Steel sheet for hot stamping, method for production thereof, and hot stamping steel material
A hot stamping steel material, which secures good hydrogen embrittlement resistance even when the steel sheet after hot stamping is subjected to processing leading to remaining of stress, such as piercing and which is easily practicable, wherein the steel sheet has the chemical composition of: C: 0.18 to 0.26%; Si: more than 0.02% and not more than 0.05%; Mn: 1.0 to 1.5%; P: 0.03% or less; S: 0.02% or less; Al: 0.001 to 0.5%; N: 0.1% or less; O: 0.001 to 0.02%; Cr: 0 to 2.0%; Mo: 0 to 1.0%; V: 0 to 0.5%; W: 0 to 0.5%; Ni: 0 to 5.0%; B: 0 to 0.01%; Ti: 0 to 0.5%; Nb: 0 to 0.5%; Cu: 0 to 1.0%; and balance: Fe and impurities, in terms of % by mass, the concentration of a Mn-containing inclusion is not less than 0.010% by mass and less than 0.25% by mass, and the number ratio of a Mn oxide to the inclusion having a maximum length of 1.0 to 4.0 μm is 10.0% or more.
1. A steel sheet for hot stamping, wherein the steel sheet comprises a chemical composition comprising:
C: 0.18 to 0.26%;
Si: more than 0.02% and not more than 0.05%;
Mn: 1.0 to 1.5%;
P: 0.03% or less;
S: 0.02% or less;
Al: 0.001 to 0.5%;
N: 0.1% or less;
O: 0.005 to 0.020%;
Cr: 0 to 2.0%;
Mo: 0 to 1.0%;
V: 0 to 0.5%;
W: 0 to 0.5%;
Ni: 0 to 5.0%;
B: 0 to 0.01%;
Ti: 0 to 0.5%;
Nb: 0 to 0.5%;
Cu: 0 to 1.0%; and
balance: Fe and impurities, in terms of % by mass,
the concentration of a Mn-containing inclusion is not less than 0.010% by mass and less than 0.25% by mass, and the number ratio of a Mn oxide to the inclusion having a maximum length of 1.0 to 4.0 μm is 10.0% or more.
2. The steel sheet for hot stamping according to claim 1 , wherein the chemical composition comprises one or more selected from the group consisting of
Cr: 0.01 to 2.0%;
Mo: 0.01 to 1.0%;
V: 0.01 to 0.5%;
W: 0.01 to 0.5%;
Ni: 0.01 to 5.0%; and
B: 0.0005 to 0.01%, in terms of % by mass.
3. The steel sheet for hot stamping according to claim 1 , wherein the chemical composition comprises one or more selected from the group consisting of
Ti: 0.001 to 0.5%;
Nb: 0.001 to 0.5%; and
Cu: 0.01 to 1.0%, in terms of % by mass.
4. The steel sheet for hot stamping according to claim 1 , wherein the steel sheet comprises, on a surface thereof, an aluminum hot-dipping layer having a thickness of 50 μm or less.
5. The steel sheet for hot stamping according to claim 1 , wherein the steel sheet comprises, on a surface thereof, a hot-dip galvanized layer having a thickness of 30 μm or less.
6. The steel sheet for hot stamping according to claim 1 , wherein the steel sheet comprises, on a surface thereof, an alloyed hot-dip galvanized layer having a thickness of 45 μm or less.
7. A hot stamping steel material, wherein the hot stamping steel material comprises a chemical composition comprising:
C: 0.18 to 0.26%;
Si: more than 0.02% and not more than 0.05%;
Mn: 1.0 to 1.5%;
P: 0.03% or less;
S: 0.02% or less;
Al: 0.001 to 0.5%;
N: 0.1% or less;
O: 0.005 to 0.020%;
Cr: 0 to 2.0%;
Mo: 0 to 1.0%;
V: 0 to 0.5%;
W: 0 to 0.5%;
Ni: 0 to 5.0%;
B: 0 to 0.01%;
Ti: 0 to 0.5%;
Nb: 0 to 0.5%;
Cu: 0 to 1.0%; and
balance: Fe and impurities, in terms of % by mass,
the concentration of a Mn-containing inclusion is not less than 0.010% by mass and less than 0.25% by mass, and the number ratio of a Mn oxide to the inclusion having a maximum length of 1.0 to 4.0 μm is 10.0% or more.
8. The hot stamping steel material according to claim 7 , wherein the chemical composition comprises one or more selected from the group consisting of Cr: 0.01 to 2.0%; Mo: 0.01 to 1.0%; V: 0.01 to 0.5%; W: 0.01 to 0.5%; Ni: 0.01 to 5.0%; and B: 0.0005 to 0.01%, in terms of % by mass.
9. The hot stamping steel material according to claim 7 , wherein the chemical composition comprises one or more selected from the group consisting of Ti: 0.001 to 0.5%; Nb: 0.001 to 0.5%; and Cu: 0.01 to 1.0%, in terms of % by mass.
10. The steel sheet for hot stamping according to claim 2 , wherein the chemical composition comprises one or more selected from the group consisting of
Ti: 0.001 to 0.5%;
Nb: 0.001 to 0.5%; and
Cu: 0.01 to 1.0%, in terms of % by mass.
11. The steel sheet for hot stamping according to claim 2 , wherein the steel sheet comprises, on a surface thereof, an aluminum hot-dipping layer having a thickness of 50 μm or less.
12. The steel sheet for hot stamping according to claim 3 , wherein the steel sheet comprises, on a surface thereof, an aluminum hot-dipping layer having a thickness of 50 μm or less.
13. The steel sheet for hot stamping according to claim 2 , wherein the steel sheet comprises, on a surface thereof, a hot-dip galvanized layer having a thickness of 30 μm or less.
14. The steel sheet for hot stamping according to claim 3 , wherein the steel sheet comprises, on a surface thereof, a hot-dip galvanized layer having a thickness of 30 μm or less.