Heat-activated fabrics made from blends containing propylene-based polymers
The invention relates to an heat-activated fabric comprising a polymer blend of 70 to 100 wt % of a polymer blend component and 0 to 30 wt % of a propylene polymer, wherein the polymer blend component comprises a first propylene-based polymer, wherein the first propylene-based polymer is a homopolymer of propylene or a copolymer of propylene and ethylene or a C 4 to C 10 alpha-olefin and a second propylene-based polymer, wherein the second propylene-based polymer is a homopolymer of propylene or a copolymer of propylene and ethylene or a C 4 to C 10 alpha-olefin, wherein the second propylene-based polymer is different than the first propylene-based polymer and wherein the polymer blend component has a MFR of greater than or equal to 20 g/10 min to less than 10,000 g/10 min; and wherein the propylene polymer has a MFR of greater than or equal to 20 g/10 min to less than 5,000 g/10 min.
1. A heat-activated fabric comprising a polymer blend of from about 70 to about 90 wt % of a polymer blend component and from about 10 to about 30 wt % of a propylene polymer,
wherein the polymer blend component comprises a first propylene-based polymer, wherein the first propylene-based polymer is a copolymer of propylene and ethylene or a C 4 to C 10 alpha-olefin and a second propylene-based polymer, wherein the second propylene-based polymer is a homopolymer of propylene or a copolymer of propylene and ethylene or a C 4 to C 10 alpha-olefin, wherein the second propylene-based polymer is different than the first propylene-based polymer and wherein the polymer blend component has a MFR, measured according to ASTM D-1238 at 230° C. and 2.16 kg, of greater than or equal to about 20 g/10 min to less than about 10,000 g/10 min; and
wherein the propylene polymer has a MFR, measured according to ASTM D-1238 at 230° C. and 2.16 kg, of greater than or equal to about 20 g/10 min to less than about 5,000 g/10 min.
2. A heat-activated fabric comprising a polymer blend of from about 70 to about 90 wt % of a polymer blend component and from about 10 to about 30 wt % of a propylene polymer,
wherein the polymer blend component comprises a first propylene-based polymer, wherein the first propylene-based polymer is a copolymer of propylene and ethylene or a C 4 to C 10 alpha-olefin and a second propylene-based polymer, wherein the second propylene-based polymer is a homopolymer of propylene or a copolymer of propylene and ethylene or a C 4 to C 10 alpha-olefin, wherein the second propylene-based polymer is different than the first propylene-based polymer, wherein the polymer blend component has a melt viscosity, measured according to ASTM D-3236 at 190° C., of about 1,000 to about 10,000 cP; and
wherein the propylene polymer has a melt viscosity, measured according to ASTM D-3236 at 190° C., of about 2,000 to about 20,000 cP.
3. The heat-activated fabric of claim 1 , wherein the polymer blend component has a MFR, measured according to ASTM D-1238 at 230° C. and 2.16 kg, of greater than or equal to about 400 g/10 min to less than about 10,000 g/10 min.
4. The heat-activated fabric of claim 1 , wherein the polymer blend component has a MFR, measured according to ASTM D-1238 at 230° C. and 116 kg, of greater than or equal to about 20 g/10 min to less than about 400 g/10 min.
5. The heat-activated fabric of claim 1 , wherein the propylene polymer is a homopolymer of propylene or a copolymer of propylene units with from about 0.5 to about 4 wt % ethylene or C 4 to C 10 alpha-olefin comonomer derived units.
6. The heat-activated fabric of claim 1 , wherein the polymer blend component has an Mw of about 10,000 g/mol to about 150,000 g/mol.
7. The heat-activated fabric of claim 1 , wherein the polymer blend component is a dual reactor blend.
8. The heat-activated fabric of claim 1 , wherein the polymer blend component is a solution blend and/or melt blend.
9. The heat-activated Fabric of claim 1 , wherein the first propylene-based polymer of the polymer blend component comprises a copolymer of propylene and ethylene, and the second propylene-based polymer of the polymer blend component comprises a copolymer of propylene and ethylene.
10. The heat-activated fabric of claim 1 , wherein the first propylene-based polymer of the polymer blend component and the second propylene-based propylene polymer of the polymer blend component have a difference in heat of fusion of at least 10 J/g.
11. An article comprising the heat-activated fabric of claim 1 .
12. An article of claim 11 , comprising the heat-activated fabric and one or more Substrates, wherein at least one of the one or more substrates comprises paper, cardboard, nonwoven fabric, metal, wood, cotton, other fiber based material, or combinations thereof.
13. A process to prepare a heat-activated fabric, comprising:
combining into a polymer blend:
from about 70 to about 90 wt % of a polymer blend component;
wherein the polymer blend component comprises a first propylene-based polymer, wherein the first propylene-based polymer is a copolymer of propylene and ethylene or a C 4 to C 10 alpha-olefin and a second propylene-based polymer, wherein the second propylene-based polymer is a homopolymer of propylene or a copolymer of propylene and ethylene or a C 4 to C 10 alpha-olefin, wherein the second propylene-based polymer is different than the first propylene-based polymer; and
wherein the polymer blend component has a MFR, measured according to ASTM D-1238 at 230° C. and 2.16 kg, of greater than or equal to about 20 g/10 min to less than about 10,000 g/10 min; and
b. from about 10 to about 30 wt % of a propylene polymer, wherein the propylene polymer has a MFR, measured according to ASTM D-1238 at 230° C. and 2.16 kg, of greater than or equal to about 20 g/10 min to less than about 5,000 g/10 min; and
forming a non-woven fabric comprising the polymer blend.
14. The process of claim 13 , wherein the polymer blend component has a melt viscosity, measured according to ASTM D-3236 at 190° C., of about 1,000 to about 10,000 cP, and wherein the propylene polymer has a melt viscosity, measured according to ASTM D-3236 at 190° C. of about 2,000 to about 20,000 cP.
15. The heat-activated fabric of claim 2 , wherein the polymer blend component has a MFR, measured according to ASTM D-1238 at 230° C. and 2.16 kg, of greater than or equal to about 400 g/10 min to less than about 10,000 g/10 min.
16. The heat-activated fabric of claim 2 , wherein the polymer blend component has a MFR, measured according to ASTM D-1238 at 230° C. and 2.16 kg, of greater than or equal to about 20 g/10 min to less than about 400 g/10 min.
17. The heat-activated fabric of claim 2 , wherein the propylene polymer is a homopolymer of propylene or a copolymer of propylene units with from about 0.5 to about 4 wt % ethylene or C 4 to C 10 alpha-olefin comonomer derived units.
18. The heat-activated fabric of claim 2 , wherein the polymer blend component has an Mw of about 10,000 mol to about 150,000 g/mol.
19. The heat-activated fabric of claim 2 , wherein the polymer blend component is a dual reactor blend.
20. The heat-activated fabric of claim 2 , wherein the polymer blend component is a solution blend and/or melt blend.