Selective formation of metallic films on metallic surfaces
Metallic layers can be selectively deposited on one surface of a substrate relative to a second surface of the substrate. In some embodiments, the metallic layers are selectively deposited on copper instead of insulating or dielectric materials. In some embodiments, a first precursor forms a layer on the first surface and is subsequently reacted or converted to form a metallic layer. The deposition temperature may be selected such that a selectivity of above about 50% or even about 90% is achieved.
1. A method for selectively depositing a film on a first metal surface of a substrate relative to a second dielectric surface of the substrate, the method comprising:
contacting the substrate with one or more silanes; and
carrying out one or more deposition cycles at a temperature of less than 150° C., each cycle comprising:
contacting the substrate with a first precursor comprising tungsten (W); and
contacting the substrate with a second precursor,
wherein deposition on the first metal surface relative to the second dielectric surface has a selectivity of greater than 50%.
2. The method of claim 1 , wherein at least one deposition cycle comprises contacting the substrate with the second precursor prior to contacting the substrate with the first precursor.
3. The method of claim 1 , wherein the substrate is contacted with a silane having the formula Si n H 2n+2 , where n is equal to or greater than 1.
4. The method of claim 1 , wherein the substrate is contacted with a silane selected from silane and trisilane.
5. The method of claim 1 , wherein the substrate is contacted with disilane.
6. The method of claim 1 , wherein the substrate is contacted with a silane having the formula SiH x L y , where L is a ligand selected from alkyl, alkenyl, alkynyl, alkoxide and amide groups.
7. The method of claim 1 , wherein substrate is contacted with an alkylhalosilane having the formula R 3-x SiL, wherein L is a halide, x is from 1 to 3 and each R can be independently selected from C1-C5 hydrocarbons.
8. The method of claim 7 , wherein L is chloride.
9. The method of claim 1 , wherein contacting the substrate with at least one silane forms —Si(CH 3 ) 3 groups on the second dielectric surface.
10. The method of claim 1 , wherein the substrate is contacted with one or more silanes after carrying out one or more deposition cycles.
11. The method of claim 1 , wherein the one or more deposition cycles are carried out subsequent to contacting the substrate with one or more silanes.
12. The method of claim 1 , wherein the second precursor comprises silicon or boron.
13. The method of claim 1 , wherein the first precursor comprises a tungsten halide.
14. The method of claim 1 , wherein the first precursor comprises WF 6 .
15. The method of claim 1 , additionally comprising cleaning the substrate prior to contacting the substrate with the one or more silanes.
16. The method of claim 15 , wherein cleaning comprises exposing the substrate to a plasma.
17. The method of claim 15 , wherein cleaning comprises removing a passivation layer from the first metal surface.
18. The method of claim 1 , wherein the first metal surface comprises copper.
19. The method of claim 1 , wherein the film comprises elemental tungsten.
20. The method of claim 1 , wherein deposition on the first metal surface relative to the second dielectric surface has a selectivity of greater than 90%.
21. The method of claim 1 , wherein contacting the substrate with one or more silanes and the deposition cycles are carried out in different reaction spaces.