Method for pre-treatment of gold-bearing oxide ores

1. A process, comprising:

a) providing particulate carbon comprising one or more of activated carbon, activated charcoal, coke, hard carbon derived from at least one of coconut shells and elemental carbon, a calcined resin, and mixtures thereof;

b) providing a precious metal-containing material having a first precious metal thiosulfate leaching value in the absence of prior contact with the particulate carbon;

c) contacting the precious metal-containing material with the particulate carbon and an oxidant to form a pre-treated slurry comprising a pre-treated precious metal-containing material; and

d) contacting the pre-treated slurry with thiosulfate to leach the precious metal from the pre-treated precious metal-containing material, wherein the pre-treated precious metal-containing material has a second precious metal thiosulfate leaching value after contacting step c) more than the first precious metal thiosulfate leaching value.

2. The process of claim 1 , wherein, in step a), the precious metal-containing material is free of contact with thiosulfate.

3. The process of claim 1 , wherein the precious metal-containing material contains more oxides than sulfides and wherein the precious metal-containing material is refractory to thiosulfate leaching.

4. The process of claim 1 , wherein the precious metal-containing material is an oxide ore that is amenable to precious metal recovery by cyanidation, wherein the precious metal-containing material has an average precious metal-containing material particle size, wherein the particulate carbon has an average carbon particle size, and wherein the average carbon particle size is more than the average precious metal-containing material particle size and further comprising:

prior to contacting step d), removing the carbon from the pre-treated slurry, wherein the carbon is removed from the pre-treated slurry by screening.

5. The process of claim 1 , wherein the oxidant is molecular oxygen, wherein the precious metal-containing material before step a) has an initial pH of at least pH 3, wherein the pre-treated slurry has a pH of from about pH 7 to about pH 10, wherein an oxidation-reduction potential during step a) ranges from about 100 to about 750 mV (Ag/AgCl electrode), wherein a rate of contact of molecular oxygen with the slurry during step a) is at least 0.10 L O 2 /L slurry/min, and wherein a weight ratio of the precious metal-bearing material to carbon ranges from about 50:1 to about 1:0.01.

6. The process of claim 1 , wherein at least about 95% of the carbon is removed from the pre-treated slurry.

7. The process of claim 1 , wherein the pre-treated slurry is contacted with thiosulfate in the absence of pH adjustment and/or slurry density adjustment.

8. The process of claim 1 , wherein the pre-treated slurry is contacted with thiosulfate in the absence of pH adjustment and/or slurry density adjustment.

9. The process of claim 8 , wherein a pH of the pre-treated slurry is adjusted by no more than pH 0.1 and the slurry density is adjusted by no more than 5%.

10. A process, comprising:

a) contacting a gold-containing material with carbon and an oxidant to form a pre-treated slurry, the carbon comprising one or more of activated carbon, activated charcoal, coke, hard carbon derived from at least one of coconut shells and elemental carbon, a calcined resin, and mixtures thereof, wherein the carbon has an average carbon particle size and the gold-containing material has an average gold-containing material particle size and wherein the average carbon particle size is more than the average gold-containing material particle size;

b) removing the carbon from the pre-treated slurry to form a carbon-depleted slurry, wherein the carbon is removed from the pre-treated slurry by screening; and

c) contacting the carbon-depleted slurry with thiosulfate to leach gold from the carbon-depleted slurry.

11. The process of claim 10 , wherein, in step a), the gold-containing material is free of contact with thiosulfate.

12. The process of claim 11 , wherein, after step a), the pre-treated slurry comprises no more than 0.0025 molar thiosulfate.

13. The process of claim 10 , wherein the gold-containing material contains more oxides than sulfides and wherein a gold recovery by thiosulfate leaching of the gold-containing material in the absence of prior contact with the carbon is less than a gold recovery by thiosulfate leaching of the gold-containing material after prior contact with the carbon.

14. The process of claim 10 , wherein the gold-containing material is an oxide ore that is amenable to gold recovery by cyanidation, wherein the carbon-depleted slurry has a greater gold thiosulfate leaching value than at least part of the gold-containing material, and wherein at least part of the gold-containing material is refractory to recovery of the gold by thiosulfate leaching.

15. The process of claim 10 , wherein the oxidant is molecular oxygen, wherein the gold-containing material before step a) has a pH at least pH 3, wherein, during step a), the slurry has a pH of from about pH 7 to about pH 10, wherein, during step a), the slurry has an oxidation-reduction potential ranging from about 100 to about 750 mV (Ag/AgCl electrode), wherein a rate of contact of molecular oxygen with the slurry during step a) is at least 0.10 L O 2 /L slurry/min, and wherein a weight ratio of the gold-bearing material to carbon ranges from about 50:1 to about 1:0.01.

16. The process of claim 10 , wherein at least about 95% of the carbon is removed from the pre-treated slurry.

17. A process, comprising:

a) contacting a gold-containing material with carbon and an oxidant to form a pre-treated slurry, the carbon comprising one or more of activated carbon, activated charcoal, coke, hard carbon derived from at least one of coconut shells and elemental carbon, a calcined resin, and mixtures thereof;

b) removing the carbon from the pre-treated slurry to form a carbon-depleted slurry, wherein the carbon is removed from the pre-treated slurry by screening; and

c) contacting the carbon-depleted slurry with thiosulfate to leach gold from the carbon-depleted slurry, wherein:

in step a), the gold-containing material is free of contact with thiosulfate;

the gold-containing material contains more oxides than sulfides;

the gold-containing material is an oxide ore that is amenable to gold recovery by cyanidation;

a gold recovery by thiosulfate leaching of the carbon-depleted slurry is greater than a gold recovery by thiosulfate leaching of the gold-containing material in the absence of prior contact with the carbon;

the oxidant is molecular oxygen;

the gold-containing material before step a) has a pH at least pH 3;

during step a), the gold-containing material has a pH of from about pH 7 to about pH 10;

during step a), the gold-containing material has an oxidation-reduction potential ranging from about 100 to about 750 mV (Ag/AgCl electrode);

a rate of contact of molecular oxygen with the slurry during step a) is at least 0.10 L O 2 /L slurry/min; and

a weight ratio of the gold-bearing material to carbon ranges from about 1:3 to about 1:0.01.

18. The process of claim 17 , wherein the carbon-depleted slurry is contacted with thiosulfate in the absence of pH adjustment and/or slurry density adjustment and wherein at least part of the gold-containing material is refractory to recovery of gold by thiosulfate leaching.

19. The process of claim 17 , wherein a pH of the carbon-depleted slurry is adjusted by no more than pH 0.1 and the slurry density is adjusted by no more than 5%.

20. The process of claim 19 , wherein, after step a), the pre-treated slurry comprises no more than 0.0025 molar thiosulfate.

21. The process of claim 17 , wherein at least about 95% of the carbon is removed from the pre-treated slurry.