display,
wherein at least one of a portion of the housing or the cover glass comprises the lithium aluminosilicate glass of claim 1 .
23. A lithium aluminosilicate glass comprising:
from 55 mol % to 75 mol % SiO 2 ;
from 10 mol % to 18 mol % Al 2 O 3 ;
from 2.5 mol % to 7.5 mol % B 2 O 3 ;
from 5 mol % to 13 mol % Li 2 O;
from 0 mol % to 4 mol % P 2 O 5 ; and
from 0 mol % to 1 mol % K 2 O;
wherein Li 2 O (mol %)/R 2 O (mol %) is in a range from 0.15 to 0.4, R 2 O=Li 2 O+Na 2 O+K 2 O+Rb 2 O+Cs 2 O, R 2 O (mol %)+R′O (mol %)−Al 2 O 3 (mol %)−B 2 O 3 (mol %)−P 2 O 5 (mol %) is in a range from −10.5 mol % to −0.11 mol %, and R′O=MgO+CaO+SrO+BaO.
24. The lithium aluminosilicate glass of claim 23 , wherein R 2 O (mol %)−Al 2 O 3 (mol %) is in a range from −2 mol % to 5.6 mol %.
25. The lithium aluminosilicate glass of claim 23 , wherein Al 2 O 3 (mol %)>B 2 O 3 (mol %).
26. The lithium aluminosilicate glass of claim 23 , wherein (Al 2 O 3 (mol %)+B 2 O 3 (mol %))/R 2 O (mol %) is in a range from 0.9 to 1.9.
27. The lithium aluminosilicate glass of claim 23 , wherein the lithium aluminosilicate glass comprises:
from 0 mol % to 5 mol % Na 2 O;
from 0 mol % to 8 mol % MgO;
from 0 mol % to 4 mol % ZnO;
from 0 mol % to 5 mol % TiO 2 ; and
from 0 mol % to 3 mol % P 2 O 5 .
28. The lithium aluminosilicate glass of claim 23 , wherein the lithium aluminosilicate glass comprises from 5 mol % to 7 mol % B 2 O 3 .
29. The lithium aluminosilicate glass of claim 23 , wherein the lithium aluminosilicate glass comprises:
from 0 mol % to 5 mol % Na 2 O; and
from 0.05 mol % to 0.5 mol % SnO 2 .
30. A consumer electronic product, comprising:
a housing having a front surface, a back surface and side surfaces;
electrical components provided at least partially within the housing, the electrical components including at least a controller, a memory, and a display, the display being provided at or adjacent the front surface of the housing; and
a cover glass disposed over the display,
wherein at least one of a portion of the housing or the cover glass comprises the lithium aluminosilicate glass of claim 23 .
31. The lithium aluminosilicate glass of claim 23 , wherein the lithium aluminosilicate glass has a softening point of 840° C. or less.
32. The lithium aluminosilicate glass of claim 23 , wherein the lithium aluminosilicate glass has an anneal point of at least 510° C.
33. The lithium aluminosilicate glass of claim 23 , wherein the lithium aluminosilicate glass has an elastic modulus of at least 68 GPa.
34. The lithium aluminosilicate glass of claim 23 , wherein the lithium aluminosilicate glass is ion exchanged.
35. The lithium aluminosilicate glass of claim 34 , wherein the ion exchanged lithium aluminosilicate glass has a compressive layer extending to a depth of layer of at least 70 μm from at least one surface into the glass, the compressive layer having a maximum compressive stress of at least 600 MPa.
36. The lithium aluminosilicate glass of claim 35 , wherein the compressive layer has a compressive stress of at least 100 MPa at a depth of 50 μm below the surface.
37. The lithium aluminosilicate glass of claim 34 , wherein the lithium aluminosilicate glass has a Vickers crack initiation threshold of at least 10 kgf.
38. The lithium aluminosilicate glass of claim 34 , wherein the lithium aluminosilicate glass has a Knoop scratch threshold of at least 8 N.
39. The lithium aluminosilicate glass of claim 23 , wherein the lithium aluminosilicate glass has a liquidus viscosity of at least 10 kP.