Manufacturing cathode material, cathode, and lithium ion battery
A cathode material which does not easily deteriorate when used in batteries, a method for producing cathode materials, a cathode, and a lithium ion battery are provided. A cathode material including a cathode active material, in which the cathode active material is expressed by Li 1+x A y D z PO 4 (here, A represents one or more metal elements selected from the group consisting of Co, Mn, Ni, Fe, Cu, and Cr, D represents one or more metal elements selected from the group consisting of Mg, Ca, Sr, Ba, Ti, Zn, B, Al, Ga, In, Si, Ge, Sc, Y, and rare earth elements, 0<x<1, 0<y<1, 0≤z<1.5, and 0.9<y+z≤1), and, in thermogravimetric analysis in an inert gas atmosphere, when a temperature is increased in a temperature range from 100° C. to 300° C. at a temperature-increase rate of 10° C./minute, a weight loss ratio in the temperature range is 0.3% by weight or less.
1. A cathode material including a cathode active material,
wherein the cathode active material is expressed by Li 1+x A y D z PO 4 , wherein A represents one or more metal elements selected from the group consisting of Co, Mn, Ni, Fe, Cu, and Cr, D represents one or more metal elements selected from the group consisting of Mg, Ca, Sr, Ba, Ti, Zn, B, Al, Ga, In, Si, Ge, Sc, Y, and rare earth elements, 0<x<1, 0<y<1, 0≤z<1.5, and 0.9<y+z≤1, and
when a temperature of the cathode material is raised to a temperature range of 100° C. to 300° C. at a temperature-increase rate of 10° C/min, a weight loss ratio in the temperature range due to evaporation of water of crystallization is 0.03% by weight to 0.3% by weight, wherein the weight loss ratio is measured in a thermogravimetric analysis, which is carried out under the following measurement conditions using a differential thermogravimetric analyzer:
specimen amount: 15 mg
temperature-increase rate: 10° C. /minute
atmosphere: N2
gas flow rate: 200 ml/minute
measurement temperature range: 100 to 300° C.
2. The cathode material according to claim 1 ,
wherein the cathode material comprises active material particles which is formed of the cathode active material and a carbonaceous material which presents on surfaces of the active material particles.
3. The cathode material according to claim 1 ,
wherein the cathode material comprises water of crystallization at ratio of 0.3% by weight or less with respect to the cathode material.
4. The cathode material according to claim 1 ,
wherein a P/(A+D) molar ratio of the cathode material is at a range from 1.00 to 1.05, wherein the P/(A+D) molar ratio is measured by using a ICP atomic emission spectroscopy.
5. A cathode comprising the cathode material according to claim 1 .
6. A lithium ion battery comprising:
the cathode according to claim 5 .
7. The cathode material according to claim 1 ,
wherein the cathode material further comprises an impurity which comprises adsorbed water or water of crystallization, wherein the impurity is from raw material of the cathode material or from intermediate products.
8. The cathode material according to claim 7 ,
wherein the impurity is a compound expressed by A 3 (PO 4 ) 2 , wherein A represents one or more metal elements selected from the group consisting of Co, Mn, Ni, Fe, Cu, and Cr.