Method for manufacturing dental mill blank
A method for producing a dental mill blank, characterized in that the method includes contacting an inorganic filler molded article produced by subjecting an inorganic filler to press molding and a polymerizable monomer-containing composition, and allowing the polymerizable monomer to polymerize and cure. When the method of the present invention is used, a dental mill blank having a high inorganic powder content and excellent mechanical strength is obtained. In addition, the dental mill blank obtained is suitably used in the fabrication of a dental prosthesis having high mechanical strength and excellent gloss retention, by machining a mill blank using a CAD/CAM system.
1. A method for producing a dental mill blank, the method comprising:
press molding an inorganic filler to obtain an inorganic filler molded article;
immersing the inorganic filler molded article in a polymerizable monomer-comprising composition; and
polymerizing and curing the polymerizable monomer-comprising composition, to obtain a dental mill blank,
wherein the polymerizable monomer-comprising composition further comprises at least one of a photopolymerization initiator and a thermal polymerization initiator.
2. The method according to claim 1 , wherein the press molding is a uniaxial press molding.
3. The method according to claim 2 , Therein a press pressure during the uniaxial press molding is 10 MPa or more.
4. The method according to claim 1 , wherein the press molding comprises a cold isotactic press molding.
5. The method according to claim 4 , wherein a press pressure during the cold isotactic press molding is 30 MPa or more.
6. The method according to claim 1 , wherein the polymerizing and curing occurs in a vacuum state.
7. The method according to claim 1 , wherein the polymerizing and curing is carried out under an applied pressure.
8. The method according to claim 7 , wherein the applied pressure is 50 MPa or more.
9. The method according to claim 1 , wherein the polymerizable monomer-comprising composition further comprises the photopolymerization initiator and the thermal polymerization initiator.
10. The method according to claim 9 , wherein the polymerizing and curing comprises, subsequent to a photopolymerization, a thermal polymerization.
11. The method according to claim 1 , wherein the inorganic filler comprises inorganic particles having an average particle size of from 0.001 to 10 μm, and a particle size range of from 0.0005 to 50 μm.
12. The method according to claim 1 , wherein the inorganic filler comprises inorganic particles having an average particle size of from 0.1 to 1 μm, and a particle size range of from 0.05 to 5 μm.
13. The method according to claim 12 , wherein the inorganic filler comprises spherical particles.
14. The method according to claim 1 , wherein the inorganic filler comprises ultrafine inorganic panicles having an average particle size of from 0.001 to 0.1 μm , and a specific surface area of from 500 to 30 m 2 /g.
15. The method according to claim 1 , wherein the inorganic filler comprises inorganic particles that are aggregated particles produced by aggregating ultrafine inorganic particles having an average particle size of from 0.001 to 0.1μm, and a specific surface area of from 500 to 30 m 2 /g, and the particle sizes of the aggregated particles range from 1 to 20μm.
16. The method according to claim 1 , wherein the inorganic filler comprises
ultrafine inorganic particles having an average particle size of from 0.001 to 0.1 μm, and a specific surface area of from 500 to 30 m 2 /g, and
inorganic particles having an average particle size of from 0.2 to 2 μm and a particle size range of from 0.1 to 10 μm.
17. The method according to claim 1 , wherein the inorganic filler comprises inorganic particles previously subjected to a surface treatment.
18. A dental mill blank obtained by the method according to claim 1 , wherein the inorganic filler does not include a calcium phosphate.
19. The dental mill blank according to claim 18 ,
wherein the inorganic filler molded article is a molded article produced by press molding two or more kinds of different inorganic particles into a layered form.
20. A dental prosthesis fabricated by a method comprising machining the dental mill blank according to claim 18 .
21. A dental mill blank obtained by the method according to claim 1 , wherein:
the mill blank comprises ultrafine inorganic particles having an average particle size of from 0.001 to 0.1 μm in an amount of from 65 to 95% by weight of the mill blank: and
the inorganic filler does not include a calcium phosphate.
22. A dental mill blank obtained by the method according to claim 1 , wherein:
the dental mill blank comprises inorganic particles having an average particle size of from 0.1 to 1 μm in an amount of from 80 to 95% by weight of the mill blank: and
the inorganic filler does not include a calcium phosphate.
23. A dental mill blank obtained by the method according to claim 1 , wherein:
the dental mill blank comprises ultrafine inorganic particles having an average particle size of from 0.001 to 0.1 μm and inorganic particles having an average particle size of from 0.2 to 2 μm in a total amount of from 80 to 96% by weight of the mill blank: and
the inorganic filler does not include a calcium phosphate.
24. The method of claim 1 , wherein the dental mill blank does not contain internal bubbles.