Positive electrode active material and non-aqueous electrolyte secondary battery containing the same
A positive electrode active material includes particles composed of a compound oxide; and coating layers composed of a compound oxide formed on at least parts of the surfaces of the particles. The particles have a layered structure and include a first compound oxide mainly composed of lithium and nickel. The coating layers include a second compound oxide mainly composed of lithium and titanium. The ratio by weight of the first compound oxide to the second compound oxide is between 96:4 and 65:35. The positive electrode active material has a mean particle diameter of 5 to 20 μm.
1. A positive electrode active material comprising inner particles having a layered structure and a coating layer formed on at least parts of the surfaces of the inner particles,
wherein said inner particle is a first compound oxide including a compound expressed by the formula LiNi (1-x) M x O 2 , wherein x is represented by 0.5>x>0.1, and element M is at least one of iron (Fe), cobalt (Co), manganese (Mn), copper (Cu), zinc (Zn), chromium (Cr), vanadium (V), titanium (Ti), aluminum (Al), tin (Sn), boron (B), gallium (Ga), magnesium (Mg), calcium (Ca), and strontium (Sr),
wherein said coating layer is a second compound oxide comprising lithium and having a spinel structure in the cubic system,
wherein the ratio by weight of the first compound oxide to the second compound oxide is between 96:4 and 65:35, and
wherein the first compound oxide is LiNi 0.50 Co 0.20 Mn 0.30 O 2 , and the second compound oxide is Li 4 Ti 5 O 12 .
2. A positive electrode active material comprising inner particles having a layered structure and a coating layer formed on at least parts of the surfaces of the inner particles,
wherein said inner particle is a first compound oxide including a compound expressed by the formula LiNi (1-x) M x O 2 , wherein x is represented by 0.5>x>0.1, and element M is at least one of iron (Fe), cobalt (Co), manganese (Mn), copper (Cu), zinc (Zn), chromium (Cr), vanadium (V), titanium (Ti), aluminum (Al), tin (Sn), boron (B), gallium (Ga), magnesium (Mg), calcium (Ca), and strontium (Sr),
wherein said coating layer is a second compound oxide comprising lithium and having a spinel structure in the cubic system,
wherein the ratio by weight of the first compound oxide to the second compound oxide is between 96:4 and 65:35, and
wherein the first compound oxide is LiNi 0.50 Co 0.20 Mn 0.30 O 2 having a layered rock-salt structure, and the second compound oxide is Li 4 Ti 5 O 12 having a spinel structure in the cubic system.
3. A positive electrode active material comprising inner particles having a layered structure and a coating layer formed on at least parts of the surfaces of the inner particles,
wherein said inner particle is a first compound oxide including a compound expressed by the formula LiNi (1-x) M x O 2 , wherein x is represented by 0.5>x>0.1, and element M is at least one of iron (Fe), cobalt (Co), manganese (Mn), copper (Cu), zinc (Zn), chromium (Cr), vanadium (V), titanium (Ti), aluminum (Al), tin (Sn), boron (B), gallium (Ga), magnesium (Mg), calcium (Ca), and strontium (Sr),
wherein said coating layer is a second compound oxide comprising lithium and having a spinel structure in the cubic system,
wherein the ratio by weight of the first compound oxide to the second compound oxide is between 96:4 and 65:35, and
wherein the first compound oxide has a layered rock-salt structure with spherically shaped particles having a mean particle diameter of 13-14 μm, and the second compound oxide is one of Li 4 Ti 5 O 12 having a spinel structure in the cubic system and particles with a mean particle diameter of 0.4 μm, Li 2 TiO 3 having a monoclinic system and particles with a mean particle diameter of 0.6 μm, and Li 2 Ti 3 O 7 having a rhombic system and particles with a mean particle diameter of 0.8 μm.